Preparation method of tooth-filling composite resin

A composite resin and tooth filling technology, which is applied in the field of medical polymers, achieves the effects of simple equipment, less allergy, and easy large-scale promotion.

Active Publication Date: 2015-01-07
GUILIN UNIVERSITY OF TECHNOLOGY
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention adopts graphene oxide modified acrylic monomer to prepare acrylic resin. This resin is used as the main raw material, and many other fillers and additives are used to prepare dental filling composite resin, which has better biocompatibility and anti-corrosion than current similar products. Allergies, wear resistance, anti-aging properties, etc., this idea of ​​the present invention has not been reported in the literature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The main raw materials for preparing dental filling composite resin in this example are graphene oxide grafted modified acrylic acid (self-made in the prior art), graphene oxide grafted modified methacrylic acid (made in the prior art), glycidyl methacrylate ( Chemically pure), n-butyl methacrylate (chemically pure), hydroxyethyl acrylate (chemically pure), octavinyl oligosilsesquioxane (chemically pure), chain regulator (chemically pure), benzene peroxide Formyl (chemically pure), 600~1500 mesh quartz powder (industrial grade), 500~5000 mesh white corundum powder (industrial grade), 0.5mm chopped micro glass fiber (industrial grade), polymerization inhibitor (industrial grade), light Initiator (industrial grade), defoamer (industrial grade).

[0017] The specific steps are:

[0018] (1) Weigh raw materials according to the following quality, 0.3 kg of graphene oxide grafted modified acrylic acid, 0.3 kg of graphene oxide grafted modified methacrylic acid, 0.4 kg of gl...

Embodiment 2

[0024] The main raw materials for preparing dental filling composite resin in this example are graphene oxide grafted modified acrylic acid (self-made in the prior art), graphene oxide grafted modified methacrylic acid (made in the prior art), glycidyl methacrylate ( Chemically pure), n-butyl methacrylate (chemically pure), hydroxyethyl acrylate (chemically pure), octavinyl oligosilsesquioxane (chemically pure), chain regulator (chemically pure), benzene peroxide Formyl (chemically pure), 600~1500 mesh quartz powder (industrial grade), 500~5000 mesh white corundum powder (industrial grade), 0.5mm chopped micro glass fiber (industrial grade), polymerization inhibitor (industrial grade), light Initiator (industrial grade), defoamer (industrial grade).

[0025] The specific steps are:

[0026] (1) Weigh raw materials according to the following quality, 0.3 kg of graphene oxide grafted modified acrylic acid, 0.4 kg of graphene oxide grafted modified methacrylic acid, 0.3 kg of gl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of composite resin for filling teeth. Graphene oxide modified acrylic monomer is used to prepare acrylic resin, using this resin as the main raw material, 600~1500 mesh quartz powder, 500~5000 mesh white corundum powder, 0.5mm chopped micro glass fiber, polymerization inhibitor, photoinitiator and defoaming agent, dental filling composite resin prepared by dispersion stirring, vacuum treatment, etc. The preparation method of the invention is simple, the equipment is simple, and it is easy to be popularized on a large scale. The prepared composite resin for filling teeth has good biocompatibility, is not prone to allergies, and has better adhesion, wear resistance, durability and anti-aging The service life can be extended by 5-10 years.

Description

technical field [0001] The invention belongs to the technical field of medical polymers, in particular to a preparation method of composite resin for filling teeth. Background technique [0002] The advent of dental filling composite resin is a breakthrough in the history of dental materials. The biggest feature of composite resin for dental fillings is beautiful color, coordinated with natural tooth color, good chemical stability, insoluble in saliva, and various varieties. There are composite resins for filling anterior teeth, composite resins for posterior teeth, and composite resins for both anterior and posterior teeth. . The restored teeth can be completely confused with the real ones, and it is difficult for a professional dentist to determine the authenticity without careful identification. As soon as it was born, it was accepted by dentists and patients. [0003] However, composite resins for dental fillings also have some problems, such as susceptibility to alle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61K6/083A61K6/027C08F283/12
Inventor 郭栋徐旭黄超梁金兴凌敏李静静
Owner GUILIN UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com