Ceramic diaphragm, and preparation method and application thereof
A ceramic diaphragm and diaphragm material technology, applied in electrical components, electrochemical generators, circuits, etc., can solve problems such as loss of isolation function, easy fire, and difference in diaphragm performance, so as to reduce VOC emissions, reduce fire risks, The effect of reducing energy consumption
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0028] Example 1
[0029] Add 20g of alumina to 80g of water-soluble polyvinylidene fluoride, and add an appropriate amount of water. Use a stirrer to perform high-speed dispersion at a speed of 100rpm or more. During the dispersion process, add 0.1-3% of the ceramic particle weight. ) Base phenol polyoxyethylene ether, and 0.1-3% of the weight of the ceramic particles polyethylene glycol type polyol, the dispersed slurry is stirred for 30-60 minutes, and then subjected to vacuum defoaming treatment to obtain a protective layer slurry;
[0030] The protective layer is coated on the diaphragm material substrate, and then dried to form a ceramic diaphragm film roll material, and finally cut into various width specifications of the finished ceramic diaphragm roll material.
[0031] Such as figure 1 As shown, the intermediate layer of the ceramic diaphragm prepared above is the diaphragm material base material 1, and the diaphragm material base
[0032] The material is a PP film layer or...
Example Embodiment
[0033] Example 2
[0034] Add 30g of alumina to 70g of water-soluble acrylic resin, and add an appropriate amount of water, and use a stirrer to perform high-speed dispersion at a speed of 100rpm or more. During the dispersion process, add 0.1-3% of the weight of the ceramic particle defoamer, and The dispersant accounts for 0.1-3% of the weight of the ceramic particles. After the dispersed slurry is stirred for 30-60 minutes, vacuum degassing is performed to obtain a protective layer;
[0035] The protective layer is coated on the diaphragm material substrate, and then dried to form a ceramic diaphragm film roll material, and finally cut into various width specifications of the finished ceramic diaphragm roll material.
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap