Dual-component solvent-free epoxy damping adhesive for marine use and preparation method thereof

A solvent-free, two-component technology, applied in the direction of epoxy resin glue, adhesive, adhesive type, etc., can solve the problems such as changes in the damping performance of epoxy substrates, and achieve long product life, convenient construction, and bonding good sex effect

Inactive Publication Date: 2015-03-04
SHISHI GUOGAO ELECTRONICS TECH
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, all these methods use polyetheramine as a toughening agent to achieve the purpose of internal toughening of epoxy resin by replacing part of the curing agent. Since polyetheramine cannot be introduced into epoxy materials in large quantities, it is not enough to make the epoxy resin tougher. The damping properties of oxygen-based materials change significantly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A preparation method of a two-component solvent-free epoxy damping adhesive for ships is prepared by mixing component A and component B at a weight ratio of 100:22.

[0043] Add 35 parts of D2000 polyetheramine and 10 parts of D400 polyetheramine to 80 parts of JX021 epoxy resin, continue to stir for 15 minutes, and place it at room temperature for 48 hours to obtain modified polyetheramine; add 15 parts of 6002 epoxy resin, 60 modified polyether amine and 10 parts of 502 active diluent are mixed evenly under stirring, add 1 part of TEGO Airex 900, 6 parts of dispersant S-100 and 6 parts of KH560, continue to stir evenly, then add 50 parts of flame retardant, Stir for 10 minutes, grind twice with a three-roller, and use a scraper to check that when the particle size reaches 40μm or less, component A can be obtained; 50 parts of 5506 curing agent, add 2 parts of accelerator under stirring, and then stir for 15 After a few minutes, the B component is obtained; the raw materi...

Embodiment 2

[0046] A method for preparing a two-component solvent-free epoxy damping adhesive for ships is prepared by mixing component A and component B at a weight ratio of 100:20.

[0047] Add 50 parts of D2000 polyetheramine and 10 parts of D400 polyetheramine to 100 parts of 5749 epoxy resin, continue to stir for 15 minutes, and leave it at room temperature for 48 hours to obtain modified polyetheramine; add 20 parts of 618 epoxy resin, 60 modified polyether amine and 10 parts of 5748 active diluent are mixed evenly under stirring, add 1.5 parts of TEGO Airex 900, 5 parts of dispersant S-100 and 6 parts of KH560, continue to stir evenly, then add 60 parts of flame retardant, Stir for 10 minutes, grind twice with a three-roller, and use a scraper to check that when the particle size is below 40μm, you can obtain component A; 50 parts of 5506 curing agent under stirring, 2 parts accelerator, and stirring for 15 minutes Then obtain the B component; mix the raw materials of the A and B comp...

Embodiment 3

[0050] A preparation method of a two-component solvent-free epoxy damping adhesive for ships is prepared by mixing component A and component B at a weight ratio of 100:23.

[0051] Add 40 parts of D2000 polyetheramine to 70 parts of JX021 epoxy resin, continue to stir for 15 minutes, and place it at room temperature for 48 hours to obtain modified polyetheramine; stir 15 parts of 618 epoxy resin and 60 modified polyetheramine Mix well, add 1.5 parts of TEGO Airex 900, 5 parts of dispersant S-100 and 5 parts of KH560, continue to stir evenly, then add 50 parts of flame retardant, stir for 10 minutes, grind twice with a three-roller, and scrape When the plate fineness meter checks that the particle size reaches 40μm or less, component A can be obtained; 60 parts of 5506 curing agent are added with 2 parts of accelerator under stirring, and then stirred for 15 minutes to obtain component B; combine A and B The raw materials are mixed uniformly to obtain a two-component solvent-free ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Initial viscosityaaaaaaaaaa
Initial viscosityaaaaaaaaaa
Initial viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a dual-component solvent-free epoxy damping adhesive for marine use and a preparation method thereof. The preparation method comprises the following steps: (1) preparing a component A: uniformly mixing epoxy resin, modified polyether amine and an active diluent while stirring, adding a defoaming agent, a dispersant and a coupling agent, further uniformly mixing while stirring, adding a flame retardant, stirring for 10 minutes, and milling twice with a three-roller mill to obtain the A component; (2) preparing a component B: uniformly stirring an epoxy curing agent, polyether amine and an accelerator to obtain the component B; and (3) preparing a coating: uniformly mixing the component A obtained in the step (1) and the component B obtained in the step (2) at a weight ratio of 100: (10-30) to obtain the product, wherein the modified polyether amine is obtained by reacting bisepoxyl epoxy resin and polyether amine. Compared with the prior art, dual-component solvent-free epoxy damping adhesive has the advantages of long pot life, stable heat release, good flame retardancy, no VOC (Volatile Organic Compounds) and good adhesion, is convenient to construct and is cured at room temperature; the material has high loss factor at room temperature and is corrosion-resistant and vibration-proof.

Description

Technical field [0001] The invention relates to a polymer-based functional material and a preparation method thereof, in particular to a two-component solvent-free epoxy damping adhesive for ships. The material has good damping performance at room temperature and is mainly suitable for ship vibration reduction The technical field of noise reduction processing. Background technique [0002] The application of damping materials is the most effective way to reduce vibration and noise in the shipbuilding industry. With the advancement of shipbuilding technology, damping materials are more and more widely used in the modern shipbuilding industry. Damping coatings can be laid on the main engine seat, the engine room front wall and the engine room floor frame, which can consume excitation energy and reduce vibration response. It can also reduce the transmission of structural noise. It can also be used for hydrofoil noise reduction of hydrofoils, submarine propellers, and ship bottom p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J163/00C09J11/08C09J11/06
Inventor 陈海波
Owner SHISHI GUOGAO ELECTRONICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com