Heat-resisting and anti-corrosion material and preparation method thereof

An anti-corrosion material and heat-resistant technology, which is applied in the direction of anti-corrosion coatings, chitin polysaccharide coatings, hyaluronic acid coatings, etc., can solve the problems of poor substrate adhesion, unsatisfactory heat resistance, and large environmental pollution, and achieve high curing content , good surface toughness, good leveling performance

Inactive Publication Date: 2015-10-28
HEFEI ZHONGHAO NEW MATERIAL CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

On the one hand, the current anti-corrosion materials generally have poor adhesion to the substrate, low curing content, and large environmental pollution; lost its original effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A heat-resistant anticorrosion material, comprising the following raw materials in parts by weight: 50 parts of polymer resin, 3 parts of additives, 10 parts of mixed solvent, 3 parts of benzoic acid, 4 parts of chitosan, 8 parts of sodium diacetate, 10 parts of calcium propionate 2 parts, 2 parts of pigment, 10 parts of filler, 10 parts of curing agent, 6 parts of water.

[0021] Auxiliaries include castor oil, dibutyl phthalate, crosslinking agents and petroleum microcrystalline wax.

[0022] Mixed solvents include ethanol, butanone, and DBE.

[0023] The polymer resin is E-44 epoxy resin.

[0024] The pigment is iron red powder.

[0025] The filler is titanium dioxide.

[0026] The curing agent is a phenalkamine epoxy curing agent.

[0027] A preparation method of a heat-resistant anti-corrosion material, comprising the following steps:

[0028] (1) Add polymer resin, benzoic acid, chitosan, sodium diacetate, calcium propionate, and water into the mixture, and t...

Embodiment 2

[0038] A heat-resistant anticorrosion material, comprising the following raw materials in parts by weight: 60 parts of polymer resin, 5 parts of additives, 15 parts of mixed solvent, 5 parts of benzoic acid, 6 parts of chitosan, 12 parts of sodium diacetate, 12 parts of calcium propionate 4 parts, 4 parts of pigment, 15 parts of filler, 20 parts of curing agent, 8 parts of water.

[0039] Auxiliaries include castor oil, dibutyl phthalate, crosslinking agents and petroleum microcrystalline wax.

[0040] Mixed solvents include ethanol, butanone, and DBE.

[0041] The polymer resin is E-44 epoxy resin.

[0042] The pigment is iron red powder.

[0043] The filler is titanium dioxide.

[0044] The curing agent is a phenalkamine epoxy curing agent.

[0045] A preparation method of a heat-resistant anti-corrosion material, comprising the following steps:

[0046] (1) Add polymer resin, benzoic acid, chitosan, sodium diacetate, calcium propionate, and water into the mixture, and ...

Embodiment 3

[0056]A heat-resistant anticorrosion material, comprising the following raw materials in parts by weight: 55 parts of polymer resin, 4 parts of additives, 12.5 parts of mixed solvent, 4 parts of benzoic acid, 5 parts of chitosan, 10 parts of sodium diacetate, 11 parts of calcium propionate parts, 3 parts of pigment, 12.5 parts of filler, 15 parts of curing agent, and 7 parts of water.

[0057] Auxiliaries include castor oil, dibutyl phthalate, crosslinking agents and petroleum microcrystalline wax.

[0058] Mixed solvents include ethanol, butanone, and DBE.

[0059] The polymer resin is E-44 epoxy resin.

[0060] The pigment is iron red powder.

[0061] The filler is titanium dioxide.

[0062] The curing agent is a phenalkamine epoxy curing agent.

[0063] A preparation method of a heat-resistant anti-corrosion material, comprising the following steps:

[0064] (1) Add polymer resin, benzoic acid, chitosan, sodium diacetate, calcium propionate, and water into the mixture,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a heat-resisting and anti-corrosion material. The heat-resisting and anti-corrosion material is composed of, by weight, 50-60 parts of high-molecular resin, 3-5 parts of auxiliaries, 10-15 parts of mixed solvent, 3-5 parts of benzoic acid, 4-6 parts of chitosan, 8-12 parts of sodium diacetate, 10-12 parts of calcium propionate, 2-4 parts of pigment, 10-15 parts of filler, 10-20 parts of curing agent and 6-8 parts of water. The heat-resisting and anti-corrosion material is high in adhesive force, high in solidification, environmentally friendly and economical and has a good heat-resisting effect.

Description

technical field [0001] The invention relates to the field of anti-corrosion materials, in particular to a heat-resistant anti-corrosion material and a preparation method thereof. Background technique [0002] With the rapid development of China's economic construction, construction, transportation, petrochemical, energy, machinery and other fields have achieved rapid growth. With the rapid development of economy, environmental pollution has become increasingly serious. Corrosion is becoming more and more serious, and the direct economic loss caused by corrosion accounts for about 1-4% of the total output value of the national economy every year; therefore, anti-corrosion materials provide a broad space for development. On the one hand, the current anti-corrosion materials generally have poor adhesion to the substrate, low curing content, and large environmental pollution; Lost the original effect. Contents of the invention [0003] In order to overcome the problems exist...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D105/08C09D7/12C09D5/08
Inventor 徐中豪徐数数
Owner HEFEI ZHONGHAO NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com