Elastic fluorocarbon paint and formula thereof

A fluorocarbon paint and elastic technology, applied in anti-corrosion coatings, coatings and other directions, can solve problems such as inability to use on-site and restrict the promotion of fluorocarbon coatings, achieve strong stain resistance and weather resistance, meet the aesthetics and service life, The effect of solving the cracking problem

Inactive Publication Date: 2015-08-12
上海奥泽涂料有限公司
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since this type of coating is still a baking type coating, although the baking temperature is much lower than that of PTFE, about 230°C, it cannot be used on site and requires factory processing, which also restricts the further promotion of fluorocarbon coatings.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The formula of the elastic fluorocarbon paint according to the embodiment of the present invention, the formula used and the percentage weight thereof are:

[0029] Fluorocarbon resin 40%-50%

[0030] Elastic resin 15%-20%

[0031] Wetting agent 0.3%-0.5%

[0032] Dispersant 0.3%-0.5%

[0033] Leveling agent 0.5%-1%

[0034] Aluminum powder 15%-20%

[0035] Defoamer 0.1%-0.2%

[0036] Anti-settling agent 0.1%-0.5%

[0037] Drier 0%-0.5%

[0038] Solvent 15%-20%

[0039] For the elastic fluorocarbon paint and its formula described in the above embodiments of the present invention, the construction steps are:

[0040] 1. Insulation base inspection: there should be no hollow drums, cracks, oil stains, water-proof and anti-cracking treatments should be done on the edge of the window sill and the parapet surface, whether the grid cloth paving and reinforcing grid cloth are correct, and the verticality and flatness of the yin and yang angles are required See Table 1 below. If the above requi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
Login to view more

Abstract

The invention relates to a formula of elastic fluorocarbon paint. The formula comprises the following ingredients: 40-50% of fluorocarbon resin, 15-20% of elastic resin, 0.3-0.5% of a wetting agent, 0.3-0.5% of a dispersant, 0.5-1% of a leveling agent, 15-20% of aluminium powder, 0.1-0.2% of an antifoaming agent, 0.1-0.5% of an anti-settling agent, 0-0.5% of a drier and 15-20% of a solvent. Long straight chain and low branched chain of a high-molecular elastic cross-linking agent react with a fluorine-containing polymer to form a highly-straight-chain and low-branched-chain polymer, the structure of which is jagged. The ultimate embodiment of properties is reflected in appropriate surface strength, excellent elasticity, telescopic springback function, high tensile strength and fracture resistance, low surface polarity and strong resistance to soiling and weatherability.

Description

Technical field [0001] The invention relates to the technical field of coatings, in particular to a water-based elastic fluorocarbon paint and its formulation which can be widely used in the fields of protection, decoration, and decoration of internal and external walls, concrete surfaces, inorganic and organic materials surfaces, and the like. Background technique [0002] The earliest "fluorocarbon coating" was actually born as early as 1938. It is the well-known Teflon coating of DuPont, that is, copolymers such as polytetrafluoroethylene (PTFE) and polyperfluoropropylene (FEP). This kind of material has unique and excellent heat resistance (180℃-260℃), low temperature resistance (-200℃), self-lubricity and chemical stability, etc., and is called "corrosion-resistant, never-stick Teflon" , Fluorocarbon paint is generally divided into three fluorine and tetrafluoride, tetrafluoride has higher anticorrosion performance. Due to the extremely high liquefaction temperature require...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D127/12C09D7/12C09D5/08
CPCC09D127/12C09D5/08C09D7/61C09D7/65C08L101/00C08K2003/0812
Inventor 杨和柏王波张锡芬李亚东吴海霞
Owner 上海奥泽涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap