Hexaphenoxy cyclotriphosphazene-containing composite flame-retardant cable material and preparation method thereof

A hexaphenoxycyclotriphosphazene and composite flame-retardant technology, which is applied in the direction of insulating cables, cables, circuits, etc., can solve the problems of poor compatibility, reduce the mechanical properties and processing properties of materials, and achieve increased fluidity and improved Mechanical properties, processing properties, and the effect of low smoke generation

Inactive Publication Date: 2014-05-21
SHANGHAI UNIV +1
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although the traditional magnesium hydroxide and aluminum hydroxide flame retardants can endow the material with good flame retardancy, however, since the matrix resin of most cable materials is a non-polar polyolefin polymer, the polar hydrogen The compatibility of magnesium oxide and aluminum hydroxide is poor, which often reduces the mechanical properties and processing properties of materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hexaphenoxy cyclotriphosphazene-containing composite flame-retardant cable material and preparation method thereof
  • Hexaphenoxy cyclotriphosphazene-containing composite flame-retardant cable material and preparation method thereof
  • Hexaphenoxy cyclotriphosphazene-containing composite flame-retardant cable material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Embodiment one: each component and mass percentage thereof are as follows:

[0034]

[0035] The sheet or plate molding preparation method of the above-mentioned cable material, the preparation method steps are as follows:

[0036] Compounding is carried out according to the total weight of 200g, 60g of LDPE, 40g of ethylene-vinyl acetate copolymer, and 2g of hexaphenoxycyclotriphosphazene are mixed to obtain mixture A.

[0037] 66 g of magnesium hydroxide and 32 g of aluminum hydroxide were uniformly mixed to obtain mixture B.

[0038] Put the mixture A into the internal mixer for banburying, and set the material temperature to 160°C; after banburying for 5 minutes, add the mixture B to the internal mixer to continue the banburying, set the material temperature to 160°C, and banbury for 10 minutes to obtain a total of mixture.

[0039] Put the above-prepared blend into an open plastic mixer for kneading, the material temperature is set at 180°C, kneading is carrie...

Embodiment 2

[0041] Embodiment two: contained component and mass percentage thereof are as follows:

[0042]

[0043] The preparation method of the above-mentioned cable material is the same as that of Example 1, and a performance testing test is carried out, and the results are shown in Table 1.

Embodiment 3

[0044] Embodiment three: contained component and mass percent thereof are as follows:

[0045]

[0046] The preparation method of the above-mentioned cable material is the same as that of Example 1, and a performance testing test is carried out, and the results are shown in Table 1.

[0047] Table 1 :

[0048]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a hexaphenoxy cyclotriphosphazene-containing composite flame-retardant cable material and a preparation method thereof. The cable material adopts exaphenoxy cyclotriphosphazene, magnesium hydroxide and aluminum hydroxide as fire retardants to improve the residual rate at a high temperature and improve the thermal stability and the flame retardant property of the cable material; the cable material has the characteristic of low smoke quantity, does not contain toxic substances such as lead, antimony and the like, and is green and environment-friendly; the exaphenoxy cyclotriphosphazene can reduce the filling amount of the magnesium hydroxide and the aluminum hydroxide, improve the flame retardant property of the material and increase the mechanical property of the materials; and the lubricating agent can improve the processability of the material; and therefore, the cable material is a novel high-efficiency flame-retardant cable material.

Description

technical field [0001] The invention relates to a composite flame-retardant cable material and a preparation method thereof, in particular to a composite flame-retardant cable material containing hexaphenoxycyclotriphosphazene and a preparation method thereof. Background technique [0002] Wire and cable have the function of power transmission and information transmission, and play an important role in people's life and production. Designing and preparing low-smoke, low-toxic cable materials with excellent flame-retardant and insulating properties has become a hot spot in flame-retardant research today. [0003] Although the traditional magnesium hydroxide and aluminum hydroxide flame retardants can endow the material with good flame retardancy, however, since the matrix resin of most cable materials is a non-polar polyolefin polymer, the polar hydrogen The compatibility of magnesium oxide and aluminum hydroxide is poor, which often reduces the mechanical properties and pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08H01B3/44H01B7/295C08K5/5399C08K3/22
CPCC08L23/06C08L2201/02C08L2203/202C08L2207/066H01B3/441
Inventor 郭强钱君质李夏郭丹丹毕宸洋刘隽
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap