A coating and oil-resistant technology, which is applied in the direction of anti-corrosion coatings, wax coatings, coatings, etc., can solve the problems of easy curing and inconvenient use of anti-corrosion and oil-resistant coatings, and achieve a product suitable for long-term construction operations, excellent impact resistance, and excellent performance Effect
Inactive Publication Date: 2015-03-11
SUZHOU MINGXUAN FLOORING COATINGS
View PDF3 Cites 5 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The main technical problem to be solved by the present invention is to provide an anti-corrosion and oil-resistant coating, whi
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0017] Embodiment 1 of the present invention includes: an anti-corrosion and oil-resistant paint, including components in the following proportions:
[0018] 12 parts of m-xylenol phenolic resin
[0019] 3.6 parts of dibutyl phthalate
[0020] Polymer resin emulsion 12 parts
[0021] Silicon alloy powder 5 parts
[0022] Modified inorganic silicate 2.0 parts
[0023] Chlorinated Paraffin 15 parts
[0024] Sodium Hexaphosphate 4 parts
[0025] 12 parts of methyl cellulose
[0026] 0.2 parts of defoamer
[0027] Thickener 0.3 parts.
Embodiment 2
[0028] Embodiment 2 of the present invention includes: an anti-corrosion and oil-resistant paint, including components in the following proportions:
[0029] 17 parts of m-xylenol phenolic resin
[0030] 4.2 parts of dibutyl phthalate
[0031] 14 parts of polymer resin emulsion
[0032] Silicon alloy powder 6 parts
[0033] 2.3 parts of modified inorganic silicate
[0034] Chlorinated Paraffin 17 parts
[0035] 6 parts of sodium hexaphosphate
[0036] 14 parts of methyl cellulose
[0037] Antifoaming agent 0.6 parts
[0038] Thickener 0.5 parts.
Embodiment 3
[0039] Embodiment 3 of the present invention includes: an anti-corrosion and oil-resistant paint, including components in the following proportions:
[0040] 23 parts of m-xylenol phenolic resin
[0041] 5.2 parts of dibutyl phthalate
[0042] 16 parts of polymer resin emulsion
[0043] Silicon alloy powder 8 parts
[0044] Modified inorganic silicate 2.6 parts
[0045] Chlorinated Paraffin 20 parts
[0046] 8 parts of sodium hexaphosphate
[0047] 15 parts of methyl cellulose
[0048] Antifoaming agent 0.8 parts
[0049] Thickener 0.6 parts.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses an anticorrosive oil-resistant paint. The anticorrosive oil-resistant paint comprises the following constituents according to the content ratio: 12 to 23 parts of m-xylene phenolic resin, 3.6 to 5.2 parts of phthalic acid dibutyl ester, 12 to 16 parts of a polymer resin emulsion, 5 to 8 parts of silicon alloy powder, 0.2 to 2.6 parts of modified inorganic silicate, 15 to 20 parts of chlorinated paraffin, 4 to 8 parts of sodium hexametaphosphate, 12 to 15 parts of methylcellulose, 0.2 to 0.8 part of an antifoaming agent, and 0.3 to 0.6 part of a thickening agent. By adopting the mode, the anticorrosive oil-resistant paint is stable in performance after a paint film is dried, more excellent in performances of oil resistance, water resistance and oil-water mixture resistance, good in adhesive force, and good in flexibility, abrasive resistance and shock resistance, has low probabilities of curing and blocking, and is suitable for long-term construction operation.
Description
Technical field [0001] The invention relates to the field of architectural coatings, in particular to an anticorrosive and oil resistant coating. Background technique [0002] The oil-resistant and anticorrosive coating has stable and reliable performance, and the anti-corrosion period is more than ten years. It is a new type of industrial coating with excellent performance and meets the characteristics of environmental protection coatings. It is environmentally friendly and non-toxic. The matching performance is good. Due to the new curing agent, it is not only low in toxicity, but also has a wide adaptability to the construction temperature. It can be constructed at high temperature or cured at low temperature. However, due to long-term storage or exposure to air, it is easy to solidify into blocks and difficult to use. Summary of the invention [0003] The main technical problem solved by the present invention is to provide an anti-corrosion and oil-resistant paint, which solv...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).