Water-borne epoxy resin flooring paint, flooring and construction process of water-borne epoxy resin flooring paint

A water-based epoxy resin and floor technology, used in epoxy resin coatings, coatings, polyurea/polyurethane coatings, etc., to achieve high compressive strength and superior chemical resistance.

Active Publication Date: 2014-03-12
中山市诚美涂料有限公司
View PDF5 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are many kinds of floor coatings. Epoxy floor coatings have become the fastest-growing variety of floor coatings because of their excellent chemical resistance, smoothness, smoothness, strong decoration, and high market recognition. The main types are whether Solvent self-leveling type, high solid solvent type, conductive type, colored mortar type and water-based epoxy floor coatings, etc. At present, the anti-slip property is the main factor limiting the use of floor coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-borne epoxy resin flooring paint, flooring and construction process of water-borne epoxy resin flooring paint
  • Water-borne epoxy resin flooring paint, flooring and construction process of water-borne epoxy resin flooring paint
  • Water-borne epoxy resin flooring paint, flooring and construction process of water-borne epoxy resin flooring paint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A kind of waterborne epoxy resin floor construction technology, it comprises the following steps:

[0037] 1) Mix 60 parts by mass of epoxy resin, 2 parts by mass of pigment, 18 parts by mass of filler, and 20 parts by mass of water-based additive A, and stir for 20 minutes at a speed of 700r / min to obtain Component A; The epoxy resin curing agent is mixed according to the mass ratio of 1:2.5, stirred for 10 minutes, and the speed is 600r / min to obtain the primer;

[0038] The pigment is rutile titanium dioxide;

[0039] The filler is cement;

[0040] The water-based additive A contains 602N dispersant, TC-3 preservative, 738 hand feeling agent, and 245 wetting agent.

[0041] 2) Mix the primer and water at a mass ratio of 1:1. After stirring evenly, roll or scrape the surface of the substrate to form a primer.

[0042] 3) Mix 50 parts by mass of primer, 50 parts by mass of water, and 100 parts by mass of stone aggregate, and stir for 10 minutes at a speed of 600r / mi...

Embodiment 2

[0046] A kind of waterborne epoxy resin floor construction technology, it comprises the following steps:

[0047] 1) Mix 75 parts by mass of epoxy resin, 2 parts by mass of pigment, 18 parts by mass of filler, and 5 parts by mass of water-based additive A, and stir for 30 minutes at a speed of 600r / min to obtain component A; The epoxy resin curing agent is mixed according to the mass ratio of 1:2.5, stirred for 20 minutes, and the speed is 500r / min to obtain the primer;

[0048] The pigment is an iron oxide pigment;

[0049] The filler is a mixture of quartz powder, ground calcium carbonate and kaolin;

[0050] The water-based additive A contains 5040 dispersant, 2060 preservative, 738 hand feeling agent, and CF-10 wetting agent.

[0051] 2) Mix the primer and water at a mass ratio of 1:1. After stirring evenly, roll or scrape the surface of the substrate to form a primer.

[0052] 3) Mix 70 parts by mass of primer, 30 parts by mass of water, and 140 parts by mass of stone ...

Embodiment 3

[0056] A kind of waterborne epoxy resin floor construction technology, it comprises the following steps:

[0057] 1) Mix 70 parts by mass of epoxy resin, 3 parts by mass of pigment, 21 parts by mass of filler, and 6 parts by mass of water-based additive A, and stir for 25 minutes at a speed of 650r / min to obtain Component A; The epoxy resin curing agent is mixed according to the mass ratio of 1:2.5, stirred for 15 minutes, and the speed is 550r / min to obtain the primer;

[0058] The pigment is a phthalocyanine pigment;

[0059] The filler is a mixture of cement, quartz powder, ground calcium carbonate, kaolin, barium sulfate, and mica powder;

[0060] The water-based additive A contains 5040 dispersant, 2060 preservative, 738 hand feeling agent, CF-10 wetting agent, C12 film-forming aid, SN-243 grinding aid, AF2130 anti-fungal agent, 805 defoamer, B Diol, L117 thickener.

[0061] 2) Mix the primer and water at a mass ratio of 1:1. After stirring evenly, roll or scrape the s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a water-borne epoxy resin flooring paint, and belongs to the technical field of chemical materials. The water-borne epoxy resin flooring paint comprises finishing paint and priming paint, the finishing paint comprises the following components in parts by mass (100 parts in total): 73-80 parts of polyurethane, 20-27 parts of water-borne auxiliary B, the 20-27 parts of water-borne auxiliary B contains 5-8 parts by mass of dispersing agent, 2-3 parts by mass of preservative, 5-8 parts by mass of feeling agent and 5-8 parts by mass of wetting agent; the priming paint comprises a component A, an epoxy resin hardener in a mass ratio of 1: 2.5, the component A (100 parts in total) comprises 60-75 parts by mass of epoxy resin, 2-3 parts by mass of pigment, 18-21 parts by mass of filler, and 1-20 parts by mass of water-boron auxiliary A; and the water-boron auxiliary A comprises the dispersing agent, the preservative, the feeling agent and the wetting agent. According to the water-boron epoxy resin flooring paint, the problem that the existing flooring paint is bad in skid resistance is overcome.

Description

technical field [0001] The invention relates to building floor materials, in particular to a water-based epoxy resin floor paint; the invention also relates to an epoxy resin floor and a construction process thereof. Background technique [0002] As a new type of building material, floor coatings are one of the types of coatings that have grown rapidly with the development of the construction industry in recent years. They are widely used in the coating of floors in factories, hospitals, schools, offices and large public places. At present, there are many kinds of floor coatings. Epoxy floor coatings have become the fastest-growing variety of floor coatings because of their excellent chemical resistance, smoothness, smoothness, strong decoration, and high market recognition. The main types are whether Solvent self-leveling type, high solid solvent type, conductive type, colored mortar type and water-based epoxy floor coating, etc., the current anti-skid property is the main ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/04C09D7/12C09D163/00C04B26/14E04F15/12
Inventor 许锦雄
Owner 中山市诚美涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More