Micaceous iron antirust paint for medical use and preparation method therefor

A technology of anti-rust paint and cloud iron, which is applied in the field of medical materials, can solve the problems of poor anti-corrosion performance and slow drying, and achieve the effect of good anti-corrosion performance, simple raw materials and simple preparation methods

Inactive Publication Date: 2015-10-07
SUZHOU JONATHAN NEW MATERIALS TECH
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The invention provides a medical mica iron antirust paint with fast drying and good anticorrosion performance and a preparation method thereof, which solves technical problems such as slow drying and poor anticorrosion performance of existing medical materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Step 1: Weigh 100 parts of mica iron oxide, 65 parts of phenolic resin coating, 25 parts of calcium carbonate, 20 parts of talcum powder, 15 parts of zinc phosphate, 30 parts of barium sulfate, 2 parts of tung oil, and zinc oxide according to the ratio of parts by mass. 5 parts, catalpa oil 10 parts, cobalt naphthenate 1 part.

[0021] Step 2: Put micaceous iron oxide, phenolic resin coating, calcium carbonate, talcum powder and barium sulfate into the reaction kettle, heat to 160°C, and stir at 300r / min for 30min.

[0022] Step 3: Let the stirred liquid stand for 100 minutes, add zinc phosphate, tung oil, zinc oxide, catalpa oil and cobalt naphthenate, mix well at 200°C, put it into a grinder for 12 hours, filter and pack.

[0023] Used for anti-rust and anti-corrosion of medical appliances, the appearance of the coating film is orange-red, the solid content is 82%, the viscosity is 85s; the anti-corrosion performance is good, the impact resistance is 55cm, and the sal...

Embodiment 2

[0025] Step 1: Weigh 100 parts of mica iron oxide, 85 parts of phenolic resin coating, 45 parts of calcium carbonate, 40 parts of talcum powder, 35 parts of zinc phosphate, 50 parts of barium sulfate, 8 parts of tung oil, and zinc oxide according to the ratio of parts by mass. 25 parts, catalpa oil 30 parts, cobalt naphthenate 20 parts.

[0026] Step 2: Put micaceous iron oxide, phenolic resin paint, calcium carbonate, talcum powder and barium sulfate into the reaction kettle, heat to 180°C, and stir at 500r / min for 50min.

[0027] Step 3: Let the stirred liquid stand for 140 minutes, add zinc phosphate, tung oil, zinc oxide, catalpa oil and cobalt naphthenate, mix well at 240°C, put it into a grinder for 18 hours, filter and pack.

[0028] Used for anti-rust and anti-corrosion of medical appliances, the appearance of the coating film is orange-red, the solid content is 83%, the viscosity is 95s; the anti-corrosion performance is good, the impact resistance is 60cm, and the sa...

Embodiment 3

[0030] Step 1: Weigh 100 parts of mica iron oxide, 70 parts of phenolic resin coating, 30 parts of calcium carbonate, 25 parts of talcum powder, 20 parts of zinc phosphate, 35 parts of barium sulfate, 4 parts of tung oil, and zinc oxide according to the ratio of parts by mass. 10 parts, catalpa oil 15 parts, cobalt naphthenate 5 parts.

[0031] Step 2: Put micaceous iron oxide, phenolic resin coating, calcium carbonate, talcum powder and barium sulfate into the reaction kettle, heat to 160°C, and stir at 300r / min for 30min.

[0032] Step 3: Let the stirred liquid stand for 100 minutes, add zinc phosphate, tung oil, zinc oxide, catalpa oil and cobalt naphthenate, mix well at 200°C, put it into a grinder for 12 hours, filter and pack.

[0033] Used for anti-rust and anti-corrosion of medical appliances, the appearance of the coating film is orange-red, the solid content is 82-88%, the viscosity is 105s; the anti-corrosion performance is good, the impact resistance is 65cm, and t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses micaceous iron antirust paint for medical use and a preparation method therefor. The micaceous iron antirust paint is prepared from micaceous iron oxide, phenolic resin coating, calcium carbonate, talcum powder, zinc phosphate, barium sulfate, tung oil, zinc oxide, stillingia oil and cobalt naphthenate. The micaceous iron antirust paint is applied to the rust protection and anticorrosion of medical instruments, the appearance of a coating film is reddish-orange, and the micaceous iron antirust paint has the solid content of 82-88 percent and the viscosity of 85-125s; the corrosion resistance is good, the impact strength is 55-75cm, and the resistance to salt water meets the condition that the micaceous iron antirust paint does not bubble and does not fall off in 15-35 days; the time for surface drying is 2-6 hours, and the time for solid drying is 20-22 hours; the preparation method is simple, the raw materials are simply and easily obtained, and the micaceous iron antirust paint can be extensively produced and continuously replace the existing materials.

Description

technical field [0001] The invention relates to the technical field of medical materials, in particular to a medical antirust paint for mica iron and a preparation method thereof. Background technique [0002] Antirust paint is a coating that protects metal surfaces from chemical or electrochemical corrosion from the atmosphere, sea water, etc. Mainly divided into two categories of physical and chemical antirust paint. The former relies on the proper combination of pigments and paints to form a dense paint film to prevent the intrusion of corrosive substances, such as iron red, aluminum powder, graphite antirust paint, etc.; the latter relies on the chemical antirust effect of antirust pigments, such as mica Iron oxide, zinc yellow antirust paint, etc. Used for rust prevention of bridges, ships, pipelines and other metals. Mica iron oxide antirust paint is a kind of paint mixed with mica iron oxide and drying oil. It has good permeability and wettability, soft paint fil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D161/06C09D5/08C09D7/12
CPCC09D161/06C08L2205/025C08L2205/03C09D5/08C09D7/40C08L91/00C08K13/02C08K2003/2265C08K2003/265C08K3/34C08K2003/321C08K2003/3045C08K2003/2296C08K5/098
Inventor 吕少波李卓才李苏杨
Owner SUZHOU JONATHAN NEW MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com