Rice and wheat straw active carbon powder artificial graphite friction material brake pad and manufacturing method thereof

A technology of activated carbon powder, rice and wheat straw, applied in friction linings, chemical instruments and methods, other chemical processes, etc., can solve problems such as pollution, waste of resources and the environment, and achieve noise reduction, friction coefficient stability, performance improvement and manufacturing. effect of motion

Active Publication Date: 2015-06-10
JIANGSU JINMAISUI NEW ENERGY TECH
View PDF4 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The annual output of crop straw in our country reaches more than 700 million tons, but most of these resources are burned

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rice and wheat straw active carbon powder artificial graphite friction material brake pad and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0040] A method for manufacturing a brake pad made of rice and wheat straw activated carbon powder artificial graphite friction material, comprising the following steps:

[0041] Step 1. Mixing: Stir the material for friction material 1 in a high-speed mixer for 30 minutes. The mixed material contains the following ingredients: 25 parts of rice straw composite fiber, 6 parts of phenolic modified resin, 10 parts of silica fume cotton 5 parts of potassium titanate whiskers, 0.5 parts of pyrite, 0.5 parts of carbon black, 1 part of alumina, 7 parts of 40 mesh brass powder, 15 parts of rice straw activated carbon powder, 5 parts of secondary reduced iron powder, Rice and wheat straw activated carbon powder 25 parts of artificial graphite; all materials are fully fused and released into barrels;

[0042] Step 2. Degreasing the steel back: remove the oil and rust on the steel back of the brake pad;

[0043] Step 3. Glue compounding: Dilute the special glue for steel back with alcoh...

Embodiment 3

[0055] The prepared brake pads include a friction material 1, a sound-absorbing sheet 2, a steel back 3 and an accessory 4, the friction material 1 is pasted on the steel back 3, the sound-absorbing sheet 2 is installed on the back of the steel back 3, and the steel back Attachment 4 is riveted on the 3, powder spraying or paint is sprayed on the steel back 3, and code spraying is also sprayed on the steel back 3.

[0056] The main technical and performance indicators of the prepared brake pads are as follows:

[0057] Friction coefficient 0.25-0.45;

[0058] Wear rate 0.2-0.4;

[0059] Lifespan of more than 60,000 kilometers;

[0060] No noise;

[0061] Thermal recession ≤ 20%;

[0062] Impact strength not less than 0.3J / cm2;

[0063] Wear rate≤0.2;

[0064] The thermal expansion rate (400℃±10℃) is not more than 2.5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a rice and wheat straw active carbon powder artificial graphite friction material brake pad and a manufacturing method thereof. The brake pad comprises a friction material, a noise elimination sheet, a steel back and an accessory, wherein the friction material comprises the following components: 25 parts of rice straw composite fibers, 6 parts of phenolic modified resin, 10 parts of wollastonite, 5 parts of potassium titanate whiskers, 0.5 parts of iron pyrite, 0.5 parts of carbon black, 1 part of aluminum oxide, 7 parts of 40-mesh brass powder, 15 parts of rice and wheat straw active carbon powder, 5 parts of secondary reduced iron powder and 25 parts of rice and wheat straw active carbon powder artificial graphite; the friction material is adhered on the steel back; the noise elimination sheet is mounted on the surface of the steel back; the accessory is riveted on the steel back. The prepared rice and wheat straw active carbon powder artificial graphite friction material enhances the toughness of the brake pad, improves the performance and the braking effect of the brake pad, guarantees stable friction coefficient of the brake pad, reduces frictional noise, is environment-friendly and pollution-free, and expands the utilization channel of rice and wheat straws.

Description

technical field [0001] The invention relates to a brake pad and a manufacturing method thereof, in particular to a brake pad made of rice straw activated carbon powder artificial graphite friction material and a manufacturing method thereof. Background technique [0002] The brake pads in motor vehicles are mainly made of various raw materials such as asbestos, steel fiber, and resin. Poor reliability, fast wear, easy aging and fracture, short service life and other defects. Secondly, because asbestos contains carcinogens, it has been banned by the state. At present, as a substitute for asbestos brake pads, they are generally made of mineral fiber, carbon fiber, steel fiber and other materials, but they all have low melting point, low thermal stability, poor heat dissipation effect, small friction coefficient, and poor braking performance to varying degrees. , Short service life, high manufacturing cost and other disadvantages, especially in the state of frequent braking o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): F16D69/02C09K3/14
Inventor 熊万军王兰芳
Owner JIANGSU JINMAISUI NEW ENERGY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap