Anti-drop heat-insulating ceramic spoon and preparation process thereof

A soup ladle and ceramic technology, which is applied in the field of drop-resistant and heat-insulated ceramic soup ladle and its preparation technology, can solve the problems of inconvenience, hot hands, and breakage of the soup ladle, and achieve the effect of high economic value, beautiful color, and not easy to break

Active Publication Date: 2014-11-19
米兰度骨瓷(上海)有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] There are many kinds of spoons, such as plastic, metal, wood, pottery, glass, etc., and the structural design is also varied; but the existing ceramic spoons are easy to burn when they are in use, and they will be broken if they are not careful. inconvenient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A drop-resistant and heat-insulating ceramic spoon is composed of the following components by weight: 35 parts of aluminum silicate fiber, 50 parts of silicon dioxide, 15 parts of kaolin, 5 parts of carbon fiber, 3 parts of calcium oxide, 12 parts of purple sand, crushed 10 parts of glass, 3 parts of boron fiber, 2 parts of pearl fiber, 0.2 parts of cobalt oxide, 0.6 parts of iron oxide, 3 parts of graphene microflakes, 2 parts of sulfate, 0.2 parts of tin oxide, 0.5 parts of zinc oxide, 1 part of stainless steel fiber , 0.2 parts of silver fiber.

[0021] A preparation process for a drop-resistant and heat-insulating ceramic spoon, comprising the following process steps,

[0022] 1) Disperse silica, kaolin, cullet and purple sand with absolute ethanol as the dispersion medium, and ultrasonically disperse them on an ultrasonic cleaning machine for 1 hour, wherein the mass ratio of materials to ethanol is 1:30;

[0023] 2) Put the ultrasonically dispersed mixture into a...

Embodiment 2

[0028] A drop-resistant and heat-insulating ceramic spoon is composed of the following components by weight: 40 parts of aluminum silicate fiber, 70 parts of silicon dioxide, 20 parts of kaolin, 8 parts of carbon fiber, 5 parts of calcium oxide, 15 parts of purple sand, crushed 15 parts of glass, 4 parts of boron fiber, 3 parts of pearl fiber, 0.5 parts of cobalt oxide, 1 part of iron oxide, 5 parts of graphene microflakes, 3 parts of sulfate, 0.8 parts of tin oxide, 0.8 parts of zinc oxide, 2 parts of stainless steel fiber , 0.5 part of silver fiber.

[0029] A preparation process for a drop-resistant and heat-insulating ceramic spoon, comprising the following process steps,

[0030] 1) Disperse silica, kaolin, cullet and purple sand with absolute ethanol as the dispersion medium, and ultrasonically disperse them on an ultrasonic cleaning machine for 1 hour, wherein the mass ratio of materials to ethanol is 1:30;

[0031] 2) Put the ultrasonically dispersed mixture into a ny...

Embodiment 3

[0036] A drop-resistant and heat-insulating ceramic spoon, which is composed of the following components in parts by weight: 30 parts of aluminum silicate fiber, 40 parts of silicon dioxide, 10 parts of kaolin, 3 parts of carbon fiber, 1 part of calcium oxide, 10 parts of purple sand, crushed 5 parts of glass, 2 parts of boron fiber, 1 part of pearl fiber, 0.1 part of cobalt oxide, 0.5 part of iron oxide, 2 parts of graphene microflakes, 1 part of sulfate, 0.1 part of tin oxide, 0.1 part of zinc oxide, 0.5 part of stainless steel fiber , 0.1 part of silver fiber.

[0037] A preparation process for a drop-resistant and heat-insulating ceramic spoon, comprising the following process steps,

[0038] 1) Disperse silica, kaolin, cullet and purple sand with absolute ethanol as the dispersion medium, and ultrasonically disperse them on an ultrasonic cleaning machine for 1 hour, wherein the mass ratio of materials to ethanol is 1:30;

[0039] 2) Put the ultrasonically dispersed mixtu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an anti-drop heat-insulating ceramic spoon, and relates to the technical field of tableware. The anti-drop heat-insulating ceramic spoon comprises the following components in parts by weight: 30-40 parts of aluminum silicate fibers, 40-70 parts of silicon dioxide, 10-20 parts of kaolin, 3-8 parts of carbon fibers, 1-5 parts of calcium oxide, 10-15 parts of red porcelain, 5-15 parts of cullet, 2-4 parts of boron fibers, 1-3 parts of pearl fibers, 0.1-0.5 part of cobalt oxide, 0.5-1 part of iron oxide, 2-5 parts of graphene mini-sheets, 1-3 parts of sulfate, 0.1-0.8 part of tin oxide, 0.1-0.8 part of zinc oxide, 0.5-2 parts of stainless steel fibers and 0.1-0.5 part of silver fibers. The anti-drop heat-insulating ceramic spoon disclosed by the invention is smooth in surface, good in strength and low in possibility of breaking due to dropping and can not scald the hand when being used through special preparation on raw materials. Compared with the traditional process, the anti-drop heat-insulating ceramic spoon disclosed by the invention has the advantages of short required time, low energy consumption, good product texture and no toxic substance residue.

Description

technical field [0001] The invention relates to the technical field of tableware, in particular to a drop-resistant and heat-insulating ceramic spoon and a preparation process thereof. Background technique [0002] Spoon is a tableware and kitchen utensil with a long history, which is indispensable in people's daily life and is mainly used to scoop soup or relatively finely divided food. Usually, spoons can be divided into soup spoons and colanders according to their functions and structures: soup spoons have a smooth concave arc surface and are mainly used for scooping soup. [0003] There are many kinds of spoons, such as plastics, metal, wood, pottery, glass, etc., and the structural design is also varied; but the existing ceramic spoons are easy to burn when they are used, and they will be broken if they are not careful. inconvenient. Contents of the invention [0004] The technical problem to be solved by the present invention is to provide a drop-resistant and heat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/80C04B35/76C04B35/14C04B35/622
Inventor 彭友才
Owner 米兰度骨瓷(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap