CPVC for power cable sleeve and preparation method thereof

A technology of power cable and CPVC resin, which is applied in the field of CPVC for power cable casing and its preparation, can solve the problems of complex mixing process, excellent formulation, high cost, etc., and achieve simple mixing process, good weather resistance and flame retardancy Good results

Active Publication Date: 2014-07-02
山东高信化学股份有限公司
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, CPVC materials have been used to prepare power cable casings in China, but there are generally problems such as unstable product performance, difficult processing, high cost, and complicated mixing process, which prevents CPVC pipes from being widely used.
[0003] At present, the CPVC power cable pipe material formulations on the market are basically produced abroad, with good processing performance and stable performance indicators, but the price is generally high; while the development of domestic CPVC power cable formulations started late and the level is low , which makes the processing of domestic formula materials difficult and the performance index of the product is low
The domestic production of CPVC formulations basically follows the PVC formulation technology, and the additives used are also common additives for processing PVC. There is no special additive developed according to the characteristics of CPVC materials, so it is impossible to prepare formulations with excellent performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • CPVC for power cable sleeve and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Embodiment 1: A kind of CPVC for power cable casing, comprising:

[0026] 50 parts of CPVC resin, a special resin for pipes prepared by the aqueous phase suspension method, with a chlorine content of 76% and a degree of polymerization of 700;

[0027] 30 parts of PVC resin, SG-5 resin for pipes;

[0028] 2.5 parts of stabilizer, which is a calcium-zinc composite stabilizer;

[0029] 2 parts lubricating impact modifier, chlorinated polyethylene with 30% chlorine content;

[0030] 2 parts of lubricated processing aid, PA101;

[0031] 10 parts filler, which is light calcium carbonate;

[0032] 0.02 part of pigment is molybdenum chrome red pigment.

[0033] After mixing the above components by weight, first add CPVC resin and PVC resin to the high mixer, then add stabilizer when the heat is mixed to 60°C, add anti-impact agent and processing aid when it reaches 70°C, Add fillers and pigments at the same time, put it in the cold mixing pot when it is hot mixed to 110°C,...

Embodiment 2

[0034] Embodiment 2: A kind of CPVC for power cable casing, comprising:

[0035] 50 parts of CPVC resin, a special resin for pipes prepared by the aqueous phase suspension method, with a chlorine content of 76% and a degree of polymerization of 800;

[0036] 30 parts of PVC resin, SG-5 resin for pipes;

[0037] 2.5 parts of stabilizer, which is a 1:1 mixture of calcium-zinc composite stabilizer and organotin stabilizer;

[0038] 2 parts lubricating impact modifier, chlorinated polyethylene with 30% chlorine content;

[0039] 2 parts of lubricated processing aid, PA101;

[0040] 10 parts filler, which is light calcium carbonate;

[0041] 0.02 part of pigment is iron red pigment.

[0042] After mixing the above components by weight, first add CPVC resin and PVC resin to the high mixer, then add stabilizer when the heat is mixed to 60°C, add anti-impact agent and processing aid when it reaches 70°C, Add fillers and pigments at the same time, put it in the cold mixing pot whe...

Embodiment 3

[0043] Embodiment 3: A kind of CPVC for power cable casing, comprising:

[0044] 50 parts of CPVC resin, a special resin for pipes prepared by the aqueous phase suspension method, with a chlorine content of 76% and a polymerization degree of 1000;

[0045] 30 parts of PVC resin, SG-5 resin for pipes;

[0046] 2.5 parts of stabilizer, which is organotin stabilizer;

[0047] 2 parts lubricating impact modifier, chlorinated polyethylene with 30% chlorine content;

[0048] 2 parts of lubricated processing aid, PA101;

[0049] 10 parts filler, which is light calcium carbonate;

[0050] 0.02 part of pigment is positive red pigment.

[0051] After mixing the above components by weight, first add CPVC resin and PVC resin to the high mixer, then add stabilizer when the heat is mixed to 60°C, add anti-impact agent and processing aid when it reaches 70°C, Add fillers and pigments at the same time, put it in the cold mixing pot when it is hot mixed to 110°C, and discharge it when it ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses CPVC for a power cable sleeve and a preparation method thereof. The CPVC consists of the following raw materials in parts by weight: 50-70 parts of CPVC resin, 30-50 parts of PVC resin, 2.5-5 parts of a stabilizer, 2-3 parts of a lubricating anti-impact modifying agent, 2-4 parts of a lubricating processing aid, 10-30 parts of a filling material and 0.02-0.2 part of a pigment. The prepared compound material disclosed by the invention is simple in mixing process and easy to process; pipes prepared are 93-95 DEG C in Vicat temperature, and various physical indexes achieve standard of the power cable sleeve; moreover, the CPVC is low in cost, good in weather fastness and good in flame retardance.

Description

technical field [0001] The invention belongs to the field of polymer materials, and in particular relates to a CPVC for power cable casing and a preparation method thereof. Background technique [0002] At present, power cables in towns and industrial parks are mostly protected by hard polyvinyl chloride plastic sleeves. This material has good corrosion resistance, light weight, low cost, and simple installation. However, its long-term use temperature does not exceed 50°C, the strength and toughness are small, the weather resistance is poor, and it is easily broken, which will easily affect the overall project quality during the construction process. CPVC material has become an ideal material for power cable bushings because of its high strength, good heat resistance and good weather resistance. Foreign countries have been developing and researching CPVC materials for a long time, and have successfully applied CPVC pipes to the field of power cable casings. At present, CPV...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/28C08L33/00C08K3/26H01B3/44
Inventor 凌玉英王曙光孙喜君
Owner 山东高信化学股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com