Printing ink with high heat resistance

A high heat-resistance, ink technology, used in inks, household appliances, applications, etc., can solve problems such as limited materials, injury to printing workers, sticky deformation, etc., to achieve low solvent residue, good printing effect, and high adhesion. Effect

Inactive Publication Date: 2015-01-28
JURONG MAOYUAN WEAVING FACTORY
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the prior art, the ink used for printing has poor heat resistance, and is easy to fade or become sticky and deformed at high temperature, and the applicable materials are limited; and a large amount of toxic solvents such as benzenes and ketones are used in the preparation. In the production process, when the solvent is not handled properly, it is easy to cause harm to the body of the production workers. When the ink is used for printing, the volatilization of the toxic solvent in the ink will also cause certain harm to the body of the printing worker, and a certain amount of residue will remain on the printed matter. Solvents are bound to affect the health of users of printed materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] High heat resistance ink, including the following components: 5-10 parts of 1053 silicone resin, 2-4 parts of 9801 silicone resin, 1-2 parts of 804 silicone resin, 4-6 parts of thermoplastic acrylic resin, alcohol-soluble polyurethane solution 10-15 parts, 9-10 parts of ternary chlorine wax resin, 20-25 parts of titanium dioxide, 20-25 parts of acetic acid, 22-25 parts of ethanol, 1-2 parts of ethyl acetate, 3-4 parts of nitrile rubber, 4-5 parts of acetone, 4-5 parts of neoprene, 1-2 parts of toluene, said parts are parts by mass, and the mass concentration of the alcohol-soluble polyurethane solution is 20-25%. The solvent of the alcohol-soluble polyurethane solution is a mixture of isopropanol and ethanol with a mass ratio of 8:1, and the alcohol-soluble polyurethane solution PU-3514 is an alcohol-soluble polyurethane resin solution.

[0019] The above raw materials are mixed, stirred at 2000 rpm until the ternary chlorine wax resin is completely dissolved, the raw m...

Embodiment 2

[0021] High heat resistance ink, including the following components: 5-10 parts of 1053 silicone resin, 2-4 parts of 9801 silicone resin, 1-2 parts of 804 silicone resin, 4-6 parts of thermoplastic acrylic resin, alcohol-soluble polyurethane solution 10-15 parts, 9-10 parts of ternary chlorine wax resin, 20-25 parts of carbon black, 20-25 parts of acetic acid, 22-25 parts of ethanol, 1-2 parts of ethyl acetate, 3-4 parts of nitrile rubber, 4-5 parts of acetone, 4-5 parts of neoprene, 1-2 parts of toluene, said parts are parts by mass, and the mass concentration of the alcohol-soluble polyurethane solution is 20-25%. The solvent of the alcohol-soluble polyurethane solution is a mixture of isopropanol and ethanol with a mass ratio of 8:1, and the alcohol-soluble polyurethane solution PU-3514 is an alcohol-soluble polyurethane resin solution.

[0022] The above raw materials are mixed, stirred at 2000 rpm until the ternary chlorine wax resin is completely dissolved, the raw mater...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a printing ink with high heat resistance. The printing ink is prepared from the following constituents in parts by weight: 5-10 parts of 1053 organic silicon resin, 2-4 parts of 9801 organic silicon resin, 1-2 parts of 804 organic silicon resin, 4-6 parts of thermoplastic acrylic resin, 10-15 parts of an alcohol-dissolving polyurethane solution, 9-10 parts of ternary hydroxyl-modified vinyl resin copolymer, 20-25 parts of a pigment, 20-25 parts of acetic acid, 22-25 parts of ethanol, 1-2 parts of ethyl acetate, 3-4 parts of acrylonitrile butadiene rubber, and 4-5 parts of acetone, wherein the mass concentration of the alcohol-dissolving polyurethane solution is 20-25%. The printing ink disclosed by the invention is high in heat resistance, is free of any change in color, any deformation and glue phenomenon when the temperature is larger than 100 DEG C, and is suitable for printing various materials; furthermore, the adhesive force is high, so that the pigment is durable and free of falling off; the printing ink is quick in drying, and the solvent on the printed material after printing is low in residual quantity, so that physical and psychological health for printing ink makers, pressmen and printed material users is guaranteed.

Description

technical field [0001] The present invention relates to a high heat resistance ink. Background technique [0002] In the prior art, the ink used for printing has poor heat resistance, and is easy to fade or become sticky and deformed at high temperature, and the applicable materials are limited; and a large amount of toxic solvents such as benzenes and ketones are used in the preparation. In the production process, when the solvent is not handled properly, it is easy to cause harm to the body of the production workers. When the ink is used for printing, the volatilization of the toxic solvent in the ink will also cause certain harm to the body of the printing worker, and a certain amount of residue will remain on the printed matter. Solvents are bound to affect the health of users of printed materials. Contents of the invention [0003] The purpose of the present invention is to provide a high heat-resistant ink, which has strong heat resistance and is suitable for printi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/102C09D11/107
CPCC09D11/102C09D11/106C09D11/107
Inventor 史高峰李玉萍贡秀珍
Owner JURONG MAOYUAN WEAVING FACTORY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products