Antifreeze rubber inner tube material

A technology of rubber inner tube and inner tube, applied in special tires, tire parts, transportation and packaging, etc., can solve the problems of poor performance and low output of butyl rubber, and achieve long service life, good air tightness, and increased tensile strength. The effect of tensile strength

Inactive Publication Date: 2015-11-11
ANHUI HUAYANG RUBBER
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, the output of butyl rubber in my country is extremely low, and the supply is in short supply. The existing butyl reclaimed rubber and other natural rubber inner tube materials have poor performance. It is urgent to find a new material for inner tubes that can reduce the amount of fixed base rubber.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] A kind of frost-resistant rubber inner tube material, which is made from the following raw materials by weight (kg): butyl rubber 30, waste butyl rubber inner tube 15, silicone rubber 10, compound intercalation modified powder 50, coumarone Resin 4, microencapsulated red phosphorus 8, sulfur powder 3, accelerator TT0.7, castor oil 3, turpentine oil 2, carbon nanotubes 5, coal slime 2, SBS resin 5, talcum powder 25, antioxidant 10100.3, anti-oxidant Oxygen 10240.3;

[0025] The compound intercalation modified powder is prepared from raw materials with the following weight (kg):

[0026] Deionized water 150, Nylon 66150, Ethylene Propylene Rubber 40, Trimethyl Cetyl Ammonium Bromide 1, Trimethyl Octadecyl Ammonium Chloride 1, Kaolin 10, Sludge 15, Activated Carbon 4, Zeolite Powder 5 ;

[0027] The preparation method of the compound intercalation modified powder comprises the following steps:

[0028] (1) Dehydrate the sludge, dry it, mix it with kaolin, activated carb...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an antifreeze rubber inner tube material. The antifreeze rubber inner tube material is made of the following raw materials in parts by weight: 30-40 parts of butyl rubber, 10-20 parts of waste butyl rubber inner tubes, 10-20 parts of silicone rubber, 40-50 parts of compound intercalation modification powder, 2-4 parts of coumdrone indene resins, 5-10 parts of microcapsulated red phosphorous, 2-3 parts of sulfur powder, 0.7-1.4 parts of accelerator, 3-5 parts of castor oil, 2-5 parts of turpentine, 5-10 parts of carbon nanotubes, 2-3 parts of slime, 5-8 parts of SBS resin, 25-40 parts of talcum powder, 0.3-0.5 parts of antioxidant 1010 and 0.3-0.6 parts of antioxidant 1024. An inner tube prepared by using the antifreeze rubber inner tube material provided by the present invention has good freezing resistance, can be used in cold areas, has good safety, is not likely to break and is wide in application scope, long in service life, high in surface softness, low in smoke and nontoxic during combustion and good in mechanical properties.

Description

technical field [0001] The invention relates to the field of inner tubes, in particular to a frost-resistant rubber inner tube material. Background technique [0002] The inner tube is commonly known as the inner tube. Refers to a circular elastic tube with a tire valve for maintaining the internal pressure of the tire. The valve is used to inflate and maintain a certain pressure of air in the inner tube. The inner tube should have good air tightness, heat resistance, elasticity, aging resistance and small permanent deformation. Generally made of butyl rubber. [0003] Butyl rubber is a kind of synthetic rubber, which is synthesized from isobutylene and a small amount of isoprene. It is generally used in the production of car tires and car sound insulation products. Now butyl rubber has been widely used to replace asphalt in the name of environmental protection. [0004] Butyl rubber inner tube colloid has good self-closing performance and high air tightness. After th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/22C08L83/04C08L53/02C08L91/00C08K13/08C08K9/10C08K3/02C08K7/24C08K3/06C08K3/34C08K3/04C08K11/00B60C1/00
CPCC08L23/22B60C1/0008C08K2201/011C08L2205/025C08L2205/035C08L2207/24
Inventor 吴治学
Owner ANHUI HUAYANG RUBBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products