PET/PTT material reinforced by glass fiber and resisting bacterial with nanometer bamboo charcoal

A nano-bamboo carbon, PTT20% technology, applied in the field of PET/PTT materials, can solve the problems of poor high heat resistance, rough product surface, unstable mechanical properties, etc., achieve excellent tensile strength, and improve the effect of application fields

Inactive Publication Date: 2015-08-19
QINGDAO JIAYIYANG IND & TRADE
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the unstable mechanical properties of PET / PTT, poor high heat resistance, rough product surface, etc., will greatly limit its application effect and application field

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A glass fiber reinforced and nano-bamboo carbon antibacterial PET / PTT material, its components are proportioned by mass percentage: PET 33%, PTT 30%, E-MA-GMA 4%, glass fiber 12%, EVA 9% , nano-modified bamboo carbon 8%, light stabilizer 1.5%, nucleating agent 1%, TAF 1%, antioxidant 1010 0.3%, antioxidant 168 0.2%, the PET has a characteristic viscosity of 0.8-1.2dL / g polyethylene terephthalate, the PTT is polytrimethylene terephthalate with an intrinsic viscosity of 0.7-1.2dL / g, the glass fiber is surface modified by a silane coupling agent, and Alkali-free chopped glass fibers with an average diameter of 8-15 μm, the nano-modified bamboo carbon is nano-bamboo carbon with a surface modified by nano-titanium dioxide and a particle size of 20-80 nm, and the light stabilizer is a mass ratio 1:1 compound of hindered amine high molecular weight light stabilizer GW-944Z and GW-622, the nucleating agent is nano-silica, sodium benzoate and polyethylene glycol with a mass rat...

Embodiment 2

[0024] A glass fiber reinforced and nano-bamboo carbon antibacterial PET / PTT material, its components are proportioned by mass percentage: PET 57%, PTT 20%, E-MA-GMA 3%, glass fiber 8%, ACR 6% , nano-modified bamboo carbon 4%, light stabilizer 0.5%, nucleating agent 0.5%, TAF 0.8%, antioxidant 1010 0.1%, antioxidant 168 0.1%, the PET has a characteristic viscosity of 0.8-1.2dL / g polyethylene terephthalate, the PTT is polytrimethylene terephthalate with an intrinsic viscosity of 0.7-1.2dL / g, the glass fiber is surface modified by a silane coupling agent, and Alkali-free chopped glass fibers with an average diameter of 8-15 μm, the nano-modified bamboo carbon is nano-bamboo carbon with a surface modified by nano-titanium dioxide and a particle size of 20-80 nm, and the light stabilizer is a mass ratio 1:1 compound of hindered amine high molecular weight light stabilizer GW-944Z and GW-622, the nucleating agent is nano-silica, sodium benzoate and polyethylene glycol with a mass ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Intrinsic viscosityaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
The average diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a PET / PTT material reinforced by glass fiber and resisting bacterial with nanometer bamboo charcoal. The material comprises the following components by weight: 33% to 57% of PET, 20% to 30% of PTT, 2% to 4% of a compatibilizing agent, 8% to 12% of glass fiber, 6% to 9% of a toughening agent, 4% to 8% of nanometer modified bamboo charcoal, 0.5% to 2% of a light stabilizer, 0.5% to 1% of a nucleating agent, 0.5% to 1% of an anti-glassfiber-exposure agent, 0.1% to 0.5% of an antioxidant 1010 and 0.1% to 0.5% of an antioxidant 168. The invention has the following beneficial effects: the PET / PTT material reinforced by the glass fiber and resisting the bacterial with the nanometer bamboo charcoal integrates respective advantages of PET and PTT and has exellent application effects of tensile strength, impact-resistant strength, bending strength, heat resistance and aging resistance; meanwhile, by using the nanometer bamboo charcoal as an antibacterial functional filler, the material also has good functions of antibacteria, ultraviolet prevention, deodorization, odor absorption and antistatic property, so the application fields of the PET / PTT are greatly improved.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a PET / PTT material reinforced with glass fiber and nano-bamboo carbon antibacterial. Background technique [0002] Polyethylene terephthalate (PET) / polytrimethylene terephthalate (PTT) is a new type of polymer plastic alloy material, which has excellent molding processing, impact resistance, and chemical resistance. Therefore, it will have broad application prospects in the fields of automobiles, electronic appliances, home appliances, and fibers. However, PET / PTT has unstable mechanical properties, poor high heat resistance, rough product surface, etc., which will greatly limit its application effect and application field. In order to improve the performance of PET / PTT, it is often necessary to add a third component to PET / PTT to obtain a practical alloy system. Contents of the invention [0003] The object of the present invention is to provide a PET / PTT material ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L67/02C08L23/08C08L33/04C08L51/00C08L51/04C08K13/06C08K9/06C08K9/02C08K7/14C08K3/04C08K5/20C08K3/36C08K5/098B29C47/92B29C48/92
Inventor 不公告发明人
Owner QINGDAO JIAYIYANG IND & TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com