Water-based waterproof coating added with calcium sulfate whiskers and preparation method of coating

A calcium sulfate whisker and fireproof coating technology, which is applied in fireproof coatings, antifouling/underwater coatings, epoxy resin coatings, etc., can solve problems such as poor water solubility and aging resistance, affecting material properties, and poor thermal stability. To achieve the effect of strong adhesion, simple operation and excellent performance

Inactive Publication Date: 2015-04-29
SICHUAN MINGXIN JIAJIE NEW MATERIAL
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this system also has disadvantages such as high dosage which affects material properties, poor thermal stability, poor water solubility and aging resistance, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based waterproof coating added with calcium sulfate whiskers and preparation method of coating
  • Water-based waterproof coating added with calcium sulfate whiskers and preparation method of coating
  • Water-based waterproof coating added with calcium sulfate whiskers and preparation method of coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Embodiment 1: a kind of water-based fireproof coating that adds calcium sulfate whisker, it is made up of the raw material of following weight portion:

[0026]

[0027] The above-mentioned preparation method of adding the water-based fireproof coating of calcium sulfate whisker, it may further comprise the steps:

[0028] S1. Weighing: Weigh each raw material according to the above ratio, the average length-to-diameter ratio of calcium sulfate whiskers is 50-80, and the diameter is 1-4 μm, and set aside;

[0029] S2. Modification: an aqueous ethanol solution prepared with anhydrous ethanol and deionized water at a volume ratio of 3:1, adding aluminate coupling agent, aluminate coupling agent and calcium sulfate crystals to the ethanol solution The weight ratio of the whiskers is 1:20, stir at 800r / min, add calcium sulfate whiskers, adjust the pH of the solution system to 4 with glacial acetic acid, stir at 2300r / min for 1 hour, and then vacuum dry to obtain modified...

Embodiment 2

[0031] Embodiment 2: a kind of water-based fireproof coating that adds calcium sulfate whisker, it is made up of the raw material of following weight portion:

[0032]

[0033]

[0034] The above-mentioned preparation method of adding the water-based fireproof coating of calcium sulfate whisker, it may further comprise the steps:

[0035] S1. Weighing: Weigh each raw material according to the above ratio, the average length-to-diameter ratio of calcium sulfate whiskers is 50-80, and the diameter is 1-4 μm, and set aside;

[0036] S2. Modification: an aqueous ethanol solution prepared with anhydrous ethanol and deionized water at a volume ratio of 3:1, adding aluminate coupling agent, aluminate coupling agent and calcium sulfate crystals to the ethanol solution The weight ratio of the whiskers is 1:30, stir at 1000r / min, add calcium sulfate whiskers, adjust the pH value of the solution system to 5 with glacial acetic acid, stir at 2700r / min for 1 hour, and then vacuum dry...

Embodiment 3

[0038] Embodiment 3: a kind of water-based fireproof coating that adds calcium sulfate whisker, it is made up of the raw material of following weight portion:

[0039]

[0040] The above-mentioned preparation method of adding the water-based fireproof coating of calcium sulfate whisker, it may further comprise the steps:

[0041] S1. Weighing: Weigh each raw material according to the above ratio, the average length-to-diameter ratio of calcium sulfate whiskers is 50-80, and the diameter is 1-4 μm, and set aside;

[0042] S2. Modification: an aqueous ethanol solution prepared with anhydrous ethanol and deionized water at a volume ratio of 3:1, adding aluminate coupling agent, aluminate coupling agent and calcium sulfate crystals to the ethanol solution The weight ratio of the whiskers is 1:22, stir at a speed of 900r / min, add calcium sulfate whiskers, adjust the pH of the solution system to 4.5 with glacial acetic acid, stir at a speed of 2500r / min for 1 hour, and then vacuu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
aspect ratioaaaaaaaaaa
Login to view more

Abstract

The invention discloses a water-based waterproof coating added with calcium sulfate whiskers and a preparation method of the coating. The water-based waterproof coating is prepared from the following raw materials in parts by weight: 10-35 parts of calcium sulfate whiskers, 5-10 parts of vinyl perchloride resin, 14-20 parts of epoxy resin, 3-10 parts of dibutyl phthalate, 1-9 parts of a thickener, 3-6 parts of pigments, 1-5 parts of additives and 30-40 parts of water. The preparation method comprises the following steps: weighing; modifying; and mixing. The water-based waterproof coating added with calcium sulfate whiskers disclosed by the invention has excellent fireproof effect and anti-cracking property, low in cost of raw materials and non-toxic and environment-friendly. The method for preparing the coating is simple to operate, convenient to produce, low in requirement on equipment and suitable for industrial large-scaled production.

Description

technical field [0001] The invention belongs to the technical field of architectural coatings, and in particular relates to a water-based fireproof coating added with calcium sulfate whiskers and a preparation method thereof. Background technique [0002] Architectural coatings have the functions of decoration, protection and habitability improvement. The proportions of various functions vary depending on the purpose of use. The decorative function is to improve the appearance value of a building by beautifying it. The protection function refers to the function of protecting the building from the influence and damage of the environment. Different types of protected objects have different requirements for protection functions. Decorative fireproof coating is a new type of coating that integrates decoration and fireproof functions. When the fire retardant coating is applied on the combustible base material, it can usually play a decorative role. Once a fire occurs, it can ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D127/24C09D5/18C09D5/14C09D7/12
CPCC08K2003/2241C09D163/00C09D5/14C09D5/18C09D7/61
Inventor 赵德明汪勇
Owner SICHUAN MINGXIN JIAJIE NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap