Anti-hydrolysis anti-static PC/ASA alloy and preparation method thereof

An alloy and antioxidant technology, which is applied in the field of polymer materials, can solve the problems of inability to use the exterior decoration environment for a long time, unfavorable promotion and application, and inability to resist the erosion of dust in the exterior decoration environment.

Active Publication Date: 2014-08-27
SHANGHAI ZHONGLEI NEW MATERIAL SCI CO LTD
View PDF10 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the disadvantages and shortcomings of this technology are: these materials cannot be exposed to high temperature and high humidity environments and used as exterior decorations, and they have no antistatic properties and cannot resist the erosion of dust in the exterior decoration environment.
However, the defects and shortcomings of this technology are: when this material is used as an exterior decoration, it has no antistatic property, cannot resist the erosion of dust in the exterior decoration environment, and cannot be used in the exterior decoration environment for a long time, which is not conducive to the large-scale promotion and application of this kind of material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-hydrolysis anti-static PC/ASA alloy and preparation method thereof
  • Anti-hydrolysis anti-static PC/ASA alloy and preparation method thereof
  • Anti-hydrolysis anti-static PC/ASA alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] This embodiment includes the following steps:

[0030] 1) The polycarbonate used in the following examples is bisphenol A polycarbonate PC lexan141R of GE Company, with a molecular weight of 25000-28000 g / mol. The acrylonitrile-styrene-acrylate graft copolymer is Taiwan Chimei PW957, and the content of acrylate rubber is 40-80% by weight. Antioxidant uses tetrakis [β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester, trade name is Irganox1010, produced by Swiss Ciba Specialty Chemicals. The present invention uses the ZE-25 twin-screw extruder that German Berstorff company produces.

[0031] This embodiment includes the following steps:

[0032] 1) Preparation of grafted ASA-g-MAH:

[0033]First, 80 parts of ASA, 20 parts of MAH, 1.5 parts of dicumyl peroxide (DCP), and 0.1 part of hindered phenolic antioxidant 1010 were uniformly mixed with a high-speed mixer for 5 minutes and then added to a twin-screw extruder for melting For blending, the temp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
epoxy valueaaaaaaaaaa
degree of graftingaaaaaaaaaa
Login to View More

Abstract

The invention provides anti-hydrolysis anti-static PC / ASA alloy and a preparation method thereof. According to the method, condensation polymerization is conducted on PPR-MWCNT compounds and ASA-g-MAH grafted copolymer through bisphenol A and epoxy chloropropane, bisphenol A epoxy resin (EP-E51) and polycarbonate (PC) are obtained and are subjected to blending extrusion, and the anti-hydrolysis anti-static PC / ASA alloy is obtained. The prepared anti-hydrolysis anti-static PC / ASA alloy has excellent anti-static performance and excellent hydrolysis resistance, is suitable for the moist rainwater weather, has excellent impact toughness and lower processing viscosity, is easy to process and suitable for mass production and popularization, and can be oriented to automobile inside and outside ornaments such as an automobile rearview mirror shell body and an automobile door plank and outdoor sport equipment.

Description

technical field [0001] The present invention relates to a method in the technical field of polymer materials, in particular to a hydrolysis-resistant and antistatic polycarbonate (PC) / acrylonitrile-styrene-acrylate graft copolymer (ASA) alloy and a preparation method thereof . Background technique [0002] The polyacrylate rubber in the rubber core layer of the ASA graft copolymer is a saturated structure without residual double bonds, and dissociates under high-energy light with a wavelength below 300nm. This high-energy light does not exist in the sun’s rays on the earth, that is, ASA The molecular structure of the resin is not easily decomposed by high-energy light, so PC / ASA has high weather resistance. PC / ASA alloy can combine the excellent properties of PC and ASA, improve the heat resistance, impact resistance and tensile strength of ASA, reduce the viscosity of PC melt, improve processing performance, reduce the internal stress of products, and significantly improve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L51/04C08L23/14C08L63/02C08K7/00C08K3/04C08G59/06C08F265/08
Inventor 刘春艳王正有
Owner SHANGHAI ZHONGLEI NEW MATERIAL SCI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com