Waterproof adhesive for pipeline joint and preparation method of waterproof adhesive

A technology for pipe joints and adhesives, applied in the directions of polymer adhesive additives, non-polymer adhesive additives, adhesives, etc., can solve the problems of poor substrate protection, achieve good acid and alkali corrosion resistance, improve Surface active, strong adhesive effect

Inactive Publication Date: 2015-09-23
CHUZHOU GUANGWEI CHEM
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional vegetable adhesives are easily hydrolyzed at high temperatures and have poor protection for the substrate, while ethylene-ethyl acrylate copolymer has strong thickening ability and good temperature resistance;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of waterproof adhesive for pipe joint, it is made up of following raw materials of weight part:

[0021] Polyvinylidene fluoride 50, sisal fiber 15, sp-80 3.5, 12mol / l nitric acid solution 0.4, ethylene-ethyl acrylate copolymer 210, zirconium oxychloride 1.3, lactic acid 0.5, glycerol 0.6, tetraisocyanate 3. Lanolin 10, tetraethyl orthosilicate 20, polyether glycol 0.8, 30-35% ammonia water 3, tert-butyl hydrodiphenol 3.

[0022] A preparation method for a waterproof adhesive for a pipe joint, comprising the following steps:

[0023] (1) Add ethyl orthosilicate to 1.2 times the weight of absolute ethanol, add the above 35% ammonia water, add 20% of the above sp-80 weight under stirring conditions, add tetraisocyanate, and keep stirring at 76°C 40 minutes to get silicon emulsion;

[0024] (2) Take 16% of the weight of the above ethylene-ethyl acrylate copolymer, mix it with polyvinylidene fluoride, add polyether diol and tert-butyl hydroquinone under stirring co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a waterproof adhesive for a pipeline joint. The waterproof adhesive has the advantages that lactic acid / glycerin organic zirconium is used as a cross-linking agent, so that remarkable thermosensitive cross-linking characteristics are achieved; an ethylene-ethyl acrylate copolymer fiber base solution is used as a thickener, through the cross-linking action, gel with favorable temperature resistance and shear resistance can be formed; the copolymer base solution treated with fibers can improve the surface activity of a copolymer, enhance the cross-linking effect, and improve the viscoelasticity and the thixotropy.

Description

technical field [0001] The invention relates to an adhesive, in particular to a waterproof adhesive for pipe joints and a preparation method thereof. Background technique [0002] Traditional vegetable adhesives are easily hydrolyzed at high temperatures and have poor protection for the substrate, while ethylene-ethyl acrylate copolymer has strong thickening ability and good temperature resistance; [0003] Usually, the most commonly used crosslinking agent for obtaining polymer gels is organoboron or organozirconium, and organoboron crosslinking agents can only withstand temperatures up to 150°C. Organic zirconium can be crosslinked under acidic conditions and has high temperature resistance. Up to 200 ° C, has broad application prospects. Contents of the invention [0004] The object of the present invention is to provide a waterproof adhesive for pipe joints and a preparation method thereof. [0005] The present invention is achieved through the following technical so...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J123/08C09J127/16C09J11/04C09J11/06C09J11/08
Inventor 李勇
Owner CHUZHOU GUANGWEI CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com