Method for preparing pectinate organic silicon-modified polyurethane grafted ethylene-vinyl acetate (EVA) water emulsion
A water-based emulsion, polyurethane technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve problems such as never before, and achieve the effect of good waterproof performance, good weather resistance, and high peel strength
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0022] Example 1
[0023] A certain amount of polyethylene glycol 1000 is added to the three-necked flask, the temperature is raised to 100°C, the water in the system is removed by vacuum, and the temperature is lowered for later use.
[0024] Add 222gIPDI into a three-necked flask, start stirring, heat up to 70°C, add dry 500g polyethylene glycol 1000, after 30min drop completion, continue the reaction, add 100ml acetone to the system for dilution, adjust the viscosity; React for 2.5h at ℃, measure the value of -NCO, and meet the requirements.
[0025] According to the molar ratio of NCO:N-methyldiethanolamine 4:1, drop N-methyldiethanolamine into it, continue the reaction, and check the value of NCO. After reaching the requirement, follow the N-methyldiethanolamine:HCl=1:0.9 A 10% aqueous hydrochloric acid solution was added dropwise with a molar ratio of 10% at a stirring speed of 700r / min. After reaction for 1 hour, a vacuum pump was used to remove acetone at room temperature to...
Example Embodiment
[0029] Example 2
[0030] Add 1000g polyethylene glycol 2000 to a three-necked flask, heat to 100°C, vacuum to remove the water in the system, cool to 80°C, turn on the stirring, add 222gIPDI to the three-necked flask, and then slowly lower the temperature to 70°C, the reaction process According to the viscosity change, add 80-120ml acetone to the system for dilution and adjust the viscosity; after 2.5 hours of reaction, the value of -NCO is measured until the requirement is reached, and the reaction is stopped.
[0031] According to the molar ratio of NCO:N-methyldiethanolamine of 4:1, drop N-methyldiethanolamine, continue the reaction, check the value of NCO, and drop according to the molar ratio of N-methyldiethanolamine:HCl=1:1 Add a 10% aqueous hydrochloric acid solution, stir quickly at a stirring speed of 800r / min, react for 1h, and use a vacuum pump to remove acetone at room temperature to obtain cationic aqueous polyurethane. The pH of the solution is 7-7.3.
[0032] Detect...
Example Embodiment
[0035] Example 3
[0036] Add 1000g polyethylene glycol 2000 to a three-necked flask, heat to 100°C, vacuum to remove the water in the system, cool to 80°C, turn on the stirring, add 168g 1,6 hexamethylene diisocyanate to the three-necked flask, and then slowly lower the temperature to At 70°C, during the reaction process, according to the viscosity change, add 60-100ml acetone to the system for dilution and adjust the viscosity; after the reaction for 2.5h, measure the -NCO value until the requirement is reached, stop the reaction.
[0037] According to the molar ratio of NCO:N-methyldiethanolamine of 4:1, drop N-methyldiethanolamine, continue the reaction, check the value of NCO, and drop according to the molar ratio of N-methyldiethanolamine:HCl=1:0.9 Add 10% hydrochloric acid aqueous solution, stirring speed 1000r / min, after 1h reaction, use vacuum pump to remove acetone at room temperature to obtain cationic waterborne polyurethane, and the pH value of the solution is 7-7.3.
...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap