PTT color master batch and preparation method therefor

A color masterbatch and dye technology, applied in the field of PTT masterbatch and its preparation, can solve the problems of large consumption, long PTT color masterbatch process, pollution, etc., achieve low cost, reduce coloring process, and avoid environmental pollution pollution effect

Inactive Publication Date: 2015-08-26
QINGDAO XINZHAN PLASTIC
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The solvent method requires the pigment to be ground in a carrier resin and an organic solvent. Although the solvent can be recycled after use, the consump

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A kind of PTT color masterbatch, its component ratio by mass percentage is: PTT resin 60%, yellow GG dye 35%, polyethylene glycol 4.5%, antioxidant 0.5%, described PTT resin has intrinsic viscosity 0.7~ Polytrimethylene terephthalate with a melting point of 1.5dL / g, a melting point of 245°C to 258°C, and a relative density of 1.30 to 1.35g / cm3, and the antioxidant is hindered phenol antioxidant 1010 and phosphorous acid at a mass ratio of 1:1 A compound of ester antioxidant 168.

[0014] Preparation method: mix the components according to the weight ratio, then add them into a high-speed mixer with a rotation speed of 500-1500 rpm, mix at a mixing temperature of 140°C-180°C for 10-20 minutes, and then add the mixed materials into the double Melting and blending in a screw extruder, the melting temperature is controlled at 180 ° C ~ 260 ° C, the screw speed is 100 ~ 300 rpm, through the shearing and mixing of the twin screw extruder for 10 ~ 15 minutes, and then granulat...

Embodiment 2

[0016] A kind of PTT color masterbatch, its component ratio by mass percentage is: PTT resin 50%, blue 2RA dye 45%, calcium stearate 4%, antioxidant 1%, described PTT resin has intrinsic viscosity 0.7~ Polytrimethylene terephthalate with a melting point of 1.5dL / g, a melting point of 245°C to 258°C, and a relative density of 1.30 to 1.35g / cm3. The antioxidant is hindered phenol antioxidant 1076 and phosphorous acid at a mass ratio of 1:1 A compound of ester antioxidant 168.

[0017] Preparation method: mix the components according to the weight ratio, then add them into a high-speed mixer with a rotation speed of 500-1500 rpm, mix at a mixing temperature of 140°C-180°C for 10-20 minutes, and then add the mixed materials into the double Melting and blending in a screw extruder, the melting temperature is controlled at 180 ° C ~ 260 ° C, the screw speed is 100 ~ 300 rpm, shearing and mixing by the twin screw extruder for 10 ~ 15 minutes, and then granulation, After drying, a ki...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Intrinsic viscosityaaaaaaaaaa
Melting pointaaaaaaaaaa
Relative densityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a PTT color master batch and preparation method therefor. The PTT color master batch comprises the following ingredients, by weight, 50%-80% of PTT resins, 20%-50% of soluble dye, 3%-5% of dispersants and 0.1%-1% of anti-oxidants. The soluble dye is a high-grade oil soluble dye. The high-grade oil soluble dye is an anthraquinone dye or a heterocycle dye after chemical purification, and comprises one selected from a yellow GG dye, a red G dye, a red EG dye, a red BB dye, a blue 2RA dye, a purple BA dye, a green G dye and a brown R dye. The beneficial effects are that the PTT color master batch has characteristics of high concentration, bright color, strong coloring power, good stability, convenient usage, low cost and the like, the coloring technologies of PTT are reduced, and environment pollution is avoided.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a PTT color masterbatch and a preparation method thereof. Background technique [0002] Polytrimethylene terephthalate (PTT) is an aromatic polyester synthesized by esterification and polycondensation (and solid-state polycondensation) of terephthalic acid (PTA) and 1,3-propanediol (PDO). Since industrialized production in the 1990s, it has been widely used in various fields of people's daily activities. PTT can be made into fibers, films, engineering plastics, etc. In particular, because PTT fiber not only has the chemical resistance and stain resistance of PET fiber, but also has the softness of nylon and the bulkiness of acrylic fiber, its elastic recovery and recovery rate are not only excellent, but its inherent bending performance and color The fastness is also very good. It is one of the newly developed popular polymer materials in the world. It is widely used ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/02C08K5/00C08K5/134C08K5/526C08J3/22
Inventor 不公告发明人
Owner QINGDAO XINZHAN PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap