A kind of anti-chemical penetration multi-layer composite adhesive tape and preparation method thereof

A multi-layer composite, chemical-proof technology, applied in textiles and papermaking, etc., can solve the problems of limited protection spectrum and insufficient organic solvent protection ability, and achieve the effect of low price, superior anti-virus performance and high value creation.

Active Publication Date: 2016-06-29
SHANXI XINHUA CHEM
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the tapes used in skin protection equipment in the domestic market are all coated or calendered with a single rubber, and the reinforcing material is mainly nylon. First, the protection spectrum is not wide, and only a limited number of substances can be protected; Obvious lack of ability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of anti-chemical permeation multi-layer composite tape, comprising a base cloth, one of the surfaces of the base cloth is coated with a fluororubber layer, and the other surface of the base cloth and the surface of the fluororubber layer are coated with a neoprene layer;

[0024] Wherein, the base cloth is aramid fiber;

[0025] Described fluororubber layer is to be made by the raw material of following parts by weight, and every part is 1kg:

[0026] Fluorine rubber: 100, bisphenol AF: 2, magnesium oxide: 8.5, calcium hydroxide: 7, talcum powder: 45, pigment: 10;

[0027] Described neoprene layer is to be made by the raw material of following parts by weight, and every part is 1kg:

[0028] Neoprene: 100, zinc oxide: 7, magnesium oxide: 3, accelerator NA-22: 1, stearic acid: 2, flame retardant: 70, pigment: 10;

[0029] The preparation method of the above-mentioned chemical permeation-resistant multi-layer composite adhesive tape includes the following steps: ...

Embodiment 2

[0035] A kind of anti-chemical permeation multi-layer composite tape, comprising a base cloth, one of the surfaces of the base cloth is coated with a fluororubber layer, and the other surface of the base cloth and the surface of the fluororubber layer are coated with a neoprene layer;

[0036] Wherein, the base cloth is aramid fiber;

[0037] Described fluororubber layer is to be made by the raw material of following parts by weight, and every part is 500g:

[0038] Fluorine rubber: 100, bisphenol AF: 1.7, magnesium oxide: 10, calcium hydroxide: 5, talcum powder: 30, pigment: 9;

[0039] Described neoprene layer is to be made by the raw material of following parts by weight, and every part is 500g:

[0040] Neoprene: 100, zinc oxide: 5, magnesium oxide: 4.5, accelerator NA-22: 1.5, stearic acid: 1.5, flame retardant: 50, pigment: 5;

[0041] The preparation method of the above-mentioned chemical permeation-resistant multi-layer composite adhesive tape includes the following ...

Embodiment 3

[0047] A kind of anti-chemical permeation multi-layer composite tape, comprising a base cloth, one of the surfaces of the base cloth is coated with a fluororubber layer, and the other surface of the base cloth and the surface of the fluororubber layer are coated with a neoprene layer;

[0048] Wherein, the base cloth is aramid fiber;

[0049] Described fluororubber layer is to be made by the raw material of following parts by weight, every part is 10kg:

[0050] Fluorine rubber: 100, bisphenol AF: 1.5, magnesium oxide: 9.5, calcium hydroxide: 8, talcum powder: 40, pigment: 6;

[0051] Described neoprene layer is to be made by the raw material of following parts by weight, and every part is 10kg:

[0052] Neoprene: 100, zinc oxide: 5, magnesium oxide: 5, accelerator NA-22: 1, stearic acid: 1.5, flame retardant: 65, pigment: 8;

[0053] The preparation method of the above-mentioned chemical permeation-resistant multi-layer composite adhesive tape includes the following steps: ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a multilayer composite adhesive tape preventing chemicals from penetrating and a preparation method thereof. The multilayer composite adhesive tape is prepared by coating aramid fiber base cloth with multiple rubber, concretely, one surface of the base cloth is coated with a fluorubber layer, and the other surface of the base cloth and the surface of the fluorubber layer are both coated with a chloroprene rubber layer. The preparation technology of the multilayer composite adhesive tape comprises preparing base cloth, coating one surface of the base cloth with the fluorubber layer, performing semi-sulfuration, coating the two surfaces of the coated base cloth with the chloroprene rubber layer, performing complete sulfuration, and obtaining the finished product adhesive tape. The multilayer composite adhesive tape employs aramid fiber fabric resistant to both acids and alkalis, possesses strong physical mechanical performances and is better than a nylon material. The multilayer composite adhesive tape has relatively strong acid and alkali resistance and chemical toxic agent resistance, and has the protection time up to 4 h. The multilayer composite adhesive tape has relatively good flame retardation performance, and can work at a high temperature. The multilayer composite adhesive tape employs chloroprene rubber and fluorubber as coating materials, is low in cost and superior in antitoxin performance.

Description

technical field [0001] The invention relates to the technical field of protective equipment, in particular to a chemical permeation-resistant multilayer composite adhesive tape and a preparation method thereof. Background technique [0002] Multi-layer composite tape is an effective protective material for high-risk chemicals, military poisons that endanger life immediately, and radioactive pollution, and protects personnel from poisonous and harmful chemical industrial products, organic solvents, and strong corrosive substances. [0003] At present, multi-layer composite materials in the world are mostly composed of 3-5 layers of materials, with a thickness of 0.3mm-0.5mm and a layer thickness of about tens of microns. [0004] At present, the tapes used in skin protection equipment in the domestic market are all coated or calendered with a single rubber, and the reinforcing material is mainly nylon. First, the protection spectrum is not wide, and only a limited number of s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06N3/18B32B25/08B32B25/18
CPCD06N3/0034D06N3/04D06N3/047D06N3/183D06N3/186D06N2201/0272
Inventor 王慧秦牡丹杨建功王立功常慧芳雷小军崔江舟金世婧赵卯青
Owner SHANXI XINHUA CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com