Optical plastic protection coating and preparation method thereof

A technology of optical plastics and protective coatings, applied in the direction of coatings, etc., can solve the problems of poor wear resistance and low hardness of optical plastic coatings, and achieve high light transmittance, high hardness, wear resistance, and high temperature resistance Effect

Inactive Publication Date: 2014-12-24
SHANGHAI INST OF TECH
View PDF5 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] One of the objectives of the present invention is to provide an optical plastic protective coating in order to solve the above-mentioned technical problems such as low hardness and poor wear resistance of the optical plastic coating, which has high light transmittance and high hardness at the same time. features

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] An optical plastic protective coating, calculated in parts by weight, its composition and content are as follows:

[0035] Tetraethyl silicate 2 parts

[0036] 5 parts of phenyltrimethoxysilane

[0037] 1.5 parts of coupling agent

[0038] 4 parts distilled water

[0039] Curing agent 0.02 parts

[0040] Catalyst 0.02 part;

[0041] The coupling agent is γ-(2,3-epoxypropoxy)propyltrimethoxysilane;

[0042] Described solidifying agent is the hydrochloric acid aqueous solution that mass percent concentration is 38%;

[0043] The catalyst is dibutyltin dilaurate.

[0044] The preparation method of above-mentioned a kind of optical plastic protective coating, the steps are as follows:

[0045] Add 2 parts of ethyl orthosilicate, 5 parts of phenyltrimethoxysilane, 1.5 parts of coupling agent, 4 parts of distilled water, 0.02 parts of curing agent and 0.02 parts of catalyst into the container in sequence, stir and leave it at room temperature for 24 hours to obtain co...

Embodiment 2

[0052] An optical plastic protective coating, calculated in parts by weight, its composition and content are as follows:

[0053] Tetraethyl silicate 2 parts

[0054] 6.5 parts of phenyltrimethoxysilane

[0055] 2 parts of coupling agent

[0056] 3 parts distilled water

[0057] Curing agent 0.03 part

[0058] Catalyst 0.04 part;

[0059] The coupling agent is γ-methacryloxypropyltrimethoxysilane;

[0060] Described curing agent is the sulfuric acid aqueous solution that mass percent concentration is 98%;

[0061] Described catalyst is stannous octoate.

[0062] The preparation method of above-mentioned a kind of optical plastic protective coating, the steps are as follows:

[0063] Add 2 parts of tetraethyl orthosilicate, 6.5 parts of phenyltrimethoxysilane, 2 parts of coupling agent, 3 parts of distilled water, 0.03 parts of curing agent and 0.04 parts of catalyst into the container in sequence, and leave it at room temperature for 24 hours after stirring to obtain col...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
transmittivityaaaaaaaaaa
transmittivityaaaaaaaaaa
transmittivityaaaaaaaaaa
Login to view more

Abstract

The invention discloses an optical plastic protection coating and a preparation method thereof. The optical plastic protection coating comprises the following raw materials in parts by weight: 2 parts of ethyl orthosilicate, 5-6.5 parts of phenyl trimethoxy silane, 1.5-2 parts of a coupling agent, 3-4 parts of distilled water, 0.02-0.03 part of a curing agent and 0.02-0.04 part of a catalyst. The preparation method comprises the following steps: adding the raw materials into a container, stirring, standing at the room temperature for 24 hours to obtain colorless transparent liquid, coating an optical plastic plate with the liquid, and drying at 80 DEG C to form a layer of coating on the optical plastic plate, wherein the coating is the optical plastic protection coating. The optical plastic protection coating has the characteristics of high transparency, high hardness and the like, can be widely used in the field of optical plastic protection, and also can be used in the fields of coatings, printing ink and the like.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to an optical plastic protective coating and a preparation method thereof. Background technique [0002] Compared with optical glass, optical plastic has many advantages such as light specific gravity, strong impact resistance, low cost, good light transmission, safety and reliability, etc., so it is widely used for making spectacle lenses, windshields on airplanes and cars, and cameras various lenses. However, optical plastics also have problems such as easy scratches and poor heat resistance. In order to overcome the above shortcomings, Zhang Chongzhao prepared a wear-resistant optical plastic protective optical plastic protective coating with a mixture of tetraalkoxysilane, trialkoxysilane, and dialkoxysilane through a catalytic reaction. The wear-resistant optical plastic protective coating has Certain hardness and wear resistance, but the siloxanes used ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D183/02C09D7/12C08J7/04
Inventor 张英强吴蓁陈丽顾亚峰崔边厅
Owner SHANGHAI INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap