Coating for metal film resistors
A technology for metal film resistors and coatings, applied in polyamide coatings, epoxy resin coatings, coatings, etc., can solve the problems that coatings cannot meet the needs of field use, and achieve the effect of good adhesion and good film formation.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0009] The coating for metal film resistors provided by the invention is composed of the following raw materials in parts by weight: 40-60 parts of high temperature resistant epoxy resin, 20 parts of polyamide resin, 10 parts of ethylene oxide, 1 part of adhesion promoter, and 2 parts of binder, 5 parts of nano silicon dioxide, 0.1 part of polyurethane.
[0010] According to the above-mentioned parts by weight, at room temperature, the ethylene oxide suspension liquid dispersed with nano-silica is added to the polyamide resin and mixed evenly, and then mixed with high-temperature resistant epoxy resin, adhesion promoter, binder and The polyurethane is mixed evenly, and the specific gravity of the paint is suitable for the coating of the metal film resistor under the stirring condition. In the high temperature resistance test of the resistor coating obtained in this example, the resistance change rate is ≤0.4, the surface drying time is 2 hours, and the viscosity value is 30 MP...
Embodiment 2
[0013] The coating for metal film resistors provided by the invention is composed of the following raw materials in parts by weight: 40-60 parts of high temperature resistant epoxy resin, 25 parts of polyamide resin, 15 parts of ethylene oxide, 3 parts of adhesion promoter, adhesive 4 parts of binder, 8 parts of nano silicon dioxide, 0.3 part of polyurethane.
[0014] According to the above-mentioned parts by weight, at room temperature, the ethylene oxide suspension liquid dispersed with nano-silica is added to the polyamide resin and mixed evenly, and then mixed with high-temperature resistant epoxy resin, adhesion promoter, binder and The polyurethane is mixed evenly, and the specific gravity of the paint is suitable for the coating of the metal film resistor under the stirring condition. In the high temperature resistance test of the resistor coating obtained in this example, the resistance change rate is ≤0.4, the surface drying time is 1 hour, and the viscosity value is ...
Embodiment 3
[0016] The coating for metal film resistors provided by the invention is composed of the following raw materials in parts by weight: 40-60 parts of high temperature resistant epoxy resin, 25 parts of polyamide resin, 15 parts of ethylene oxide, 3 parts of adhesion promoter, adhesive 4 parts of binder, 8 parts of nano silicon dioxide, 0.3 part of polyurethane.
[0017] According to the above-mentioned parts by weight, at room temperature, the ethylene oxide suspension liquid dispersed with nano-silica is added to the polyamide resin and mixed evenly, and then mixed with high-temperature resistant epoxy resin, adhesion promoter, binder and The polyurethane is mixed evenly, and the specific gravity of the paint is suitable for the coating of the metal film resistor under the stirring condition. In the high temperature resistance test of the resistor coating obtained in this example, the resistance change rate was ≤0.4, the surface drying time was 1.2 hours, and the viscosity valu...
PUM
Property | Measurement | Unit |
---|---|---|
viscosity | aaaaa | aaaaa |
viscosity | aaaaa | aaaaa |
viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com