Water element stone ceramic ball and preparing method thereof

A technology of hydrostone and ceramic balls, applied in the field of hydrostone ceramic balls and its preparation, to enhance human body functions, eliminate odors, and improve microcirculation

Active Publication Date: 2014-10-01
徐州雅居乐环保科技有限公司
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is no report about the hydrostone ceramic ball in the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A hydrostone ceramic ball, made of the following raw materials in weight (kg): 80 hydrostone, 45 green shoushi, 20 garnet, 10 carbon fiber, 24 rectorite, 18 diatomite, and illite 14-22, ocher 12, goose pipe stone 10, nano-silver carbon molecular sieve 7, cyanite 15, natural manganese sand 25, titanium dioxide 5.

[0018] The preparation method of hydrostone ceramic ball comprises the following steps:

[0019] (1) Mix green shoushi, garnet, diatomaceous earth and illite evenly, calcinate at 720°C for 3 hours, take it out and put it in 2°C, cool to below 50°C, crush it after cooling, pass through a 100-mesh sieve, dry, and set aside ;

[0020] (2) Mix hydronite, rectorite, and natural manganese sand evenly, crush them, pass through a 300-mesh sieve, add hydrogen peroxide and beat to make a slurry with a concentration of 45, grind at a high speed until the particle size of the slurry reaches 15 μm, and spray dry it into powder ,stand-by;

[0021] (3)...

Embodiment 2

[0024] A hydrostone ceramic ball, made of the following raw materials (kg): 90 hydrostone, 55 green shoushi, 30 garnet, 12 carbon fiber, 32 rectorite, 22 diatomite, illite 18. Ocher 16, goose pipe stone 12, nano-silver carbon molecular sieve 11, cyanite 18, natural manganese sand 35, titanium dioxide 8.

[0025] The preparation method of hydrostone ceramic ball comprises the following steps:

[0026] (1) Mix green shoushi, garnet, diatomaceous earth and illite evenly, calcinate at 740°C for 2.5 hours, take it out and put it in 3°C, cool to below 50°C, crush it after cooling, pass through a 150-mesh sieve, and dry it. use;

[0027] (2) Mix hydronite, rectorite, and natural manganese sand evenly, crush them, pass through a 350-mesh sieve, add hydrogen peroxide and beat to make a slurry with a concentration of 50%, grind at a high speed until the particle size of the slurry reaches 20 μm, and spray dry it into powder, ready to use;

[0028] (3) Mix ochre, g...

Embodiment 3

[0031] A hydrostone ceramic ball, made of the following raw materials (kg): 100 hydrostone, 65 green shoushi, 40 garnet, 15 carbon fiber, 36 rectorite, 26 diatomite, illite 22. Ocher 18, goose pipe stone 15, nano-silver carbon molecular sieve 14, cyanite 20, natural manganese sand 45, titanium dioxide 10.

[0032] The preparation method of hydrostone ceramic ball comprises the following steps:

[0033] (1) Mix green shoushi, garnet, diatomaceous earth, and illite evenly, calcinate at 760°C for 2 hours, take it out and put it in 5°C, cool it below 50°C, crush it after cooling, pass through a 150-mesh sieve, dry, and set aside ;

[0034] (2) Mix hydronite, rectorite, and natural manganese sand evenly, crush them, pass through a 400-mesh sieve, add hydrogen peroxide and beat to make a slurry with a concentration of 55%, grind at a high speed until the particle size of the slurry reaches 25 μm, and spray dry it into powder, ready to use;

[0035] (3) Mix och...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water element stone ceramic ball and preparing method thereof. The water element stone ceramic ball is prepared from the following raw materials in parts by weight: 80-100 parts of water element stones, 45-65 parts of green stones, 20-40 parts of garnet, 10-15 parts of carbon stone fiber, 24-36 parts of rectorite, 18-26 parts of diatomite, 14-22 parts of illite, 12-18 parts of ocher, 10-15 parts of Balanophyllia sp, 7-14 parts of nano silver carbon molecular sieves, 15-20 parts of green frontiers stones, 25-45 parts of natural manganese sands and 5-10 parts of titanium dioxide. After being processed by the water element stone ceramic ball, drinking water is weakly alkaline in water quality with small molecules and negative potential, rich in oxygen, minerals and trace elements needed by the body, and beneficial to human health; the water element stone ceramic ball has the functions of killing bacteria and viruses in the drinking water, eliminating odors and adsorbing harmful substances of chlorine dioxide, heavy metals and the like, so as to ensure the good quality of the drinking water.

Description

technical field [0001] The invention relates to a hydrostone ceramic ball and a preparation method thereof, belonging to the field of ceramic materials. Background technique [0002] Water element stone, the geological category belongs to iron dolomite, also known as wood grain stone, is a precious natural ore rich in various rare elements, formed in the middle Cambrian geological age about 570 million years ago, in the shallow sea A precious mineral resource formed by chemical deposition. The unique natural circulating magnetic field of water element stone can change the structure of water molecules, which can instantly improve the water quality of ordinary drinking water and turn ordinary drinking water into active water that is beneficial to human health. Therefore, it is of great significance to develop a kind of hydrostone ceramic ball for water treatment. Yet do not see the report about the hydrostone ceramic ball in the market at present. Contents of the invention...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/00C04B35/622
Inventor 任新年
Owner 徐州雅居乐环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com