Preparation method of tubular polyurethane/keratin composite nanofiber material

A technology of composite nanofibers and keratin, which is applied in the field of preparation of polyurethane-keratin composite nanofiber tubular materials, can solve the problem of no biological activity, unfavorable adhesion and growth of endothelial cells and other tissue cells, lack of cell recognition signal sites, etc. problems, to achieve the effect of adjustable inner diameter, simple preparation method, and lower mechanical properties.

Inactive Publication Date: 2014-09-03
DONGHUA UNIV
View PDF7 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the polyurethane material itself has no biological activity and lacks cell recognition signal sites, which is not conducive to the adhesion and growth of tissue cells such as endothelial cells

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The keratin was extracted from wool by reduction method. The specific method was: weigh 5g of wool, use petroleum ether as solvent to remove the oil on the surface of wool by Soxhlet extraction, then wash the wool with ethanol and air-dry it. Add the above-mentioned wool into 100ml, 1mol / l mercaptoethanol, adjust the pH to about 10.0 with NaOH, and then react at 40°C for 12h. After the reaction was finished, the reaction solution was collected (referred to as filtrate 1), and the wool solid remaining in the reaction was collected by filtration, and continued to be treated with 100ml, 0.1mol / l Tris lye at 40°C for 2h, and then filtered to remove the solid. The filtrate was collected (designated as filtrate 2). .The filtrates 1 and 2 were combined, centrifuged at 6000rpm for 5 minutes, and then dialyzed with a dialysis bag with a molecular weight cut-off of 40,000 for 36 hours. Finally, the dialysate was added to liquid nitrogen for quick freezing, and then dried in a fre...

Embodiment 2

[0029] Using human hair as raw material to extract keratin by reduction method, the specific method is: weigh 5g of human hair, use petroleum ether as solvent to remove human hair surface oil by Soxhlet extraction, then wash human hair with ethanol and air-dry. Add the above-mentioned human hair into a mixed solution of 200ml of water and 5g of sodium metabisulfite, adjust the pH to about 10.0 with NaOH, and then react at 60°C for 5h. After the reaction, collect the reaction solution (referred to as filtrate 1), and collect the remaining human hair solid by filtration at the same time, continue to treat it with 100ml, 0.1mol / l Tris lye at 40°C for 2h, and then filter to remove the solid , collect the filtrate (referred to as filtrate 2). .The filtrates 1 and 2 were combined, centrifuged at 6000rpm for 5 minutes, and then dialyzed with a dialysis bag with a molecular weight cut-off of 8,000 for 36 hours. Finally, the dialysate was added to liquid nitrogen for quick freezing, an...

Embodiment 3

[0032] The keratin is extracted from wool by oxidation method. The specific method is: weigh 5g of wool, use petroleum ether as solvent to remove the oil on the surface of wool by Soxhlet extraction, then wash the wool with ethanol and air-dry it. 100ml of deionized water and 5ml of 30% hydrogen peroxide were added to the wool, and then reacted at 100°C for 2h. After the reaction was finished, the reaction solution was collected (referred to as filtrate 1), and the wool solid remaining in the reaction was collected by filtration, and continued to be treated with 100ml, 0.1mol / l Tris lye at 40°C for 2h, and then filtered to remove the solid. The filtrate was collected (designated as filtrate 2). .The filtrates 1 and 2 were combined, centrifuged at 6000rpm for 5 minutes, and then dialyzed with a dialysis bag with a molecular weight cut-off of 8,000 for 36 hours. Finally, the dialysate was added to liquid nitrogen for quick freezing, and then dried in a freeze dryer to obtain dry...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
molecular weightaaaaaaaaaa
concentrationaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a tubular polyurethane/keratin composite nanofiber material. The preparation method comprises the steps of dissolving polyurethane in solvent and stirring until dissolving completely to obtain a polyurethane solution; dissolving keratin into a solvent and stirring until dissolving completely to obtain a keratin solution; mixing the polyurethane solution and the keratin solution with mass ratio of 95:5-5:95, stirring uniformly to obtain a polyurethane/keratin spinning solution, performing electrostatic spinning and using a cylindrical collecting roller as a receiver. The method can compound natural biomacromolecular keratin and polyurethane into the tubular nanofiber material through electrostatic spinning, so that the material has high porosity and good mechanical and biological functions.

Description

technical field [0001] The invention belongs to the field of preparation of nanofiber tubular materials, in particular to a preparation method of polyurethane-keratin composite nanofiber tubular materials. Background technique [0002] Keratin is an insoluble fibrous animal protein, a structural protein of ectodermal cells, widely present in animal skin and skin appendages, such as hair, hooves, shells, claws, horns, scales, etc. A large number of studies in recent years have shown that keratin is a high-quality biomedical material with good biocompatibility and not rejected by the body's immune system, and has broad application prospects. Most prominently, the amino acid sequence of keratin derived from wool and other sources was found to contain the same Arg-Gly-Asp (RGD) tripeptide sequence. This tripeptide sequence is recognized as an effective binding site for cell binding in the extracellular matrix, and has the function of promoting cell adsorption. Therefore, a lar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F8/16D01F8/02D01D5/00
Inventor 杨光王夏辉曹张军
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap