A large amount of fly ash ceramsite foam concrete and its preparation method

A foamed concrete and fly ash ceramsite technology, applied in the field of building materials, can solve problems such as large usage, and achieve the effects of reducing cement usage, ensuring strength, and reducing material costs

Active Publication Date: 2016-06-08
中冶武汉冶金建筑研究院有限公司
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the technical problems existing in the existing foam concrete, the present invention provides a large-volume fly ash ceramsite foam concrete and a preparation method thereof. production cost, and ensure that the foamed concrete has high mechanical strength and volume stability while being lightweight

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A large amount of fly ash ceramsite foam concrete and its preparation method
  • A large amount of fly ash ceramsite foam concrete and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Embodiment 1: A preparation method of a large amount of fly ash ceramsite foam concrete, its raw material composition and the mass ratio of each component are arranged as follows, P.O42.5 ordinary Portland cement: II grade fly ash: pottery Lightweight aggregate: water: polycarboxylate superplasticizer: aluminum carbonate: protein-type KC-16 foaming agent: polypropylene fiber with a length of 8 mm = 190:210:300:180:0.9:5:1.7:1.2, The ceramsite light aggregate is compounded with ceramsite with large and small particle sizes. The particle size of the large particle size ceramsite is 20-28mm, and the particle size of the small particle size ceramsite is 8-15mm. The mass ratio is 180:120.

[0029] The concrete molding steps of above-mentioned foamed concrete are as follows:

[0030] (1) Add P.O42.5 ordinary Portland cement, Class II fly ash, ceramsite light aggregate, aluminum carbonate, and polypropylene fiber with a length of 8mm to the mixer for pre-mixing according to t...

Embodiment 2

[0037] A method for preparing large-volume fly ash ceramsite foamed concrete, the composition of its raw materials and the mass ratio of each component are arranged as follows, P.O42.5 ordinary Portland cement: Class II fly ash: ceramsite light aggregate : Tap water: Polycarboxylate water reducer: Sodium aluminate: Rosin-type KC-15 foaming agent: Polyethylene fiber with a length of 10 mm=215:215:290:170:1.3:13:0.4:1.2. The ceramsite light aggregate is compounded with ceramsites with large and small particle sizes. The particle size of the large particle size ceramsite is 15-20mm, and the particle size of the small particle size ceramsite is 3-10mm. The mass ratio is 200:90.

[0038] The concrete molding steps of above-mentioned foamed concrete are as follows:

[0039] (1) Add P.O42.5 ordinary Portland cement, Class II fly ash, ceramsite light aggregate, sodium aluminate, and polyethylene fiber with a length of 10 mm into the mixer for pre-treatment. Stir, the stirring speed ...

Embodiment 3

[0046] A preparation method of a large amount of fly ash ceramsite foam concrete, the raw material composition and the mass ratio of each component are as follows, P.O42.5 ordinary Portland cement: II grade fly ash: S95 grade granulated blast furnace slag Powder: ceramsite light aggregate: water: polycarboxylate superplasticizer: sodium aluminate: protein foaming agent: polyvinyl alcohol fiber with a length of 6-9mm = 180:220:30:290:170:1.3:13 :1.7:1.2. The ceramsite light aggregate is compounded with ceramsite with large and small particle sizes, the average particle size of large particle size ceramsite is 22-26mm, and the average particle size of small particle size ceramsite is 8-11mm, The mass ratio of the two is 190:100; the water is tap water meeting the water standard for concrete, and the protein foaming agent can be a commercially available common protein foaming agent.

[0047] The concrete molding steps of above-mentioned foamed concrete are as follows:

[0048] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
power levelaaaaaaaaaa
densityaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of high-volume coal ash ceramsite foam concrete. The preparation method of the ceramsite foam concrete comprises the following steps: putting 38%-50% of a binding material, 29%-40% of ceramsite lightweight aggregates, 0.5%-1.5% of an excitant and 0.12%-0.14% of a fiber into a stirrer, and stirring evenly; simultaneously adding 0.04%-0.20% of a foaming agent and foam which is formed by a part of water in a foaming machine and has the particle sizes of 50-1,000mu m, the residual water and 0.09%-0.15% of a water reducer into the stirrer, and stirring with powder evenly to form slurry; adding the foam into the slurry, stirring evenly, and then pouring into a mold to mold; and demolding to prepare the ceramsite foam concrete of which the density is 300-800kg / m<3>. According to the formula provided by the invention, low-cost coal ashes are taken as a main raw material, and the material cost is reduced; meanwhile, the volume-weight of the concrete is reduced by adding the ceramsite lightweight aggregates with different particle sizes; and the mechanical strength and the stability of the concrete are effectively improved.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a large-volume fly ash ceramsite foam concrete and a preparation method thereof. Background technique [0002] At present, the common wall thermal insulation materials in my country mainly include organic thermal insulation materials and inorganic thermal insulation materials, among which foamed concrete is a typical inorganic thermal insulation material. The main application field of foam concrete is building thermal insulation, accounting for about 80% of its total output. Compared with common organic insulation materials on the market such as polystyrene foam board and phenolic foam board, foam concrete has the advantages of high strength, long service life and good fire resistance. The existing foam concrete itself has the disadvantage of relatively high bulk density. If the bulk density is reduced by increasing the foam content, the foamed concrete pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/02C04B28/00C04B16/06C04B14/02
Inventor 曾明王智周紫晨张冰陈晶
Owner 中冶武汉冶金建筑研究院有限公司