Special defoaming agent for high-interface fluorocarbon resin emulsion and preparation method of special defoaming agent

A technology of fluorocarbon resin emulsion and defoamer, which is applied in the direction of foam dispersion/prevention, can solve the problems of low surface tension and easy foaming of fluorocarbon resin emulsion, achieve low surface tension, superior thermal stability, improve affinity Harmonious effect

Active Publication Date: 2015-08-12
安徽柏晨新材料科技有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a special defoamer for high-interface fluorocarbon resin emulsion and its preparation method, which has strong defoaming and anti-foaming effects, low surface tension, no volatility, and excellent thermal stability, especially in combination with fluorocarbon resin emulsion. Good compatibility, and can effectively solve the phenomenon that fluorocarbon resin emulsion is easy to foam during construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special defoaming agent for high-interface fluorocarbon resin emulsion and preparation method of special defoaming agent
  • Special defoaming agent for high-interface fluorocarbon resin emulsion and preparation method of special defoaming agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The first step: Take 42g of hydrogen-containing silicone oil, 157.5g of fluorine-containing polyether, and 66.5g of toluene into the reaction kettle, start stirring, slowly raise the temperature to 80-110°C, and slowly add isopropanol, which is a self-made catalyst, dropwise under a nitrogen atmosphere After the solution was dripped and reacted at a constant temperature for 2 hours, the toluene was distilled off under reduced pressure, the temperature was lowered and the material was discharged to obtain a fluorine-containing polyether modified polysiloxane.

[0025] The second step: Take 22.2g of fluorine-containing polyether modified polysiloxane obtained in the first step, 18g of white carbon black, 180g of silicone oil, 1.8g of thickener, and 1.485g of polyether, put them into the reaction kettle, start stirring, Slowly raise the temperature to 80-100°C, emulsify for 2 hours, then add 0.44g hydroxypropyl methylcellulose and 220g water, thicken for 0.5 hours, cool and...

Embodiment 2

[0027] Step 1: Take 60g of silicone oil, 190g of fluorine-containing polyether, and 80g of toluene into the reaction kettle, start stirring, and slowly raise the temperature to 80-110°C. After the reaction at constant temperature for 2.5 hours, the toluene was removed by distillation under reduced pressure, the temperature was lowered and the material was discharged to obtain fluorine-containing polyether modified polysiloxane.

[0028] The second step: Take 22g of fluorine-containing polyether modified polysiloxane obtained in the first step, 28g of white carbon black, 220g of silicone oil, 2.0g of thickener, and 1.665g of polyoxyethylene ether, add them to the reaction kettle, and start stirring , slowly raise the temperature to 80-100°C, emulsify for 3 hours, then add 0.60g hydroxypropyl methylcellulose and 300g water, thicken for 1 hour, cool and discharge to obtain a special defoamer for high-interface fluorocarbon resin emulsion 2.

Embodiment 3

[0030] Step 1: Take 110g of hydrogen-containing silicone oil, 157.5g of fluorine-containing polyether, and 57g of toluene into the reaction kettle, start stirring, slowly raise the temperature to 80-110°C, and slowly add the isopropanol solution of self-made catalyst dropwise under nitrogen atmosphere After dripping, the constant temperature reaction was carried out for 3 hours, the toluene was distilled off under reduced pressure, the temperature was lowered and the material was discharged to obtain fluorine-containing polyether modified polysiloxane.

[0031] Step 2: Take 22g of fluorine-containing polyether modified polysiloxane obtained in the first step, 30g of white carbon black, 240g of silicone oil, 1.8g of thickener, and 1.485g of polyoxyethylene ether, add them to the reaction kettle, and start stirring , slowly raise the temperature to 80-100°C, emulsify it for 2 hours, then add 0.11g hydroxypropyl methylcellulose and 320g water, thicken for 1 hour, cool and discharg...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a special defoaming agent for a high-interface fluorocarbon resin emulsion. The special defoaming agent is characterized in that the special defoaming agent comprises the following components in percentage by mass: 3-10% of fluorine-containing polyether modified polysiloxane, 2-7% of white carbon black, 40-60% of methylsilicone oil, 0.27-0.45% of a thickener, 0.22-0.33% of polyoxyethylene ether, 0.016-0.21% of cellulose and 30-45% of water. The special defoaming agent disclosed by the invention has the advantages of strong defoaming and foam-inhibiting efficacy, low surface tension, no volatility, excellent thermal stability and good compatibility with the fluorocarbon resin emulsion, and can effectively solve the problem that the fluorocarbon resin emulsion is liable to foaming in construction process.

Description

technical field [0001] The invention relates to the technical field of auxiliary agent synthesis, in particular to a special defoamer for high-interface fluorocarbon resin emulsion and a preparation method thereof. Background technique [0002] Fluorocarbon resin emulsion is a water-based polymer material with high interface function. Because of its extremely low surface tension and hydrophobic effect, it has been widely used in textile, leather, construction and other fields. In recent years, domestic enterprises and colleges and universities have made significant progress in the research and development of fluorocarbon emulsions with high interface functions, and achieved important breakthroughs in the field of practice. However, the development of the supporting additives is still in the process of debugging, which brings great difficulties to the industrialization and engineering of fluorocarbon resin emulsion. The special defoamer for fluorocarbon resin emulsion is one ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01D19/04
Inventor 陈奠宇邓昭逸程威范新传
Owner 安徽柏晨新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap