Preparation method of electroconductive silicone rubber

A conductive silicon and rubber technology, applied in the field of silicone rubber, can solve the problems of poor thermal conductivity and the limitation of conductive silicone rubber, and achieve the effects of large conductive current, heat resistance and compressibility, and good adhesion

Active Publication Date: 2014-03-26
广东长博电子绝缘材料有限公司
View PDF2 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the conductivity of general silicone rubber can meet the requirements, but conduction will generate heat, and the thermal conductivity of general silicone rubber is relatively poor, so that the use of conductive silicone rubber is limited. The method of the present invention can overcome the above application limitations

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment １

[0033] A kind of preparation method of conductive silicone rubber of the present invention, comprises the following steps:

[0034] (1) Mix acetylene carbon black, aluminum oxide, hydroxy silicone oil and water accounting for 1% of the weight of the acetylene carbon black, and then add it to a granulator to make acetylene carbon black and aluminum oxide particles with a diameter of 0.5-0.8mm;

[0035] (2) Mixing raw silicone rubber;

[0036] (3) Add white carbon black, quartz powder, zinc stearate, liquid silicone rubber, acetylene carbon black and aluminum oxide mixed particles, structure inhibitor, and vinyl-containing silane coupling agent in sequence;

[0037] (4) Add vulcanizing agent and knead for 5-10 minutes to obtain conductive silicone rubber.

[0038] The particle size of aluminum oxide in step (1) is 2000-8000 mesh.

[0039] Structural inhibitors are hexamethylcyclotrisilazane, diphenylsilanediol.

[0040] The vinyl-containing silane coupling agent is methylviny...

Embodiment 2

[0058] A kind of preparation method of conductive silicone rubber of the present invention, comprises the following steps:

[0059] (1) Mix acetylene carbon black, aluminum oxide, hydroxy silicone oil and water accounting for 1% of the weight of the acetylene carbon black, and then add it to a granulator to make acetylene carbon black and aluminum oxide particles with a diameter of 0.5-0.8mm;

[0060] (2) Mixing raw silicone rubber;

[0061] (3) Add white carbon black, quartz powder, zinc stearate, liquid silicone rubber, acetylene carbon black and aluminum oxide mixed particles, structure inhibitor, and vinyl-containing silane coupling agent in sequence;

[0062] (4) Add vulcanizing agent and knead for 5-10 minutes to obtain conductive silicone rubber.

[0063] The particle size of aluminum oxide in step (1) is 2000-8000 mesh.

[0064] The structural inhibitor is methylphenyldiethoxysilane.

[0065] The vinyl-containing silane coupling agent is methylvinyl organopolysiloxa...

Embodiment 3

[0083] A kind of preparation method of conductive silicone rubber of the present invention, comprises the following steps:

[0084] (1) Mix acetylene carbon black, aluminum oxide, hydroxy silicone oil and water accounting for 1% of the weight of the acetylene carbon black, and then add it to a granulator to make acetylene carbon black and aluminum oxide particles with a diameter of 0.5-0.8mm;

[0085] (2) Mixing raw silicone rubber;

[0086] (3) Add white carbon black, quartz powder, zinc stearate, liquid silicone rubber, acetylene carbon black and aluminum oxide mixed particles, structure inhibitor, and vinyl-containing silane coupling agent in sequence;

[0087] (4) Add vulcanizing agent and knead for 5-10 minutes to obtain conductive silicone rubber.

[0088] The particle size of aluminum oxide in step (1) is 2000-8000 mesh.

[0089] The structural inhibitor is hexamethylcyclotrisilazane.

[0090] The vinyl-containing silane coupling agent is methylvinyl organopolysiloxa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Particle sizeaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of electroconductive silicone rubber. Acetylene black, aluminum oxide, hydroxyl silicone oil and water accounting for 1% of the acetylene black by weight are mixed and added into a granulator to be produced into acetylene black and aluminum oxide particles for mixing. The silicone rubber has the advantages of high heat conductivity, heat resistance and low compressibility, the tensile strength is larger than 9.6 MPa, the tear strength is above 36 N / mm, and the volume resistivity is smaller than 45 omega.cm.

Description

technical field [0001] The invention relates to the technical field of silicone rubber, in particular to a preparation method of conductive silicone rubber. Background technique [0002] Silicone rubber has excellent heat resistance, low temperature resistance, insulation, shock resistance, compression resistance, wear resistance and good biological characteristics, making it widely used in construction, transportation, electronic appliances, chemicals, biological materials and aerospace materials. [0003] The currently used conductive silicone rubber generally adds reinforcing agents, conductive additives, coupling agents, and vulcanizing agents to methyl vinyl silicone rubber to meet electrical and mechanical performance requirements. However, the conductivity of general silicone rubber can meet the requirements, but conduction will generate heat, and the thermal conductivity of general silicone rubber is relatively poor, so that the use of conductive silicone rubber is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L83/04C08K13/06C08K9/06C08K3/04C08K3/22C08K3/36C08K5/098
Inventor 尤晓明李洋张国栋王显涛延云峰魏文祥
Owner 广东长博电子绝缘材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com