Method for preparing ultralight ceramsites from clay iron-containing tailings

A technology of ultra-light ceramics and tailings, applied in applications, ceramic products, household appliances, etc., can solve the requirements of raw material formulations are very strict, the total solid waste ultra-light ceramsite is less, and the total solid waste ultra-light ceramsite has not been found yet, etc. problems, to achieve significant economic benefits, high cost performance, and strong market competitiveness.

Active Publication Date: 2015-09-02
SINOSTEEL MAANSHAN INST OF MINING RES
View PDF6 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ultra-light ceramsite has very strict requirements on the raw material formula, so it is generally only partially replaced by solid waste for clay or shale, or solid waste is added to non-solid waste mater

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing ultralight ceramsites from clay iron-containing tailings
  • Method for preparing ultralight ceramsites from clay iron-containing tailings
  • Method for preparing ultralight ceramsites from clay iron-containing tailings

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] In order to further describe the present invention, a method for preparing ultra-light ceramsite by using clay iron-containing tailings of the present invention will be described in detail below in conjunction with the accompanying drawings and examples.

[0037] Table 1 is a chemical composition list of raw materials used in a method of preparing ultra-light ceramsite by utilizing clay iron-containing tailings in the present invention.

[0038] Table 1 Chemical composition of raw materials used (%)

[0039]

[0040] Depend on figure 1 A technical roadmap for the method of preparing ultra-light ceramsite by utilizing clay iron-containing tailings in the present invention and combining figure 2 It can be seen that a kind of technique and parameters adopted in the method of utilizing clay iron-containing tailings to prepare ultra-light ceramsite in the present invention are:

[0041] (1) Raw material selection

[0042] When firing ultra-light ceramsite, the che...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing ultralight ceramsites from clay iron-containing tailings. The ultralight ceramsites are prepared from the following raw materials in percentage by weight according to dry basis weight: 40-48 percent of clay iron-containing tailings, 40-48 percent of coal series kaolinite or coal gangue and 8-15 percent of dewatered sludge; the method comprises the following preparation processes: mixing materials, pelletizing, drying, preheating, calcining and cooling; under an optimum formula and process conditions that the preheating temperature is 500-600 DEG C, calcination temperature is 1250-1350 DEG C, and the heating rate is 10-15 DEG C/min, the all-solid waste ultralight ceramsites with the bulk density of 390 kg/m<3>, cylinder compressive strength of 1.2 MPa and the water absorption of 3.8% can be prepared through firing, and meet requirements of GB/T17431.1-2010, a novel approach is developed for abundant utilization of tailings, coal gangue and dewatered sludge and obvious economic benefits, environmental benefits and social benefits are realized.

Description

technical field [0001] The invention belongs to the field of comprehensive utilization of solid waste, and in particular relates to a method for preparing lightweight ceramsite by using solid waste such as clay iron-containing tailings. The prepared ultra-light ceramsite can be used for thermal insulation concrete and its products, and It is used in horticulture, food and beverage, chemical industry, petroleum and other fields. Background technique [0002] Tailings, coal gangue, and dewatered sludge are solid wastes, and their large stockpiles will bring economic, environmental, and safety problems, such as occupying a large area of ​​land, polluting the environment, and causing potential safety hazards. How to utilize solid waste such as tailings, coal gangue and dewatered sludge in large quantities to achieve the purpose of reduction, harmlessness and resource utilization has become a research hotspot and difficulty at home and abroad. [0003] Traditional ceramsite raw ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B38/00
Inventor 罗书亮那琼潘旭方孙磊陈宏贵郭庆王帆朱桐徐庆荣
Owner SINOSTEEL MAANSHAN INST OF MINING RES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap