Material for magnesium alloy doors and windows and production method of material

A production method, magnesium alloy technology, applied in the field of magnesium alloy door and window materials and its production, can solve the problems of affecting popularization and use, difficult processing, poor plasticity, etc., to improve water corrosion resistance, ensure corrosion resistance, and uniform structure stable effect

Inactive Publication Date: 2015-07-22
SUZHOU CITY WUZHONG DISTRICT XUKOU FENGSHOU MACHINERY PARTS FACTORY
View PDF10 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As people's living styles become more and more diverse, doors and windows are gradually occupying and expanding their market. At present, more door and window materials on the market are mainly aluminum alloy, color steel, and PVC materials, and aluminum alloy is because of its higher hardness, Light weight, no aging, beautiful and practical after color coati

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038]This embodiment provides a material for magnesium alloy doors and windows, which is composed of Mg, Al, Mn, Zn, Cu, Ni, Sc, P, Zr, Y, Ca, Sr, B, Co, and rare earth elements , its weight percentage components are: Al: 15%, Mn: 7%, Zn: 10%, Cu: 1%, Ni: 2%, Sc: 2%, P: 0.5%, Zr: 9%, Y: 3%, Ca: 8%, Sr: 4%, B: 4%, Co: 2%, rare earth element 3%, and the rest is Mg;

[0039] Rare earth elements are composed of Ce, Nd, Gd, Pr, Dy, Yb, La, Sm, each component by weight percentage is: Ce: 10%, Nd: 18%, Gd: 17%, Pr: 11%, Dy : 9%, Yb: 5%, La: 15%, Sm: 15%.

[0040] The production method of the above-mentioned magnesium alloy door and window material is operated according to the following specific steps:

[0041] (1) Turn on the smelting furnace to preheat for 13 minutes, add the above-mentioned chemical components as raw materials into Mg, Al, Mn, Ni, Sc, P, Zr, Y, Co, and adjust according to the component content, and place the raw materials in graphite Crucible, then put the grap...

Embodiment 2

[0055] This embodiment provides a material for magnesium alloy doors and windows, which is composed of Mg, Al, Mn, Zn, Cu, Ni, Sc, P, Zr, Y, Ca, Sr, B, Co, and rare earth elements , its weight percentage components are: Al: 20%, Mn: 8%, Zn: 12%, Cu: 3%, Ni: 3%, Sc: 3%, P: 1.0%, Zr: 7%, Y: 5%, Ca: 11%, Sr: 5%, B: 7%, Co: 4%, rare earth element 1%, and the rest is Mg;

[0056] Rare earth elements are composed of Ce, Nd, Gd, Pr, Dy, Yb, La, Sm, each component by weight percentage is: Ce: 15%, Nd: 15%, Gd: 20%, Pr: 8%, Dy : 8%, Yb: 4%, La: 20%, Sm: 10%.

[0057] The production method of the above-mentioned magnesium alloy door and window material is operated according to the following specific steps:

[0058] (1) Turn on the smelting furnace to preheat for 10 minutes, add the above-mentioned chemical components as raw materials to Mg, Al, Mn, Ni, Sc, P, Zr, Y, Co, and adjust according to the component content, and place the raw materials on the graphite Crucible, then put the g...

Embodiment 3

[0072] This embodiment provides a material for magnesium alloy doors and windows, which is composed of Mg, Al, Mn, Zn, Cu, Ni, Sc, P, Zr, Y, Ca, Sr, B, Co, and rare earth elements , its weight percentage components are: Al: 18%, Mn: 5%, Zn: 10%, Cu: 2%, Ni: 2%, Sc: 1%, P: 0.8%, Zr: 5%, Y: 2%, Ca: 10%, Sr: 2%, B: 6%, Co: 3%, rare earth elements 2%, and the rest is Mg;

[0073] Rare earth elements are composed of Ce, Nd, Gd, Pr, Dy, Yb, La, Sm, each component by weight percentage is: Ce: 14%, Nd: 17%, Gd: 14%, Pr: 12%, Dy : 9%, Yb: 5%, La: 19%, Sm: 10%.

[0074] The production method of the above-mentioned magnesium alloy door and window material is operated according to the following specific steps:

[0075] (1) Turn on the smelting furnace to preheat for 15 minutes, add the above-mentioned chemical components as raw materials to Mg, Al, Mn, Ni, Sc, P, Zr, Y, Co, and adjust according to the component content, and place the raw materials on the graphite Crucible, then put the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a material for magnesium alloy doors and windows. The material for the magnesium alloy doors and windows is composed of Mg, Al, Mn, Zn, Cu, Ni, Sc, P, Zr, Y, Ca, Sr, B, Co and a rare earth element, wherein the rare earth element is composed of Ce, Nd, Gd, Pr, Dy, Yb, La and Sm; the invention further discloses a production method of the material for the magnesium alloy doors and windows, and the method comprises the following steps: smelting, heat treatment, forging, quenching and tempering heat treatment, cooling, checking and storing, the production method is simple and easy, the manufacturing cost is low, and the produced material for the magnesium alloy doors and windows is excellent in corrosion resistance, can resist high temperature, is solderable, and has a prolonged service life.

Description

technical field [0001] The invention relates to a door and window material and a production method thereof, in particular to a magnesium alloy door and window material and a production method thereof. Background technique [0002] As people's living styles become more and more diverse, doors and windows are gradually occupying and expanding their market. At present, more door and window materials on the market are mainly aluminum alloy, color steel, and PVC materials, and aluminum alloy is because of its higher hardness, Light weight, no aging, beautiful and practical after color coating, so it is favored by the market, and the market demand is more and more strong, but the processing hardness of traditional aluminum alloy is too high, the plasticity is poor, the processing difficulty is relatively large, and the product price is obviously higher than similar products The ordinary plate products of aluminum alloy, thus affecting its popularization and use. [0003] Magnesiu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C30/06C22F1/00
Inventor 黄龙海黄瑶琼吴磊
Owner SUZHOU CITY WUZHONG DISTRICT XUKOU FENGSHOU MACHINERY PARTS FACTORY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap