Bioactive degradable coral hydroxyapatite artificial bone

A coral hydroxyapatite and biologically active technology, applied in medical science, prostheses, etc., can solve the problems of artificial bone degradability, poor osteoinductive activity, etc., achieve good bone conduction activity, cheap and sufficient, and not easy churn effect

Active Publication Date: 2015-04-01
筴文奎 +1
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the defects of unsatisfactory degradability and poor osteoinductive activity of the existing artificial bone, the present invention provides a bioactive degradable coral hydroxyapatite artificial bone and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bioactive degradable coral hydroxyapatite artificial bone
  • Bioactive degradable coral hydroxyapatite artificial bone
  • Bioactive degradable coral hydroxyapatite artificial bone

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0070] The present invention provides a bioactive degradable coral hydroxyapatite artificial bone. The artificial bone includes a bracket, and the bracket is attached with osteoinducing active cytokines and slow-release agents; the bracket includes a bracket body, and the bracket body is Coral, the surface of the support body is covered with a layer of hydroxyapatite; the osteoinductive cytokine is recombinant human bone morphogenic protein-2 mature peptide; the slow-release agent is a combination of collagen and fibronectin, collagen and fibronectin The mass ratio is 1:1.

[0071] The amino acid sequence of the recombinant human bone morphogenic protein-2 mature peptide is as follows:

[0072] KRLKSSCKRHPLYVDFSDVGWNDWIVAPPGYHAFYCHGECPFPLADHLNSTNHAIVQTLVNSVNSKIPKACCVPTELSAISMLYLDENEKVVLKNYQDMVVEGCGCR (see SEQ ID NO: 1).

[0073] The artificial bone is granular, with a diameter of 2-6 mm, the diameter of the micropores is 77-180 μm, and the porosity of the micropores is 8%-11%...

Embodiment 2

[0080] The present invention provides a bioactive degradable coral hydroxyapatite artificial bone. The artificial bone includes a bracket, and the bracket is attached with osteoinducing active cytokines and slow-release agents; the bracket includes a bracket body, and the bracket body is Coral, the surface of the support body is covered with a layer of hydroxyapatite; the osteoinductive cytokine is recombinant human bone morphogenic protein-2 mature peptide; the slow-release agent is selected from the combination of collagen and hyaluronic acid, collagen and hyaluronic acid The mass ratio of acid is 1:1.

[0081]The amino acid sequence of the recombinant human bone morphogenic protein-2 mature peptide is as follows:

[0082] KRLKSSCKRHPLYVDFSDVGWNDWIVAPPGYHAFYCHGECPFPLADHLNSTNHAIVQTLVNSVNSKIPKACCVPTELSAISMLYLDENEKVVLKNYQDMVVEGCGCR. (see sequence 1)

[0083] The support is granular, with a diameter of 5-6 mm, the diameter of the micropores is 77-180 μm, and the porosity of th...

Embodiment 3

[0089] The present invention provides a bioactive degradable coral hydroxyapatite artificial bone. The artificial bone includes a bracket, and the bracket is attached with osteoinducing active cytokines and slow-release agents; the bracket includes a bracket body, and the bracket body is Coral, the surface of the bracket body is covered with a hydroxyapatite layer; the osteoinducing cytokine is recombinant human bone morphogenic protein-2 mature peptide; the slow-release agent is a combination of hyaluronic acid and polyvinylpyrrolidone, hyaluronic acid The mass ratio to polyvinylpyrrolidone is 1:1.

[0090] The amino acid sequence of the recombinant human bone morphogenic protein-2 mature peptide is as follows:

[0091] KRLKSSCKRHPLYVDFSDVGWNDWIVAPPGYHAFYCHGECPFPLADHLNSTNHAIVQTLVNSVNSKIPKACCVPTELSAISMLYLDENEKVVLKNYQDMVVEGCGCR. (see sequence 1)

[0092] The artificial bone is granular, with a diameter of 4-6 mm, the diameter of the micropores is 77-180 μm, and the porosity o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Apertureaaaaaaaaaa
Diameteraaaaaaaaaa
Apertureaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of medical biological materials, in particular to a bioactive degradable coral hydroxyapatite artificial bone and a preparation method thereof. The artificial bone comprises a bracket, wherein bone-inducing active cell factors and controlled release formulations are attached onto the bracket; the bracket comprises a bracket body; the bracket body is coral; a hydroxyapatite layer coats the surface of the bracket body; the bone-inducing active cell factors are made of recombinant human bone morphogenetic protein-2 mature peptide; the controlled release formulations are selected from collagen, fibronectin, hyaluronic acid and the like; the bracket is granular or cylindrical; the aperture range of micropores is 77-180 microns; the porosity of the micropores is 8-11%. According to verification results of the National Institute for the Control of Pharmaceutical and Biological Products (verification report numbers comprise QZ200701428 and QZ200804480) and the National Institutes for Food and Drug control (verification report number is QZ201206312), the artificial bone is excellent bone graft substitute.

Description

technical field [0001] The invention relates to the technical field of medical biomaterials, in particular to a biologically active and degradable coral hydroxyapatite artificial bone and a preparation method thereof. Background technique [0002] Patients with bone defects account for a high proportion of orthopedic patients. These patients cannot repair the defect through the body's own recovery mechanism, so bone transplantation must be performed. [0003] The material used for bone grafting treatment is called artificial bone for short. Artificial bone needs to have suitable size, suitable porosity and pore diameter, and have suitable materials and functions. [0004] An ideal bone graft material needs to have both osteoconductive and osteoinductive activities. Coral and coral-derived hydroxyapatite materials have a pore structure similar to that of human bone, and are widely used as scaffold materials for filling bone defects. Because of their good three-dimensional st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61L27/54A61L27/56A61L27/36A61L27/12
Inventor 筴文奎后力
Owner 筴文奎
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com