Dipping solution formula of industrial canvas and preparation process thereof

A preparation process and technology of dipping solution, applied in the field of dipping solution formulation of industrial canvas and its preparation process, can solve the problems of poor adhesion between fiber skeleton material and rubber, release toxic gas, etc. Environmental hazards, improved adhesion, reduced release of toxic substances

Active Publication Date: 2014-04-30
ANHUI HUAYE ADVANCED MATERIALS CO LTD
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a formula of dipping solution for industrial canvas and its preparation process, so as to overcome the poor adhesion between fiber skeleton material and rubber and the release of toxic substances during the dipping process in the prior art. lack of gas

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A dipping solution formula for industrial canvas and a preparation process thereof, which includes a first bath formula and a second bath formula, and the formula is as follows in parts by weight:

[0039] (1) The first bath recipe includes the following:

[0040] ①The formula of isocyanate solution is:

[0041] soft water 260,

[0042] Isocyanate 25;

[0043] ② The formula of dipping solution is:

[0044] soft water 700,

[0045] epoxy resin 12;

[0046] Isocyanate solution 285,

[0047] Sodium hydroxide 0.1;

[0048] (2) The formula for the second bath includes the following:

[0049] ①The formula of RF fluid is:

[0050] soft water 340,

[0051] Sodium hydroxide 1.3,

[0052] Resorcinol 21,

[0053] Formaldehyde 16,

[0054] 2-Chloromethylthiobenzothiazole 25;

[0055] ② The formula of the second-bath dipping solution is:

[0056] soft water 180,

[0057] Sodium hydroxide 0.8,

[0058] Butylpyrrolate latex 430,

[0059] Ammonia 30,

[0060] RF Flui...

Embodiment 2

[0067] A dipping solution formula for industrial canvas and a preparation process thereof, which includes a first bath formula and a second bath formula, and the formula is as follows in parts by weight:

[0068] (1) The first bath recipe includes the following:

[0069] ①The formula of isocyanate solution is:

[0070] soft water 300,

[0071] Isocyanate 30;

[0072] ② The formula of the one-bath dipping solution is:

[0073] soft water 730,

[0074] epoxy resin 15;

[0075] Isocyanate solution 330,

[0076] Sodium hydroxide 0.3;

[0077] (2) The formula for the second bath includes the following:

[0078] ③ The formula of RF fluid is:

[0079] soft water 400,

[0080] Sodium Hydroxide 2.0,

[0081] Resorcinol 25,

[0082] Formaldehyde 24,

[0083] 2-Chloromethylthiobenzothiazole 30;

[0084] ④ The formula of the second-bath dipping solution is:

[0085] soft water 200,

[0086] sodium hydroxide 1,

[0087] Butylpyrrolate latex 450,

[0088] Ammonia 35,

...

Embodiment 3

[0094] A dipping solution formula for industrial canvas and a preparation process thereof, which includes a first bath formula and a second bath formula, and the formula is as follows in parts by weight:

[0095] (1) The first bath recipe includes the following:

[0096] ①The formula of isocyanate solution is:

[0097] soft water 250,

[0098] Isocyanate 20;

[0099] ② The formula of the one-bath dipping solution is:

[0100] soft water 680,

[0101] epoxy resin 10;

[0102] Isocyanate solution 270,

[0103]Sodium hydroxide 0.1;

[0104] (2) The formula for the second bath includes the following:

[0105] ① The formula of resorcinol formaldehyde resin solution (referred to as RF solution) is:

[0106] soft water 300,

[0107] Sodium Hydroxide 1.0,

[0108] Resorcinol 15,

[0109] Formaldehyde 20,

[0110] 2-Chloromethylthiobenzothiazole 20;

[0111] ② The formula of the second-bath dipping solution is:

[0112] soft water 150,

[0113] Sodium hydroxide 0.5, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention aims to provide a dipping solution formula of an industrial canvas and a preparation process thereof. The dipping solution formula comprises a first bath formula and a second bath formula. The dipping solution formula and the preparation process have the beneficial effects that 2-chloromethylthiobenzothiazole is added to a two-bath dipping solution, so that unreacted resorcinol is etherified through etherification reaction, thus the content of free resorcinol is less than 1% and the harms to workshop workers and the environment are reduced; during dipping solution preparation, an organic solvent serves as a carrier to form a solvent type dipping system, so that high tenacity of the canvas can be ensured while endowing the canvas with high degree of adhesion, thus forming a product with high added values; release of toxic substances in the dipping process is reduced and the environment is protected by adopting the environment-friendly dipping system.

Description

technical field [0001] The invention relates to the technical field of sizing material for impregnating chemical fiber and synthetic fiber fabrics, in particular to a formula of dipping liquid for industrial canvas and a preparation process thereof. Background technique [0002] In recent years, the emergence of new high-performance synthetic fiber materials has accelerated the development of industrial canvas materials, but how to further improve the bonding performance between fiber skeleton materials and rubber has always been a difficult issue. In the traditional dipping system, RFL dipping solution is used, that is, resorcinol-formaldehyde-latex dipping system, and isocyanate is added as a crosslinking agent. Since the cohesive energy density of polyester is not like that of RF resin, the molecular contact between RFL dipping solution and polyester phase is poor. Moreover, resorcinol is easy to volatilize in a high temperature environment, which not only reduces the co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/693D06M15/55D06M13/395D06M11/38D06M13/127D06M13/352D06M11/60
Inventor 周业昌欧正清
Owner ANHUI HUAYE ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap