Regular porous metal material as well as preparation method and application thereof
A porous metal and metal technology, applied in the field of porous materials, can solve the problems of uneven size and distribution, difficult to control the pore size and distribution of porous metal materials, complicated processes, etc., to achieve uniform pore size and distribution, and excellent impact energy absorption capacity. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0053] Correspondingly, for the structure of the regular porous metal material 2 above, the embodiment of the present invention also provides the following preparation method, the method for preparing the regular porous metal material 2 includes the following steps, and please refer to the attached Figure 1-11 :
[0054] S01. Prepare the metal unit cell 1, and the metal unit cell 1 is a hollow polyhedron;
[0055] S02. The metal unit cells 1 are stacked and connected in an array along the three-dimensional space direction.
[0056] Specifically, the structure of the metal unit cell in the above step S01 is the same as that of the metal unit cell 1 of the regular porous metal material 2 above, such as hollow trihedron, tetrahedron, tetrahedron, tetrahedron, etc., specifically as figure 2 , Image 6 The metal unit cell body 1 shown is not described here in order to save space.
[0057] Wherein, as a preferred embodiment, the method for preparing the metal unit cell is a sta...
Embodiment 1
[0065] A regular porous metal material containing cube metal unit cells and a preparation method thereof. The method comprises the steps of:
[0066] S11. Prepare cubic metal unit cells 11, the preparation method of which is as follows Figure 10 Shown:
[0067] S111. Select the sheet material coated with brazing material on the surface, and cut the sheet material into such figure 1 the shape shown;
[0068] S112. The metal sheet is folded into a cube using a progressive die to obtain the following figure 2 The volume shown is 5mm×5mm×5mm, and the metal unit cell body 11 with a thickness of 0.2mm;
[0069] S12. Arraying and stacking the cube metal unit cells 11 prepared in step S11 along the three-dimensional space direction to form a regular porous metal material precursor;
[0070] S13. Put the regular porous metal material precursor prepared in step S12 in a brazing furnace for welding to form a regular porous metal material with a structure as shown in FIG. 3 .
Embodiment 2
[0072] A regular porous metal material containing cube metal unit cells and a preparation method thereof. The method comprises the steps of:
[0073] S21. Prepared as figure 2 Shown cubic metal unit cell body 11, its preparation method is the same as the preparation method of cubic metal unit cell body 11 in embodiment 1; Ordinary sheet metal for welding materials;
[0074] S22. Coating the surface of the cubic metal unit cells 11 prepared in step S21 with an adhesive, and stacking them in an array along the three-dimensional direction, so that two adjacent cubic metal unit cells 11 are bonded to each other, thereby forming a regular porous metal material.