Material pellets for halogen-free high-barrier polyolefin gasket and preparation method thereof

A high-barrier, polyolefin technology, applied in the field of polymer materials, can solve problems such as food hygiene and safety hazards, and achieve the effect of better environmental protection, better environmental protection and sanitation of pellets

Active Publication Date: 2017-08-25
湖北格霖威新材料科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

PVC bottle mats contain a variety of plasticizers that are harmful to the human body. Among them, the plasticizers are precipitated into the food. The phthalates and oxalic acid in them are carcinogens, so they pose a great safety hazard to food hygiene. Hidden danger

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A material pellet for a halogen-free high-barrier polyolefin gasket, which is made of the following raw materials in parts by weight: 55.3 parts of metallocene polyethylene, 15.2 parts of a compatibilizer, 19.4 parts of a toughening agent, and 1.5 parts of a processing aid , 0.5 part of antioxidant.

Embodiment 2

[0019] A material pellet for a halogen-free high-barrier polyolefin gasket, which is made of the following raw materials in parts by weight: 85.7 parts of metallocene polyethylene, 21.4 parts of a compatibilizer, 33.5 parts of a toughening agent, and 3.5 parts of a processing aid part, 1.9 parts of antioxidant.

Embodiment 3

[0020] Example 3: A pellet for a halogen-free high-barrier polyolefin gasket, which is made of the following raw materials in parts by weight: 55.3 parts of metallocene polyethylene, 21.4 parts of SBES, 19.4 parts of POE, 2.9 parts 1 part processing aid and 1 part antioxidant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a material particle for a halogen-free high-barrier polyolefin gasket and a preparation method thereof. The material particle is prepared from the following raw materials in parts by weight: 55.3-85.7 parts of metallocene polyethylene, 15.2-21.4 parts of compatibilizer, 19.4-33.5 parts of flexibilizer, 1.5-3.5 parts of processing agent, and 0.5-1.9 parts of anti-oxidant. During preparation, the material particles is prepared by the following steps: weighing each raw material according to the proportion, stirring in a stirrer, mixing uniformly, adding the mixed materials into an extruder, plasticizing, extruding, granulating and cooling, screening and drying finally, cooling, so as to obtain the material particle for a halogen-free high-barrier polyolefin gasket, wherein the extruding temperature is 160-180 DEG C. The products are non-toxic and odorless and free of any plasticization assistant, so the foot safety requirement is met completely, and the EU standard is met.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a material pellet for a halogen-free high-barrier polyolefin gasket and a preparation method thereof. Background technique [0002] At present, 90% of the special gaskets for food packaging lids in China are made of polyvinyl chloride (PVC). PVC bottle mats contain a variety of plasticizers that are harmful to the human body. Among them, the plasticizers are precipitated into the food. The phthalates and oxalic acid in them are carcinogens, so they pose a great safety hazard to food hygiene. Hidden danger. Therefore, the relevant national ministries and commissions have stipulated that since 2011, PVC in contact with food will be phased out. Foreign countries have begun to abandon PVC gasket materials as early as 20 years ago, and use non-PVC gasket particles. The main reasons are as follows: 1. Pressure from environmental protection groups on the use of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L23/08C08L53/02C08L23/16C08L75/04C08K13/02C08K5/09C08K3/30C08K3/16C08K5/134C08K5/526
CPCC08L23/06C08L2201/22C08L2205/03C08L2205/08C08L2207/04C08L53/025C08L23/0815C08K13/02C08L23/0853C08L23/16C08K5/1345C08L53/02C08L75/04C08K5/526C08K5/09C08K2003/3045C08K3/16
Inventor 郭庆时袁友诚程海
Owner 湖北格霖威新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products