Preparation method of halloysite loading phosphoric acid Silverlight catalyst

A catalyst and halloysite technology, applied in the direction of physical/chemical process catalysts, chemical instruments and methods, chemical/physical processes, etc., can solve problems such as silver phosphate particle agglomeration, increase light transmittance, increase pore size, and avoid agglomeration and shedding effect

Active Publication Date: 2014-07-23
江阴智产汇知识产权运营有限公司
View PDF2 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing technology only loads nano-silver particles on the outer surface of halloysite, while the inner surface area is huge and has a good adsorption effect. If the inner layer is fully utilized, it can effectively solve the agglomeration of silver phosphate particles The problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Add halloysite with a purity of not less than 80wt% into a 5wt% nitric acid solution, the solid-to-liquid ratio of the reaction system is 10% by mass, stir at room temperature for 8 hours, centrifuge and dry, to obtain acid-treated halloysite; Dissolve 2 g of silver nitrate in 100 mL of ethanol to prepare a silver nitrate ethanol solution; place 8 g of acid-treated halloysite in a vacuum filter flask, put a magnetic stirring rotor in the vacuum filter flask, and the side of the vacuum filter flask is thin The neck is connected to the vacuum pump, and the mouth of the vacuum filter bottle is connected to the separatory funnel through a rubber stopper. The rubber stopper acts as a seal to make the separatory funnel and the vacuum filter bottle tightly connected. The stopper of the separatory funnel is closed; the silver nitrate ethanol The solution is put into the separatory funnel, the vacuum filter bottle connected to the separatory funnel is placed on the magnetic stirre...

Embodiment 2

[0017] Add halloysite with a purity of not less than 80wt% into a 1wt% nitric acid solution, the solid-liquid ratio of the reaction system is 5% by mass, stir at room temperature for 4h, centrifuge for dehydration and dry to obtain acid-treated halloysite; Dissolve 2g of silver nitrate in 80mL of ethanol to prepare a silver nitrate ethanol solution; place 4g of acid-treated halloysite in a vacuum filter flask, put a magnetic stirring rotor in the vacuum filter flask, and the side of the vacuum filter flask is thin The neck is connected to the vacuum pump, and the mouth of the vacuum filter bottle is connected to the separatory funnel through a rubber stopper. The rubber stopper acts as a seal to make the separatory funnel and the vacuum filter bottle tightly connected. The stopper of the separatory funnel is closed; the silver nitrate ethanol The solution is put into the separatory funnel, the vacuum filter bottle connected to the separatory funnel is placed on the magnetic stir...

Embodiment 3

[0020] Add halloysite with a purity of not less than 80wt% to a 3wt% nitric acid solution, the solid-to-liquid ratio of the reaction system is 10% by mass, stir at room temperature for 8 hours, centrifuge and dry, and obtain acid-treated halloysite; Dissolve 2 g of silver nitrate in 100 mL of ethanol to prepare a silver nitrate ethanol solution; place 8 g of acid-treated halloysite in a vacuum filter flask, put a magnetic stirring rotor in the vacuum filter flask, and the side of the vacuum filter flask is thin The neck is connected to the vacuum pump, and the mouth of the vacuum filter bottle is connected to the separatory funnel through a rubber stopper. The rubber stopper acts as a seal to make the separatory funnel and the vacuum filter bottle tightly connected. The stopper of the separatory funnel is closed; the silver nitrate ethanol The solution is put into the separatory funnel, the vacuum filter bottle connected to the separatory funnel is placed on the magnetic stirrer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
decolorization rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a halloysite loading phosphoric acid Silverlight catalyst. The preparation method comprises the following specific steps of adding halloysite in a salpeter solution so as to obtain the halloysite after acid treatment, placing the 4-8g halloysite after acid treatment into a vacuum filtration bottle, mixing the halloysite and a silver nitrate ethanol solution under a vacuum state, enabling the silver nitrate to fully enter a halloysite pipe, sequentially stirring 2-5h, carrying out solid-liquid separation, and vacuum drying at 70-80 DEG C; adding the obtained product after drying in a 50 mL of sodium dihydrogen phosphate solution the concentration of which is 0.5-1.5mol / L, stirring for 4-5h, carrying out solid-liquid separation, washing, drying at 100-105 DEG C so as to obtain the halloysite loading phosphoric acid Silverlight catalyst. The preparation method provided by the invention has the advantages that the air and moisture in a halloysite pipeline are discharged, the silver nitrate enters a pipeline, an aluminum oxide of the inner wall of the halloysite is removed, the effects of increasing light penetrating degree and aperture property action can be achieved, the obtained silver phosphate particles are arranged in a halloysite pipe and are prevented from birdnesting and falling.

Description

Technical field [0001] The invention relates to the field of new materials for environmental pollution control, in particular to the preparation of a halloysite-supported silver phosphate photocatalyst. Background technique [0002] With the development of science and technology, toxic organic pollutants from industrial and agricultural production seriously threaten the environment and human health. It is of great significance to seek a new and efficient environmental treatment technology. Because of its advantages of energy saving, high efficiency, thorough degradation of pollutants, and no secondary pollution, photocatalytic technology has become an emerging environmental treatment technology with important application prospects. In recent years, the development of new and efficient visible light photocatalysts has become an important research content in photocatalysis technology. Among them, photocatalytic materials with surface plasmon resonance effect have become a major sou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J27/18
Inventor 马建锋邹静李良银姚超
Owner 江阴智产汇知识产权运营有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com