Bone matte glaze and method for manufacturing bone china product by using same

A matte glaze and bone china technology, which is applied in the field of bone matt glaze and the production of bone china products with the glaze, can solve the problems of poor acid and alkali corrosion resistance, complicated decoration process, poor stain resistance and the like , to achieve the effect of good acid and alkali resistance, good hardness and good stain resistance

Active Publication Date: 2014-08-27
GUANGDONG SONGFA CERAMICS
View PDF6 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Bone china is good in decoration, which is an inherent characteristic that other porcelains cannot match. At present, high-grade bone china colored porcelain is made by the decoration method of pasting in-glaze colored flower paper on white bone china products. Melted into the glaze layer during the firing process; Chinese red and imperial yellow low-temperature colored glaze decorations have been widely used in bone china, and the decoration process is complex and diverse
Due to technical reasons, low-temperature matte glaze has low glaze hardness, poor stain resistance, poor acid and alkali corrosion resistance, etc., and matte glaze has not been used in the decoration of bone china products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] This embodiment discloses a bone matte glaze and a method for making bone china products with the glaze.

[0017] Take the following components and parts by weight: 16 parts of quartz, 28 parts of potassium feldspar, 16 parts of borax, 6 parts of boric acid, 1 part of strontium carbonate, 5 parts of lithium carbonate, 2 parts of zinc oxide, 3 parts of talc, 10 parts of calcite part, 0.5 part of zirconium silicate, stir the above raw materials evenly, melt at a temperature of 1310°C, and make frit for later use;

[0018] Take 100 parts of the above-mentioned frit, 5 parts of clay, 10 parts of wollastonite, 6 parts of aluminum oxide, 10 parts of zinc oxide, and 6 parts of tin oxide, put the above raw materials into the mill, and add 30% by mass based on the total mass water, ground for 50 hours, fineness 325 mesh sieve residue 0.09%, crossed 200 mesh sieve, for subsequent use;

[0019] Spray and dry the glaze obtained above on bisque, the thickness of the glaze layer is ...

Embodiment 2

[0022] This embodiment discloses a bone matte glaze and a method for making bone china products with the glaze.

[0023] Take the following components and parts by weight: 20 parts of quartz, 32 parts of potassium feldspar, 13 parts of borax, 6 parts of boric acid, 4 parts of strontium carbonate, 7 parts of lithium carbonate, 10 parts of zinc oxide, 1 part of talc, 5 parts of calcite part, 0.2 part of zirconium silicate, stir the above raw materials evenly, melt at a temperature of 1330 ℃, and make a frit for later use;

[0024] Take 100 parts of the above-mentioned frit, 7 parts of clay, 6 parts of wollastonite, 5 parts of aluminum oxide, 8 parts of zinc oxide, and 6 parts of tin oxide, put the above raw materials into the mill, and add 32% by mass based on the total mass water, ground for 55 hours, fineness 325 mesh sieve residue 0.08%, crossed 220 mesh sieve, for subsequent use;

[0025] Spray and dry the glaze obtained above on the bisque, the thickness of the glaze layer...

Embodiment 3

[0028] This embodiment discloses a bone matte glaze and a method for making bone china products with the glaze.

[0029] Take the following components and parts by weight: 24 parts of quartz, 38 parts of potassium feldspar, 12 parts of borax, 3 parts of boric acid, 5 parts of strontium carbonate, 9 parts of zinc oxide, 1 part of talc, 12 parts of calcite, zirconium silicate 0.5 parts, the above raw materials are stirred evenly, melted at a temperature of 1300 ℃, and made into a frit for later use;

[0030] Take 100 parts of the above frit, 8 parts of clay, 9 parts of wollastonite, 6 parts of aluminum oxide, 6 parts of zinc oxide, and 6 parts of tin oxide, put the above raw materials into the mill, and add 30% by mass based on the total mass water, grind for 52 hours, fineness 325 mesh sieve residue 0.05%, pass 250 mesh sieve, standby;

[0031] Spray and dry the glaze obtained above on the bisque, the thickness of the glaze layer is 6 g / 100 cm 2 , into the kiln for oxidation ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to bone matte glaze. The bone matte glaze comprises, by weight, 100 parts of frits, 3-8 parts of clay, 2-12 parts of aedelforsite, 3-6 parts of aluminum oxide, 6-15 parts of zinc oxide and 6 parts of stannic oxide. The frits comprise, by weight, 16-24 parts of quartz, 28-38 parts of potash feldspar, 12-18 parts of borax, 0-7 parts of boric acid, 0-5 parts of strontium carbonate, 0-8 parts of lithium carbonate, 0-10 parts of zinc oxide, 0-3 parts of talcum, 0-12 parts of calcite and 0-0.5 part of zirconium silicate. The glaze surface of a product using the glaze is fine, smooth, resistant to pollution, resistant to acid and alkali, easy to wash and suitable for the decoration means such as decal. The invention further provides a method for manufacturing the bone china product by using the bone matte glaze. The method is simple in firing process, stable in production and good in benefit.

Description

technical field [0001] The invention relates to a bone matt glaze and a method for making bone china products with the glaze. Background technique [0002] Bone china is called bone china for short, and its scientific name is bone china. It is a kind of porcelain made of animal bone carbon, clay, feldspar and quartz as the main raw materials, which are fired twice after high-temperature plain firing and low-temperature glaze firing. The national standard for bone china contains more than 30% tricalcium phosphate from animal bones, and the finished product has light transmission, so it can become bone china, while the American standard must reach at least 25%. [0003] Bone china has beautiful appearance, delicate and transparent porcelain, high regularity, elegant and beautiful shape, moist and bright glaze, strong decoration, colorful flower surface, high mechanical strength, good impact resistance, and can be made into thin tire products. Bone China was originally produ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86
Inventor 林道藩
Owner GUANGDONG SONGFA CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More