An antibacterial coating and nanotechnology, applied in antifouling/underwater coatings, coatings, paints containing biocides, etc., can solve the problems of easy breeding of bacteria, poor stability and long-term effect, limited antibacterial effect, etc. The effect of breeding and reproduction, simple production process and good compatibility
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0018] A new type of nano antibacterial paint, which is composed of nano titanium dioxide, resin, hardener, pigment, acrylic emulsion and water, and the weight parts of each component are as follows:
[0019]
[0020] The particle size of the above-mentioned nano titanium dioxide is between 10-90 nm.
[0021] The above-mentioned curing agent is a polyamide curing agent.
[0022] When preparing, the components can be blended according to the conventional method in the field. Take the new nano antibacterial coating prepared in this example, and test with reference to GB15981-1995, Q / 02GZS001 test method and standard. The result shows that Calculated by the number of colonies, the antibacterial coating of the present invention has an antibacterial rate of 91% against Escherichia coli and 92% against Staphylococcus aureus.
Embodiment 2
[0024] A new type of nano antibacterial paint, which is composed of nano titanium dioxide, resin, hardener, pigment, acrylic emulsion and water, and the weight parts of each component are as follows:
[0025]
[0026] The particle size of the above-mentioned nano titanium dioxide is between 10 nm and 90 nm.
[0027] The above-mentioned curing agent is a polyamide curing agent.
[0028] When preparing, the components can be blended according to the conventional method in the field. Take the new nano antibacterial coating prepared in this example, and test with reference to GB15981-1995, Q / 02GZS001 test method and standard. The result shows that Calculated by the number of colonies, the antibacterial coating of the present invention has an antibacterial rate of 90% against Escherichia coli and 90% against Staphylococcus aureus.
Embodiment 3
[0030] A new type of nano antibacterial paint, which is composed of nano titanium dioxide, resin, hardener, pigment, acrylic emulsion and water, and the weight parts of each component are as follows:
[0031]
[0032] The particle size of the above-mentioned nano titanium dioxide is between 10 nm and 90 nm.
[0033] The above-mentioned curing agent is a polyamide curing agent.
[0034] When preparing, the components can be blended according to the conventional method in the field. Take the new nano antibacterial coating prepared in this example, and test with reference to GB15981-1995, Q / 02GZS001 test method and standard. The result shows that Calculated by the number of colonies, the antibacterial coating of the present invention has an antibacterial rate of 91% against Escherichia coli and 91% against Staphylococcus aureus.
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
antibacterial rate | aaaaa | aaaaa |
antibacterial rate | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com