Epoxy anticorrosive antibacterial paint

An anti-corrosion, anti-bacterial and coating technology, applied in anti-corrosion coatings, epoxy resin coatings, polyurea/polyurethane coatings, etc., can solve the problems of corrosive media infiltrating into the film, corrosion and other problems, achieve low viscosity characteristics, reduce viscosity, and maintain good isolation. The effect of thermal properties

Active Publication Date: 2015-02-18
GUANGDONG TAISHI IND CO LTD
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the film formation process, the pinholes left by the solvent volatilization will cause the corrosive medium to penetrate under the film and cause corrosion.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The preparation method of epoxy anticorrosion and antibacterial coating is:

[0026] (1) By weight, weigh 150g of deionized water, 300g of bisphenol A epoxy resin, 150g of phenalkamine, 100g of antibacterial modified resin and nano-silicon solution with a weight percentage of 30:1, 85g of polyurethane, and 100g of nitrile Add rubber, 5g dispersant, 4g defoamer, 4g preservative together into the dispersion tank, disperse and stir at the speed of 300-500r / min in the dispersion tank for 5-10 minutes to obtain the mixture.

[0027] (2) Weigh 100g of flaky high wear-resistant pigments and fillers and 2g of leveling agent into the mixture, disperse and stir at the speed of 1000-1500r / min in the dispersion tank for 10-15 minutes to obtain epoxy anti-corrosion and anti-bacterial coating . The flaky high wear-resistant pigments and fillers consist of 320 mesh glass flakes with a content of 2g, 160 mesh glass flakes with a content of 3g and sericite powder with a content of 5g. ...

Embodiment 2

[0029] The preparation method of epoxy anticorrosion and antibacterial coating is:

[0030] (1) By weight, weigh 160g of deionized water, 400g of bisphenol A epoxy resin, 80g of phenalkamine, 50g of antibacterial modified resin and nano-silicon solution with a weight percentage of 30:1, 50g of polyurethane, and 120g of nitrile Add rubber, 9g dispersant, 8g defoamer, and 8g preservative together into the dispersion tank, disperse and stir at the speed of 300-500r / min in the dispersion tank for 5-10 minutes to obtain a mixture.

[0031] (2) Weigh 110g of flaky high wear-resistant pigments and fillers and 5g of leveling agent into the mixture, disperse and stir at the speed of 1000-1500r / min in the dispersion tank for 10-15 minutes to obtain an epoxy anti-corrosion and antibacterial coating . The flaky high wear-resistant pigments and fillers consist of 320 mesh glass flakes with a content of 2g, 160 mesh glass flakes with a content of 3g and sericite powder with a content of 6g...

Embodiment 3

[0033] The preparation method of epoxy anticorrosion and antibacterial coating is:

[0034] (1) By weight, weigh 150g of deionized water, 300g of bisphenol A epoxy resin, 80g of phenalkamine, 50g of antibacterial modified resin and nano-silicon solution with a weight percentage of 30:1, 100g of polyurethane, and 120g of nitrile Add rubber, 9g dispersant, 8g defoamer, and 8g preservative together into the dispersion tank, disperse and stir at the speed of 300-500r / min in the dispersion tank for 5-10 minutes to obtain a mixture.

[0035] (2) Weigh 170g of flaky high wear-resistant pigments and fillers and 5g of leveling agent into the mixture, disperse and stir at the speed of 1000-1500r / min in the dispersion tank for 10-15 minutes to obtain epoxy anti-corrosion and anti-bacterial coating . The flaky high wear-resistant pigments and fillers consist of 320 mesh glass flakes with a content of 4g, 160 mesh glass flakes with a content of 6g, and sericite powder with a content of 7g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an epoxy anticorrosive antibacterial paint which is composed of 30-40% of bisphenol A epoxy resin, 8-15% of phenol formaldehyde amine, 5-10% of antimicrobial modified resin and nano silicon solution in a weight ratio of 30:1, 5-10% of polyurethane, 10-18% of butadiene-acrylonitrile rubber, 10-17% of flaky high-wear-resistance pigment and filler, 0.5-0.9% of dispersing agent, 0.4-0.8% of defoaming agent, 0.4-0.8% of preservative, 0.2-0.5% of leveling agent and 15-23% of deionized water. The epoxy anticorrosive antibacterial paint has the advantages of favorable corrosion resistance, favorable impact resistance, favorable toughness and favorable mold resistance.

Description

technical field [0001] The invention relates to an epoxy anticorrosion and antibacterial coating. Background technique [0002] There are three main functions of anti-corrosion coatings: the shielding effect of paint film and sheet pigment, the corrosion inhibition and passivation effect of alkaline or oxidative pigments, and the electrochemical protection effect of zinc powder. Among them, the shielding effect that can isolate corrosive media such as water, oxygen, and ions is the most critical. At present, most of the commonly used marine heavy-duty anti-corrosion coatings are solvent-based coatings. During the film formation process, the pinholes left by the solvent volatilization will cause the corrosive medium to penetrate under the film and cause corrosion. The resulting corrosion product expands and breaks the coating, allowing the corrosive medium to diffuse, eventually causing the coating to flake off and fail. In addition, for the coating layer in special occasi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D175/04C09D5/08C09D7/12
CPCC08L2205/035C09D5/08C09D7/61C09D7/70C09D163/00C08L101/00C08L75/04C08L9/02C08K7/00C08K3/40C08K3/34
Inventor 徐妍玲
Owner GUANGDONG TAISHI IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap