A liquid phase solvent for acetylene hydrogenation to ethylene slurry bed

A liquid-phase solvent and acetylene hydrogenation technology, applied in the field of liquid-phase solvents, can solve the problems of rising production costs, increasing the concentration and viscosity of the solvent system, and increasing the load of the solvent recovery process, so as to prolong the life, improve the efficiency, and reduce the product. Effects of carbon and deactivation

Active Publication Date: 2017-08-08
北京锦泰诚瑞科技发展有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, experiments have revealed that the optimum temperature for the hydrogenation of acetylene to ethylene is around 160°C, which is just within the boiling range of the solvent system. As the reaction progresses, the solvents such as NMP and DMF in the solvent continue to evaporate. The target product ethylene gas escapes from the reaction system, resulting in a continuous increase in the concentration and viscosity of the solvent system in the reactor. The escape of the solvent will also increase the load of the solvent recovery process, resulting in a substantial increase in production costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of liquid phase solvent, is made by the component of following parts by weight: 2-methylcyclohexyl acetate (MCHA) 8 parts, 2-methylformamide (DMF) 8 parts, methyl methacrylate (MMA) 2 parts, N-methylpyrrolidone (NMP) 65 parts, ionic liquid [BMIM] (MeO) 2 PO 2 2 parts, 0.3 parts of hydrogen donor 2,6-naphthoquinone.

Embodiment 2

[0023] A liquid phase solvent, made by the following components by weight: 10 parts of 2-methylcyclohexyl acetate (MCHA), 8 parts of 2-methylformamide (DMF), methyl methacrylate (MMA) 2 parts, N-methylpyrrolidone (NMP) 60 parts, ionic liquid [BMIM] (MeO) 2 PO 2 5 parts, 0.3 parts of hydrogen donor 2,6-naphthoquinone.

Embodiment 3

[0025] A liquid phase solvent, made by the following components by weight: 15 parts of 2-methylcyclohexyl acetate (MCHA), 8 parts of 2-methylformamide (DMF), methyl methacrylate (MMA) 2 parts, N-methylpyrrolidone (NMP) 55 parts, ionic liquid [BMIM] (MeO) 2 PO 2 5 parts, 0.3 parts of hydrogen donor 2,6-naphthoquinone.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a liquid phase solvent for an acetylene hydrogenation to ethylene slurry state bed. The liquid phase solvent comprises the following components in parts by weight: 0.5-15 parts of 2-methylcyclohexyl acetate, 50-85 parts of a selective solvent, 0.5-15 parts of an ionic liquid and 0.3-10 parts of a hydrogen donor. The obtained liquid solvent not only can be used for uniformly dispersing a catalyst in the liquid phase solvent to immediate transfer reaction heat and prevent the catalyst from being sintered, inactivated and the like, but also can be used for efficiently providing hydrogen free radicals to acetylene hydrogenation for adsorption in an active center of the catalyst when the reaction gas enters into the liquid phase solvent so as to improve the efficiency of the catalyst, prevent coverage of the catalyst as acetylene is self-polymerized to generate a green oil polymer and prolong the service life of the catalyst; meanwhile, the boiling point of a liquid phase solvent system is increased, the concentration and viscosity of the solvent required by a reactor are ensured, the load of solvent recovery in the next step is reduced, and the energy consumption level of the device is effectively reduced.

Description

technical field [0001] The invention relates to a liquid phase solvent used for acetylene hydrogenation to produce ethylene slurry bed, and belongs to the technical field of ethylene preparation. Background technique [0002] In coal chemical technology, coal is used as raw material to produce acetylene through calcium carbide process or natural gas as raw material through non-catalytic partial oxidation process, and then acetylene is used as raw material to produce ethylene products by hydrogenation under the action of selective hydrogenation catalyst. Since the acetylene hydrogenation reaction is an instantaneous strong exothermic reaction, experiments at home and abroad have shown that when a fixed-bed reactor is used for the acetylene hydrogenation reaction, a large amount of heat will be accumulated instantaneously in the reaction, resulting in a "flying temperature" phenomenon. Therefore, domestic and overseas tend to adopt the slurry bed with good mass transfer and he...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07C11/04C07C5/09
CPCY02P20/54
Inventor 车中山史雪君余海鹏吴道洪
Owner 北京锦泰诚瑞科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products