Preparation method of chitosan membrane

A technology of chitosan film and chitosan, applied in the field of preparation of chitosan film, can solve the problem of low mechanical strength of chitosan film

Inactive Publication Date: 2015-09-23
QINGDAO UNIV OF SCI & TECH
View PDF6 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Because there are a large amount of hydrogen bonds in and between chitosan molecules, resulting in the compact structure and strong rigidity of chitosan itself, at present, the existing patented film-forming technology (such as, CN03118535. 2) The mechanical strength of gained chitosan film is all very low, therefore, how to improve film-making process technology is the key problem of preparing high-performance chitosan film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of chitosan membrane

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Prepare 1.5% 1-carboxymethyl-3-methylimidazolium chloride salt ionic liquid aqueous solution 50g, 0.75g chitosan is completely dissolved in the above-mentioned solvent, make the chitosan film-making stoste that concentration is 1.5%, through Squeeze and filter, stand for defoaming, spin coating on glass plate, dry at 50% constant temperature at 40°C and constant humidity, soak in 2.0% sodium hydroxide solution for 2.5h to remove the film, wash with distilled water until neutral, and keep at constant temperature at 40°C and constant humidity 50% drying and other operations to obtain a transparent chitosan film, the thickness of which is 3.35 μm, the breaking strength is 171 MPa, the breaking elongation is 3.97%, and the initial modulus is 3.39 GPa.

Embodiment 2

[0019] Prepare 2.0% 1-carboxymethyl-3-methylimidazolium chloride salt ionic liquid aqueous solution 50g, 1.25g chitosan is completely dissolved in the above-mentioned solvent, make the chitosan membrane stock solution that concentration is 2.5%, through Squeeze and filter, stand for defoaming, spin coating on glass plate, dry at 50% constant temperature at 40°C and constant humidity, soak in 1.5% sodium hydroxide solution for 3.5h to remove the film, wash with distilled water until neutral, and keep at constant temperature at 40°C and constant humidity 50% drying, etc., to obtain a transparent chitosan film with a thickness of 3.22 μm, a breaking strength of 177 MPa, a breaking elongation of 4.01%, and an initial modulus of 3.47 GPa.

Embodiment 3

[0021] Prepare 3.0% 1-carboxymethyl-3-methylimidazolium chloride salt ionic liquid aqueous solution 50g, 1.0g chitosan is completely dissolved in the above-mentioned solvent, make the chitosan membrane stock solution that concentration is 2.0%, through Squeeze and filter, stand for defoaming, spin coating on glass plate, dry at 50% constant temperature and humidity at 40°C, soak in 2.0% sodium hydroxide solution for 3.0h to remove the film, wash with distilled water until neutral, and keep at constant temperature and humidity at 40°C 50% drying and other operations to obtain a transparent chitosan film with a thickness of 3.14 μm, a breaking strength of 180 MPa, a breaking elongation of 3.92%, and an initial modulus of 3.54 GPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
breaking strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a chitosan membrane. The method comprises the following steps of: dissolving chitosan in 1-carboxymethyl-3-methyl chlorine salt ion liquid water solution of 1-5%, and enabling the chitosan to completely dissolve so as to obtain a stock solution of 1-5 wt% for preparing the chitosan membrane; performing squeezing and filtering; performing standing and defoaming; performing rotary membrane coating on a glass plate; performing drying under constant temperature of 40 DEG C and constant humidity of 50%; performing soaking in a sodium hydroxide solution of 1-5% for 1-5h and stripping a membrane; cleaning the membrane in distilled water till the pH is neutral; and drying the cleaned membrane under the constant temperature of 40 DEG C and constant humidity of 50% so as to obtain the chitosan membrane. According to the chitosan membrane, the thickness is 2.5-3.5 mu m, the breaking strength is larger than or equal to 170MPa, the elongation at break is larger than 3.6%, and the initial modulus is larger than 3.3 GPa. The chitosan membrane can be used as anticoagulant materials, bone repairing materials, wound dressing materials, and the like.

Description

technical field [0001] The invention belongs to the technical field of preparation of membrane materials, and in particular relates to a method for preparing chitosan membranes. The method overcomes the disadvantages of easy volatilization of solvents, serious pollution, and large amount of three wastes in the preparation process of chitosan membranes. Specifically, It is said to use high molecular weight chitosan as raw material and the aqueous solution of 1-carboxymethyl-3-methylimidazolium chloride salt ionic liquid as solvent to prepare a suitable concentration of film-making liquid; After soaking to remove the film, constant temperature and humidity drying and other processes, the chitosan film is finally obtained. Background technique [0002] Chitosan is a natural polymer biomass resource, which widely exists in marine organisms such as shrimps, crabs and other arthropods, molluscs and fungal cells, and is known as animal cellulose. Chitosan film is made of chitosan ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08J5/18C08L5/08
Inventor 于世涛李露刘仕伟刘福胜解从霞赵丽丽
Owner QINGDAO UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap