Method for producing cool sense honeycomb fibers

A technology of honeycomb fiber and production method, which is applied in the production field of cool-feeling honeycomb fiber, can solve the problems of large thermal resistance, reduce coolness, etc., and achieve the effects of enhancing cooling effect, improving thermal conductivity, and improving mechanical properties

Active Publication Date: 2014-03-05
VIOLET HOME TEXTILE TECH
View PDF8 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because the coolness depends on the joint action of thermal resistance and moisture resistance, the moisture resistance of honeycomb fiber is small but the thermal resistance is large, thus reducing the coolness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0009] The invention discloses a method for producing cool-feeling honeycomb fiber, which comprises adding high-thermal-conductivity nano-silicon carbide powder into pulp of honeycomb fiber at a weight ratio of 1%, and after stirring evenly, the honeycomb fiber is formed by flash-exploding filaments. The pulp of the honeycomb fiber is: chemical fiber polyester fiber. The crystal form of nano-silicon carbide powder is mixed crystal, the color is white, the average particle size is 20nm, the purity is 99.91, and the specific surface area is 43.2m 2 / g, the bulk density is 0.16g / cm 3 .

specific Embodiment 2

[0010] The invention discloses a method for producing cool-feeling honeycomb fibers. The high thermal conductivity nano-silicon carbide powder is added to the pulp of the honeycomb fibers according to the proportion of 2% by weight, and after being stirred evenly, the honeycomb fibers are formed by flashing out filaments. The pulp of the honeycomb fiber is: soybean fiber.

[0011] As a preference, the crystal form of the nano-silicon carbide powder is mixed crystal, the color is white, the average particle size is 40nm, the purity is 99.94, and the specific surface area is 43.2m 2 / g, the bulk density is 0.16g / cm 3 .

specific Embodiment 3

[0012] The invention discloses a method for producing cool-feeling honeycomb fiber, which comprises adding high heat-conducting nano-silicon carbide powder into the pulp of honeycomb fiber at a weight ratio of 1.5%, stirring evenly, and flashing out filaments to form the honeycomb fiber. The pulp of the honeycomb fiber is: bamboo charcoal fiber.

[0013] Preferably, the crystal form of the nano-silicon carbide powder is mixed crystal, the color is white, the average particle size is 28nm, the purity is 99.96, and the specific surface area is 43.2m 2 / g, the bulk density is 0.16g / cm 3 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Bulk densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for producing cool sense honeycomb fibers. The method comprises the following steps: adding high-thermal-conductivity nano silicon carbide powder into master batch or pulp of honeycomb fibers according to a weight ratio of 1-2 percent, uniformly stirring, performing steam explosion on yarns, and preparing the honeycomb fibers. The invention discloses a technical method for improving a cool effect of the honeycomb fibers by changing heat-conducting property of thermal resistance enhanced fibers of the honeycomb fibers by using silicon carbide and the like, and the high-thermal-conductivity nano silicon carbide powder is added into the honeycomb fibers according to a ratio being about 1-2 percent, so that the thermal conductivity of the fibers can be improved from the original 0.1 to 2.0-3.8, and the thermal conductivity is improved by 20-40 times. The method has the characteristics that the addition amount is low, an effect of obviously improving the mechanical property of the product is achieved, the heat-conducting effect is obviously improved, and the like. Moreover, the original excellent performance of the honeycomb fibers is not changed. The clothing made of the fibers has obvious low thermal resistance and low damp obstruction characteristics, and the fiber is a special cool fiber.

Description

technical field [0001] The invention specifically relates to a production method of cool-feeling honeycomb fiber. Background technique [0002] The fabric made of honeycomb structure fiber does not need to be finished (that is, it does not need to use any chemical additives to finish the fabric to achieve the purpose of moisture absorption and quick drying, anti-pilling and soft and lubricating), and the more it is used, the softer it is. Very good dimensional stability, no shrinkage and deformation. Therefore, it can not only greatly reduce the pollution to the environment caused by the discharge of a large number of chemical additives due to the need for finishing, but more importantly, it can protect the human skin from the direct damage of chemical substances attached to the clothes. High safety performance. According to the actual operation test, the fabric made of honeycomb structure fiber is compared with the cotton fabric, the moisture absorption speed is 1~2 times...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F1/10D01D5/11
Inventor 汪明星陈永兵
Owner VIOLET HOME TEXTILE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com