Thermoplastic halogen-free flame-retardant polyphenyl ether elastomer cable material and preparation method thereof

The technology of polyphenylene ether elastomer and polyolefin elastomer is applied in the field of thermoplastic halogen-free flame retardant polyphenylene ether elastomer and its preparation field, which can solve the problems of high hardness and high production cost, achieve high toughness and improve comprehensive performance. , The effect of good low temperature resistance

Active Publication Date: 2014-07-09
JIANGSU LINRY NEW MSTAR TECH
View PDF10 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to provide a thermoplastic halogen-free flame-retardant polyphenylene ether elastomer cable material and a preparation method thereof, in view of the above shortcomings of the prior art, using styrene-based elastomers with high styrene content, high Fluid polyolefin elastomer and high-efficiency high-temperature-resistant, water-resistant, and humidity-resistant composite phosphorus-nitrogen flame retardants modify polyphenylene ether. The process of the present invention improves the original disadvanta

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermoplastic halogen-free flame-retardant polyphenyl ether elastomer cable material and preparation method thereof
  • Thermoplastic halogen-free flame-retardant polyphenyl ether elastomer cable material and preparation method thereof
  • Thermoplastic halogen-free flame-retardant polyphenyl ether elastomer cable material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] This embodiment provides a thermoplastic halogen-free flame-retardant polyphenylene ether elastomer cable material, which can be used for flexible wire and cable coating layers,

[0034] (1) The cable material is selected from the following components in parts by mass, as shown in Table 1 below:

[0035]

[0036] (2) The preparation method of the cable material:

[0037] Put all the components in the above table 1 into the high-speed mixer, firstly stir evenly in the high-speed mixer, and then extrude through the twin-screw extruder at a temperature range of 200°C, granulate with water strands, dry with moisture and then pack , Serve as a finished product of thermoplastic halogen-free flame-retardant polyphenylene ether elastomer cable material for flexible wire and cable coating.

[0038] In this embodiment, the kinematic viscosity of the plasticizer is between 50 cSt.

[0039] In this embodiment, the polyphenylene ether resin powder is in the form of light yellow...

Embodiment 2

[0045] This embodiment provides a thermoplastic halogen-free flame-retardant polyphenylene ether elastomer cable material, which can be used for flexible wire and cable coating layers,

[0046] (1) The cable material selects the following components in parts by mass, as shown in Table 2 below:

[0047]

[0048] (2) The preparation method of the cable material:

[0049] Put all the components in the above table 2 into the high-speed mixer, firstly stir evenly in the high-speed mixer, and then extrude through the twin-screw extruder at a temperature range of 180°C, granulate with water strands, dry with moisture and then pack , Serve as a finished product of thermoplastic halogen-free flame-retardant polyphenylene ether elastomer cable material for flexible wire and cable coating.

[0050] In this embodiment, the kinematic viscosity of the plasticizer is between 20 cSt.

[0051] In this embodiment, the polyphenylene ether resin powder is light yellow fluid powder, and the p...

Embodiment 3

[0057] This embodiment provides a thermoplastic halogen-free flame-retardant polyphenylene ether elastomer cable material, which can be used for flexible wire and cable coating layers,

[0058] (1) The cable material is selected from the following components in parts by mass, as shown in Table 3 below:

[0059]

[0060]

[0061] (2) The preparation method of the cable material:

[0062] Put all the components in the above table 3 into the high-speed mixer, firstly stir evenly in the high-speed mixer, and then extrude through the twin-screw extruder at a temperature range of 210°C, granulate with water strands, dry with moisture and then pack , Serve as a finished product of thermoplastic halogen-free flame-retardant polyphenylene ether elastomer cable material for flexible wire and cable coating.

[0063] In this embodiment, the kinematic viscosity of the plasticizer is between 65 cSt.

[0064] In this embodiment, the polyphenylene ether resin powder is light yellow fl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Kinematic viscosityaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Melt indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a thermoplastic halogen-free flame-retardant polyphenyl ether elastomer cable material and a preparation method thereof. The cable material is used for a soft type electric wire and cable coating, and comprises the following components: polyphenyl ether resin powder, styrene-series elastomers, a plasticizer, a polyolefin elastomer, a compound phosphor-nitrogen flame retardant, an antioxidant and a lubricant. The material components are uniformly stirred in a high-speed mixer, extruded by a twin-screw extruder, pelletized in water, dried and then packaged to obtain a thermoplastic halogen-free flame-retardant polyphenyl ether elastomer cable material finished product. The thermoplastic halogen-free flame-retardant polyphenyl ether elastomer cable material designed by the invention has excellent performance such as good processing performance, halogen-free and flame-retardant performance, low density, high tensile strength, good scraping resistance, good softness, good low temperature resistance, capacity of being extruded at a processing temperature of 200 DEG C-280 DEG C and not decomposed, free of cracks on a sample sheet for seven days under a high-temperature high-humidity environment with 98% humidity and a temperature of 85 DEG C, free of precipitates on surface, and the like.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and relates to a cable material and a preparation method thereof, in particular to a thermoplastic halogen-free flame-retardant polyphenylene ether elastomer cable material used for coating layers of soft electric wires and cables and a preparation method thereof . Background technique [0002] As one of the important inventions of human industrial civilization, wires and cables have been widely used in the transmission of various types of electric energy and signals. Compared with other materials, polymers are the preferred materials for coating layers of various wires and cables due to their light specific gravity, easy molding, good comprehensive mechanical properties and excellent performance of cable insulation. [0003] Polyphenylene ether (PPE or PPO for short) is a high-performance thermoplastic engineering plastic with good mechanical properties, chemical stability, dielectric...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L71/12C08L53/02C08L23/08C08L23/06C08K13/02C08K5/3492C08K5/5313C08K5/524C08K5/1535C08K3/22C08K3/34C08K3/04B29C47/92B29C48/92
CPCB29B7/46B29B7/72B29B7/7461B29B9/065B29B9/12B29B2009/125B29C48/40B29C48/625B29C48/92B29C2948/922B29C2948/92485B29C2948/9259B29C2948/92704C08L71/12C09K21/14C08L23/00C08L25/00
Inventor 郭振勤谢俊
Owner JIANGSU LINRY NEW MSTAR TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap