Partially-etched precision stainless steel strip used in communication industry as well as production process and application thereof

A stainless steel strip and production process technology, applied in the direction of tension/pressure control, roll speed control, metal rolling, etc., can solve the problems of parts scrapping, not fully meeting the production requirements of precision stainless steel parts, and the precision stainless steel strip is easy to be seriously deformed, etc.

Active Publication Date: 2012-10-03
YONGXIN PRECISION MATERIAL WUXI
View PDF8 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The precision stainless steel strips produced by the above two methods are easily deformed severely during half-etching stamping, resulting in the scrapping of parts, which cannot fully meet the production requirements of precision stainless steel parts.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Partially-etched precision stainless steel strip used in communication industry as well as production process and application thereof
  • Partially-etched precision stainless steel strip used in communication industry as well as production process and application thereof
  • Partially-etched precision stainless steel strip used in communication industry as well as production process and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0099] In this example, the selected grade is the surface of SUS304 cold-rolled raw material coil 2B, with a thickness of 0.60mm and a width of 400mm. Requirements for finished steel strips: thickness 0.30mm, width 125+125+128 each, tensile strength ≥ 930Mpa, Vickers hardness HV310-370, elongation ≥ 3%, semi-etched without deformation.

[0100] (1) First select SUS304 cold-rolled raw material coil, the surface is in 2B state, chemical composition: carbon (C) 0.05%, silicon (Si) 0.41%, manganese (Mn) 1.3%, phosphorus (P) 0.045%, sulfur (S ) 0.028%, nickel (Ni) 8.03%, chromium (Cr) 18.1%, copper (Cu) 0.13%, nitrogen (N) 0.029%, molybdenum (Mo) 0.01%.

[0101] (2) For the stainless steel cold-rolled raw material coil with a thickness of 0.60mm, use Sendzimir 20-roll mill for semi-finish rolling, and use Guohong Lubricating Oil (China) Co., Ltd. model DN.STAINLESS ROLLP-T mineral rolling during rolling Make oil for lubrication and cooling, control the oil temperature at 25°C duri...

Embodiment 2

[0117]In this example, the cold-rolled raw material coil of brand SUS304 is selected, the surface is in 2B state, the thickness is 0.90mm, the width is 400mm, the thickness of the finished steel strip is 0.50mm, the coil degree is 128+128+125mm each, and the tensile strength is ≥930Mpa. Vickers hardness HV310 ~ 370, elongation ≥ 3%, half-etching requires no deformation.

[0118] (1) First select SUS304 cold-rolled stainless steel raw material coil, the surface is in 2B state. Chemical composition: with embodiment 1.

[0119] (2) For the stainless steel cold-rolled raw material coils with a thickness of 0.90mm, a 20-roll Sendzimir rolling mill is used for semi-finish rolling. During rolling, the model DN.STAINLESSROLL OIL P-T mineral rolling oil produced by Guohong Lubricating Oil (China) Co., Ltd. is used for lubrication and cooling. The oil temperature is controlled at 50°C during rolling, and the hardness of the work roll surface is selected to be HRC62. The surface roughn...

Embodiment 3

[0135] In this example, the cold-rolled raw material coil of brand SUS304 is selected, the surface is in 2B state, its thickness is 1.50mm, and its width is 400mm. Vickers hardness HV310 ~ 370, elongation ≥ 3%, half-etching requires no deformation.

[0136] (1) First select SUS304 cold-rolled stainless steel raw material coil, the surface is in 2B state. Chemical composition: with embodiment 1.

[0137] (2) For the stainless steel cold-rolled raw material coils with a thickness of 1.50mm, a 20-roller Sendzimir is used for semi-finish rolling. During rolling, DN.STAINLESSROLL OIL P-T mineral rolling oil produced by Guohong Lubricating Oil (China) Co., Ltd. is used for lubrication and cooling. The oil temperature is controlled at 30°C during rolling, and the hardness of the work roll surface is selected to be HRC61. The surface roughness of the roll is controlled at Ra0.10μm, and the shape control roll selects a cone length of 270mm and a taper of 1 / 850. Then the 1.5mm thick ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
surface roughnessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a production method of a partially-etched precision stainless steel strip, which comprises the following steps: semi-finish rolling; degreasing, washing and drying; solution heat treatment; tension rewinding; finish rolling; degreasing, cleaning and drying; micro extending, straightening and bundling. Due to the implementation of the technical scheme of the production process, the product has high thickness tolerance precision, low fluctuation, smooth surface, uniform surface roughness and no surface color difference. The plate is flat, has stable mechanical performance, is not easy to deform after being partially etched and can met the needs of producing the intelligent mobile phones in the communication industry.

Description

technical field [0001] The invention relates to the field of precision stainless steel strips, in particular, the invention relates to a semi-etched precision stainless steel strip, its production process and its application. Background technique [0002] Strip steel is a common metal product. Precision stainless steel strip is a kind of steel strip with high technical content. It can not only have precise dimensions, but also can guarantee the required mechanical performance indicators. The thickness of the finished steel strip can be as thin as 0.02mm, and the width can reach 1250mm; Hardness (Vickers) can be controlled in the range of 135-600. [0003] Precision stainless steel belt (generally refers to products with a thickness less than 0.5mm) is widely used in industries with special needs such as information technology, computers, auto parts, medical treatment, metal hoses, semiconductors, etc., and is a high value-added product. Therefore, the production of precisi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B21B1/22B21B37/48B21B37/46C21D8/02
Inventor 濮晓芳
Owner YONGXIN PRECISION MATERIAL WUXI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap