Low-smoke zero-halogen flame-retardant silicone rubber for LED-lamp-used cables

A technology of LED lamps and silicone rubber, which is applied in the field of low-smoke, halogen-free, flame-retardant silicone rubber for LED lamp cables. It can solve the problems of limited application and low mechanical properties, and achieve good mechanical properties and excellent flame-retardant properties.

Inactive Publication Date: 2015-09-30
ANHUI LVLONG PHOTOELECTRIC TECH
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the usual halogen-free flame-retardant silicone rubber meets the requirements of low smoke and environmental protection, it needs to add a large amount of halogen-free flame retardants to meet higher flame-retardant requirements, which will inevitably lead to low mechanical properties, including tensile strength and tear resistance. Crack strength, etc., which limits its application in wire and cable, and the same is true in the LED light source industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A low-smoke, halogen-free, flame-retardant silicone rubber for LED lamp cables, made of the following raw materials in parts by mass: 100 parts of methyl vinyl silicone rubber, 5 parts of nano-cerium dioxide, 3 parts of melamine polyphosphate, and pentaerythritol 3 parts, 2 parts of ammonium polyphosphate, 5 parts of vanadium trichloride, 2 parts of triethylaluminum, 3 parts of diphenylsilanediol, 1 part of carbon fiber, 5 parts of calcium stearate, 2 parts of clay, anti-aging agent VK-B045 parts, salicylic acid 3 parts.

[0015] Wherein, the particle size of nano cerium oxide is 10-30nm.

[0016] First add methyl vinyl silicone rubber to the kneader, then add clay and diphenylsilanediol, knead at 170-190°C for 1 hour under nitrogen, then cool the kneader to 60°C, add nanometer diol Cerium oxide, melamine polyphosphate, pentaerythritol, ammonium polyphosphate, vanadium oxychloride and triethylaluminum, continue to mix for 0.5h and then discharge, cool to room temperatu...

Embodiment 2

[0018] A low-smoke, halogen-free, flame-retardant silicone rubber for LED lamp cables, made of the following raw materials in parts by mass: 110 parts of methyl vinyl silicone rubber, 8 parts of nano-cerium dioxide, 4 parts of melamine polyphosphate, and pentaerythritol 4 parts, 3 parts of ammonium polyphosphate, 6 parts of vanadium trichloride, 3 parts of triethylaluminum, 5 parts of diphenylsilanediol, 2 parts of carbon fiber, 8 parts of calcium stearate, 4 parts of clay, anti-aging agent VK-B047 parts, 5 parts of salicylic acid.

[0019] Wherein, the particle size of nano cerium oxide is 10-30nm.

[0020] First add methyl vinyl silicone rubber to the kneader, then add clay and diphenylsilanediol, knead at 170-190°C for 1 hour under nitrogen, then cool the kneader to 60°C, add nanometer diol Cerium oxide, melamine polyphosphate, pentaerythritol, ammonium polyphosphate, vanadium oxychloride and triethylaluminum, continue to mix for 0.5h and then discharge, cool to room tempe...

Embodiment 3

[0022] A low-smoke, halogen-free, flame-retardant silicone rubber for LED lamp cables, made of the following raw materials in parts by mass: 120 parts of methyl vinyl silicone rubber, 10 parts of nano-cerium dioxide, 5 parts of melamine polyphosphate, and pentaerythritol 5 parts, 4 parts of ammonium polyphosphate, 8 parts of vanadium trichloride, 5 parts of triethylaluminum, 6 parts of diphenylsilanediol, 3 parts of carbon fiber, 10 parts of calcium stearate, 5 parts of clay, anti-aging agent VK-B048 parts, salicylic acid 8 parts.

[0023] Wherein, the particle size of nano cerium oxide is 10-30nm.

[0024] First add methyl vinyl silicone rubber to the kneader, then add clay and diphenylsilanediol, knead at 170-190°C for 1 hour under nitrogen, then cool the kneader to 60°C, add nanometer diol Cerium oxide, melamine polyphosphate, pentaerythritol, ammonium polyphosphate, vanadium oxychloride and triethylaluminum, continue to mix for 0.5h and then discharge, cool to room temper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-smoke zero-halogen fame-retardant silicone rubber for LED-lamp-used cables and relates to the technical field of LED lamp production. The low-smoke zero-halogen fame-retardant silicone rubber is prepared from the following raw materials in parts by mass: 100-120 parts of methyl vinyl silicone rubber, 5-10 parts of nano cerium oxide, 3-5 parts of melamine pyrophosphate, 3-5 parts of pentaerythrotol, 2-4 parts of ammonium polyphosphate, 5-8 parts of vanadium, 2-5 parts of aluminum triethyl, 3 to 6 parts of diphenyl silandiol, 1-3 parts of carbon fibers, 5-10 parts of calcium stearate, 2-5 parts of potter's clay, 5-8 parts of an anti-ager VK-B04 and 3-8 parts of salicylic acid. The low-smoke zero-halogen fame-retardant silicone rubber does not contain halogen, generates extremely low-concentration smoke and toxicity during combustion, and therefore causes no harm to humans; besides, owing to the synergistic effect of all the components, excellent flame resistance and favorable mechanical strength are achieved.

Description

Technical field: [0001] The invention relates to the technical field of LED lamp production, in particular to a low-smoke, halogen-free, flame-retardant silicone rubber for LED lamp cables. Background technique: [0002] With the rapid development of the global economy and the enhancement of human awareness of environmental protection, the quality and performance requirements of wire and cable in various fields are also getting higher and higher. There are more and more fires caused by the aging of wires and cables. How to reduce the incidence of fire and the death rate in the event of fire, low smoke, halogen-free, flame retardant, and environmental protection have also become the development direction of the wire and cable industry. [0003] Silicone rubber is flexible, resistant to ozone, corona, flame, good insulation, high and low temperature resistance, and is a safe and reliable material for the production of wires and cables. Although the usual halogen-free flame-re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/07C08K13/02C08K3/22C08K5/3492C08K5/053C08K3/32C08K5/098C08K3/34C08K7/06
Inventor 陈福宝
Owner ANHUI LVLONG PHOTOELECTRIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More