Environment-friendly high-cushioning polyurethane packaging material

A packaging material and cushioning technology, which is applied in the field of environmentally friendly high-cushioning polyurethane packaging materials, can solve the problems of poor mechanical properties of polystyrene, high mold costs, and destructive effects of the atmosphere, achieving high foaming ratio and low cost. Low, light weight effect

Active Publication Date: 2017-08-15
河南铎润新材料有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Nowadays, the packaging of products mostly adopts molded or assembled polystyrene, the mold cost is high, and it is suitable for mass production; the spliced ​​polystyrene has poor mechanical properties and is easily broken by impact
However, traditional polyurethane foam packaging materials are inseparable from foaming agents. Most of the foaming agents used in polyurethane are destructive to the atmosphere or are flammable and explosive, have low safety factors, and are not conducive to environmental protection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Example 1: An environment-friendly high-buffering polyurethane packaging material, which is made by mixing combined polyether raw materials and polymethylene polyphenylisocyanate, wherein the combined polyether raw materials are composed of the following components according to the ratio: polyether triol 42 parts, 35 parts of polyether diol, 5 parts of chain extender, 3 parts of foam stabilizer, 25 parts of water, 0.5 part of dimethylaminoethyl ether, 0.45 part of triethylenediamine, polymethylene polyphenyl The ratio of polyisocyanate (PAPI) to combined polyether raw materials is 0.8:1. In this embodiment: the preferred polyether triol is 330N, produced by Shandong Dongda; the preferred polyether diol is 210, produced by Nanjing Jinling Petrochemical Co., Ltd., the chain extender is triethanolamine, produced by Jiangsu Luyuan Co., Ltd., and the foam stabilizer is preferred Polyurethane foam stabilizer, model: Momentive L-3633, polymethylene polyphenyl isocyanate (PAPI)...

Embodiment 2

[0014] Example 2: An environment-friendly high-buffering polyurethane packaging material, which is made by mixing polyether raw materials with polymethylene polyphenylisocyanate, wherein the polyether raw materials are composed of the following components: 45 parts of polyether triols , 40 parts of polyether glycol, 7 parts of chain extender, 5 parts of foam stabilizer, 30 parts of water, 0.6 part of dimethylaminoethyl ether, 0.5 part of triethylenediamine, of which polymethylene polyphenyl The ratio of isocyanate (PAPI) to combined polyether raw material is 1:1. Wherein in this embodiment, the chain extender is polyether 403, and the foam stabilizer is polyurethane foam stabilizer.

[0015] For the packaging material prepared by using the components of this embodiment, the performance test is as follows: in a beaker, weigh polyether triol, polyether diol, chain extender, foam stabilizer, water, dimethyl Aminoethyl ether and triethylenediamine were stirred and mixed, and left...

Embodiment 3

[0017] Example 3: An environment-friendly high-buffering polyurethane packaging material, which is made by mixing polyether raw materials with polymethylene polyphenylisocyanate, wherein the raw materials for polyether composites are the following components: 40 parts of polyether triols , 30 parts of polyether glycol, 3 parts of chain extender, 2 parts of foam stabilizer, 20 parts of water, 0.3 part of dimethylaminoethyl ether, 0.3 part of triethylenediamine, of which polymethylene polyphenyl The ratio of isocyanate (PAPI) to combined polyether raw material is 0.9:1. In this embodiment, the chain extender is triethanolamine.

[0018] For the packaging material prepared by using the components of this embodiment, the performance test is as follows: in a beaker, weigh polyether triol, polyether diol, chain extender, foam stabilizer, water, dimethyl Aminoethyl ether, triethylenediamine, and polymethylene polyphenylisocyanate were stirred and mixed, left to stand for 5 minutes, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly high-buffering-property polyurethane packaging material. The packaging material is formed by mixing a combined polyether raw material and polymethylene polyphenyl isocyanate, wherein the combined polyether raw material is composed of, by proportion, 40-45 parts of polyether trihydric alcohol, 30-40 parts of polyether glycol, 3-8 parts of chain extenders, 2-5 parts of foam stabilizers, 20-30 parts of water, 0.3-0.6 part of dimethylamino ethylether and 0.3-0.5 part of triethylene diamine. The proportion of the polymethylene polyphenyl isocyanate to the combined polyether raw material is 0.8-1.0:1. The material has a good buffering property, the buffering property is three times that of a general foaming material, and the material has good elasticity, and can be used repeatedly, and foamed and formed into the packaging material anytime and anywhere within a short time; as the water is used for replacing other foaming agents, intensity is low, the production cost is reduced, substances damaging an ozone layer are avoided, pollution is really reduced, and the environment-friendly effect of the foaming agent is completely achieved.

Description

technical field [0001] The invention relates to a packaging material, in particular to an environment-friendly polyurethane packaging material with high cushioning properties. Background technique [0002] Nowadays, the packaging of products is mostly made of molded or assembled polystyrene, the cost of the mold is high, and it is suitable for mass production; the mechanical properties of spliced ​​polystyrene are poor, and they are easily broken by impact. Traditional polyurethane foam packaging materials are inseparable from foaming agents. Most of the foaming agents used in polyurethane have destructive effects on the atmosphere or are flammable and explosive, have low safety factors, and are not conducive to environmental protection. Contents of the invention [0003] The purpose of the present invention is to solve the problems and deficiencies in the packaging materials in the prior art, and provide an environment-friendly polyurethane packaging material with high cu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/48C08G18/76C08J9/00C08G101/00
Inventor 孟繁勤
Owner 河南铎润新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com