Aluminate cement and preparation method thereof

A technology of aluminate cement and nickel silicate, which is applied in the field of building materials, can solve the problems of environmental pollution, failure to improve the long-term strength of aluminate cement, and occupying land, so as to improve high temperature resistance, improve long-term strength, and improve The effect of intensity

Inactive Publication Date: 2015-07-22
苏州市德莱尔建材科技有限公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can be seen from this that the technical solution is to use aluminum slag, calcareous materials, and aluminum-containing materials as raw materials. After preparing clinker, it is a kind of aluminate cement obtained by fine grinding. This method is a kind of aluminum slag waste. A new method of harmless utilization. Although its products meet the national quality standards, it still cannot improve the long-term strength of aluminate cement
[0006] Red mud, also known as red mud, is the industrial solid waste discharged after refining alumina from bauxite. In the aluminum industry, on average, 1.0-2.0 tons of red mud is produced for every ton of alumina produced. In a big country, a large amount of red mud is produced every year. Since a large amount of red mud cannot be fully and effectively utilized, it can only be piled up in a large area of ​​storage yard, occupying a large amount of land and causing serious pollution to the environment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminate cement and preparation method thereof
  • Aluminate cement and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A kind of aluminate cement, comprises each component of following mass percentage:

[0029] (1) Aluminate cement clinker 55.0%, of which alumina content is 53.0%;

[0030] (2) Barium slag 10.0%;

[0031] (3) Nickel silicate tailings 15.0%;

[0032] (4) Red mud 10.0%;

[0033] (5) Electric furnace slag 6.0%;

[0034] (6) Desulfurization gypsum 4.0%.

[0035] Aluminate cement is prepared according to the preparation method of aluminate cement provided by the present invention, and the preparation steps are as follows:

[0036] (1) Material preparation: Accurately weigh each component according to the mass content of each component;

[0037] (2) Pulverization: pulverize barium slag, nickel silicate tailings and electric furnace slag until the average particle size of the powder is 100um;

[0038] (3) Grinding: Mix the various components together according to the mass percentage and grind until the average particle size is 20um to obtain aluminate cement.

Embodiment 2

[0040] A kind of aluminate cement, comprises each component of following mass percentage:

[0041] (1) Aluminate cement clinker 75.0%, of which alumina content is 53.0%;

[0042] (2) Barium residue 3.0%;

[0043] (3) Nickel silicate tailings 5.0%;

[0044] (4) Red mud 5.0%;

[0045] (5) Electric furnace slag 7.0%;

[0046] (6) Desulfurization gypsum 5.0%.

[0047] Aluminate cement is prepared according to the preparation method of aluminate cement provided by the present invention, and the preparation steps are as follows:

[0048] (1) Material preparation: Accurately weigh each component according to the mass content of each component;

[0049] (2) Pulverization: pulverize barium slag, nickel silicate tailings and electric furnace slag until the average particle size of the powder is 100um;

[0050] (3) Grinding: Mix the various components together according to the mass percentage and grind until the average particle size is 20um to obtain aluminate cement.

Embodiment 3

[0052] A kind of aluminate cement, comprises each component of following mass percentage:

[0053] (1) Aluminate cement clinker 60.0%, of which alumina content is 53.0%;

[0054] (2) Barium residue 7.0%;

[0055] (3) Nickel silicate tailings 12.0%;

[0056] (4) Red mud 10.0%;

[0057] (5) Electric furnace slag 7.0%;

[0058] (6) Desulfurization gypsum 4.0%.

[0059] Aluminate cement is prepared according to the preparation method of aluminate cement provided by the present invention, and the preparation steps are as follows:

[0060] (1) Material preparation: Accurately weigh each component according to the mass content of each component;

[0061] (2) Pulverization: pulverize barium slag, nickel silicate tailings and electric furnace slag until the average particle size of the powder is 100um;

[0062] (3) Grinding: Mix the various components together according to the mass percentage and grind until the average particle size is 20um to obtain aluminate cement.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses aluminate cement and a preparation method thereof, and relates to the field of building materials. The aluminate cement comprises the following components in percentage by mass: (1) 55.0%-75.0% of aluminate cement clinker, (2) 3.0%-10.0% of barium slag, (3) 5.0%-15.0% of garnierite tailings, (4) 5.0%-15.0% of red mud, (5) 3.0%-10.0% of steel slag, and (6) 2.5%-5.0% of gypsum, wherein the content of aluminium oxide in the aluminate cement clinker is 47.0%-65.0%. The preparation method of the aluminate cement comprises the following steps: (1) preparing materials, (2) grinding, and (3) pulverizing. The aluminate cement has the characteristics of being high in hardening rate and high in hardening strength, and besides, effectively overcomes the defect that the long-term strength of the conventional aluminate cement is relatively low, and effectively uses various industrial wastes, and is a very ideal cement material.

Description

technical field [0001] The invention belongs to the field of building materials, in particular to an aluminate cement and a preparation method of the cement. Background technique [0002] Aluminate cement is a hydraulic cementitious material made of bauxite and limestone as raw materials, calcined clinker with calcium aluminate as the main component and alumina content of about 50%, and then finely ground. Aluminate cement is often yellow or brown, but also gray. The main minerals of aluminate cement are monocalcium aluminate and other aluminates, as well as a small amount of dicalcium silicate. [0003] Aluminate cement has fast setting and hardening speed, large cement hydration heat and concentrated heat release. It is mainly used in projects with urgent construction schedules. Even if it is constructed at -10°C, aluminate cement can quickly set and harden. It can be used Construction works in winter. Under ordinary hardening conditions, aluminate cement has a strong r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B11/30
Inventor 计慷
Owner 苏州市德莱尔建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products