High-brightness aluminum-alloy polishing section and production process thereof
A production process and technology of aluminum profiles, applied in anodizing, electrolytic coatings, surface reaction electrolytic coatings, etc., can solve the problems of difficult research and development, low surface brightness of profiles, and difficult brightness of 6463 aluminum alloy profiles, and achieve surface corrosion. The effect of fewer defects
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0027] Example 1
[0028] Use the following steps to prepare aluminum alloy polished profiles:
[0029] (1) Melting and casting: Melting molten aluminum, casting the molten aluminum into aluminum rods;
[0030] You can use 80% (mass) of aluminum ingots and the remaining leftovers (the leftovers left after the aluminum rods are extruded by the extruder) to melt the aluminum liquid; then add silicon, magnesium and other alloys to it The ingredients are adjusted so that the mass content of the following chemical elements contained in the molten aluminum is Si 0.32~0.36%, Mg1.2~1.24%, Fe≤0.18, Zn≤0.1, Cu0.04~0.07%, Mn≤ 0.03%, Cr≤0.005%, Ti≤0.05%, Sn≤0.003%, Pb≤0.001%; after refining and slagging, the molten aluminum is allowed to stand and its composition is stable, then the molten aluminum is cast into aluminum rods.
[0031] (2) Extrusion: The aluminum rod cast in step 1 is fed into the extruder, the temperature of the aluminum rod is controlled to 450℃~470℃, and the temperature of t...
Example Embodiment
[0039] Example 2
[0040] Use the following steps to prepare aluminum alloy polished profiles:
[0041] (1) Melting and casting: basically the same as in Example 1, and will not be repeated;
[0042] (2) Extrusion: The aluminum rod cast in step 1 is sent to the extruder, the temperature of the aluminum rod is controlled to 460℃~480℃, and the temperature of the aluminum extrusion die in the extruder is controlled to 440~470℃ , The aluminum rod is extruded by an extruder to form an aluminum profile, the discharge temperature of the aluminum profile is about 490℃, and the wall thickness of the aluminum profile obtained by extrusion is about 2.0mm;
[0043] (3) Use a polishing machine to mechanically polish the aluminum profile;
[0044] (4) Degreasing: At room temperature, use an AC degreasing agent with a mass content of 8% in the degreasing tank to degrease the aluminum profile, and the processing time is 1 to 2 minutes;
[0045] (5) Dewaxing: At 60°C, use a solution with a wax dewaxing ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap