Heat-insulating coating for outer walls

A technology for heat-insulating coatings and exterior walls, applied in the direction of coatings, etc., can solve the problems of cumbersome preparation process, high production cost, and expensive price, and achieve the effects of high bonding strength, prolonging service life, and reducing indoor temperature

Inactive Publication Date: 2015-03-25
韦棋
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The nano-modified silicone acrylic emulsion and nano-modified hollow opaque polymers used in the preparation process are cumbersome, the production cost is high, and the whole coating is expensive, which is not conducive to popularization.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] An exterior wall heat-insulating coating, made of the following raw materials in parts by weight: 15 parts of hollow ceramic microspheres, 10 parts of diatomite, 25 parts of heavy calcium, 8 parts of talcum powder, 30 parts of mica, 5 parts of titanium dioxide, 10 parts of zinc, 10 parts of acrylic elastic emulsion, 1 part of hydroxycellulose, 1 part of auxiliary agent, 80 parts of water, wherein said auxiliary agent is defoamer, dispersant, leveling agent, lignocellulose thickener, moistening agent Wetting agent, film forming agent, and various auxiliary components are mixed in equal parts.

[0015] The preparation process of the above coating can be as follows: put water into the mixing tank, add lignocellulose thickener and hydroxycellulose at 400-500 rpm, stir for 8 minutes, add dispersant, defoamer, wetting agent, Titanium dioxide, zinc oxide, disperse at 1000-1500 rpm for 25 minutes, grind until the fineness is less than 50 microns, then add acrylic elastic emulsi...

Embodiment 2

[0017] A thermal insulation coating for exterior walls, made of the following raw materials in parts by weight: 30 parts of hollow ceramic microspheres, 20 parts of diatomite, 10 parts of heavy calcium, 18 parts of talcum powder, 15 parts of mica, 12 parts of titanium dioxide, 3 parts of zinc, 2 parts of acrylic acid elastic emulsion, 8 parts of hydroxycellulose, 5 parts of auxiliary agent, 150 parts of water, wherein said auxiliary agent is defoamer, dispersant, film-forming agent, and each auxiliary agent component is according to Mix equal parts.

[0018] The preparation process of the above coating can be as follows: put water into the mixing tank, add hydroxycellulose at 400-500 rpm, stir for 8 minutes, add dispersant, defoamer, titanium dioxide, zinc oxide, and add hydroxycellulose at 1000-1500 rpm. Disperse for 20 minutes at a speed of 400-500 rpm, and then grind until the fineness is less than 50 microns, then add acrylic elastic emulsion and film-forming agent at a sp...

Embodiment 3

[0020] A thermal insulation coating for exterior walls, made of the following raw materials in parts by weight: 22 parts of hollow ceramic microspheres, 15 parts of diatomaceous earth, 18 parts of heavy calcium, 12 parts of talcum powder, 20 parts of mica, 8 parts of titanium dioxide, 5 parts of zinc, 7 parts of acrylic elastic emulsion, 4 parts of hydroxycellulose, 3 parts of auxiliary agent, 115 parts of water, wherein said auxiliary agent is dispersant, leveling agent, lignocellulose thickener, wetting agent, and The auxiliary components are mixed in equal parts.

[0021] The preparation process of the above coating can be as follows: put water into the mixing tank, add lignocellulose thickener and hydroxyl cellulose at 400-500 rpm, stir for 8 minutes, add dispersant, wetting agent, titanium dioxide, oxidation Zinc, disperse at a speed of 1000-1500 rpm for 18 minutes, grind until the fineness is less than 50 microns, then add acrylic elastic emulsion and leveling agent at a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a heat-insulating coating for outer walls. The heat-insulating coating is prepared from raw materials in parts by weight as follows: 15-30 parts of hollow ceramic microspheres, 10-20 parts of diatomite, 10-25 parts of coarse whiting, 8-18 parts of talc powder, 15-30 parts of muscovite, 5-12 parts of titanium dioxide, 3-10 parts of zinc oxide, 2-10 parts of an elastic acrylic emulsion, 1-8 parts of hydroxyl cellulose, 1-5 parts of an aid and 80-150 parts of water. The prepared coating can effectively reduce temperatures of surfaces of the outer walls of buildings and indoor temperatures, has the good heat-insulating effect, is high in bonding strength to wall bodies, greatly improves heat-insulating, waterproof and corrosion-resistant functions of the wall bodies, and prolongs service lives of the wall bodies.

Description

technical field [0001] The invention relates to a coating, in particular to an exterior wall heat-insulating coating, which belongs to the technical field of building materials. Background technique [0002] With the increasingly acute energy problems, people pay more and more attention to energy saving and emission reduction while developing new energy sources. In the field of construction, thermal insulation coatings with advantages such as economy, environmental protection, and energy saving are used more and more widely as thermal insulation materials on the surface of buildings in the construction industry. Building exterior wall thermal insulation coatings are divided into three types according to their thermal insulation mechanism: 1) barrier coatings that increase the thermal resistance of the external wall to block and reduce heat conduction and heat convection; 2) reflective coatings that reflect visible light and infrared light to reduce the temperature of the ext...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/02C09D1/00C09D7/12C04B24/38C04B14/08C04B14/02
Inventor 韦棋
Owner 韦棋
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com