Conductive aluminum alloy section bar formula of subway locomotive and preparation method thereof

A technology of aluminum alloy profile and preparation process, which is applied in the field of metal materials and can solve the problems of reducing material plasticity and electrical conductivity, etc.

Inactive Publication Date: 2014-07-09
GUANGDONG XINGFA ALUMINUM +2
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main reason is that the heat treatment strengthening phase is an impurity phase formed by magnesium silicide, excess silicon and impurity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The formula of the conductive aluminum alloy profile of the subway locomotive used in this embodiment is prepared by the following element components by weight percentage, 0.45% of Si, 0.5% of Mg, 0.2% of Fe, 0.02% of Mn, 0.02% of Cr, 0.04% of Cu, 0.03% of Zn, 0.03% of Ti, the content of other individual impurities is ≤0.03%, the total of other impurities is ≤0.1%, the balance is Al, and the total weight percentage of each component is 100%. Among them, Al is an industrial pure Al ingot with a content of not less than 99.85wt%, Mg is a pure Mg ingot with a content of not less than 99.95wt%, and a high-quality Al-Si master alloy is used as raw materials. Before melting and casting, clean the melting and casting furnace with industrial pure Al ingot with Al content not less than 99.85wt.%. All sticker tools that may be in contact with the melt should be painted to prevent the iron material from falling off and falling into the melt to affect the quality and prevent melt c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of metal materials and particularly relates to a conductive aluminum alloy section bar formula and a preparation method thereof. The aluminum section bar formula is prepared from the following element components in percentage by weight: 0.45%-0.5% of Si, 0.5%-0.65% of Mg, 0.1%-0.25% of Fe, not greater than 0.03% of Mn, not greater than 0.03% of Cr, not greater than 0.05% of Cu, not greater than 0.05% of Zn, not greater than 0.05% of Ti, not greater than 0.03% of other single impurity, not greater than 0.1% of other impurities, and the balance of Al, based on 100% in total. The preparation method of the conductive aluminum alloy section bar formula comprises steps of casting, homogenizing, cast ingot heating, extruding and thermal processing, wherein the thermal processing step adopts double-stage manual ageing thermal treatment, and the ageing condition is T6 + (210+/-5 DEG C, 2h). The aluminum alloy magnesium silicide manufactured by the conductive aluminum alloy section bar formula disclosed by the invention is uniform in strengthening phase diffusion, and has good strength and inter-crystalline corrosion resistance.

Description

【Technical field】 [0001] The invention belongs to the field of metal materials, and in particular relates to a formula of a conductive aluminum alloy profile for a subway locomotive and a preparation process thereof. 【Background technique】 [0002] At present, the bus bar of the overhead rigid suspension system of domestic urban rail transit is generally made of aluminum alloy profiles. The main function of the bus bar is to conduct current and clamp the contact wire. Therefore, there are certain requirements for the conductivity and mechanical properties of aluminum alloy. Achieving tensile strength ≥ 215MPa, yield strength ≥ 160MPa, elongation ≥ 8%, volume resistivity < 0.0329Ω.mm at 20°C 2 / m (equivalent to a volume conductivity IACS of 52.5%). As we all know, the higher the purity of the aluminum alloy, the better the electrical conductivity, but the lower the mechanical properties. Therefore, there is a contradiction between improving the electrical conductivity o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C21/08C22F1/05
Inventor 罗铭强聂德键陈树钦
Owner GUANGDONG XINGFA ALUMINUM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap