Anti-microbial synthetic leather and preparation method thereof

A technology of synthetic leather and antibacterial agent, applied in the field of synthetic leather, can solve the problems of environmental protection and human health hazards, poor wear resistance, etc., and achieve the effects of improving air permeability and moisture permeability, improving wear resistance, and enhancing smoothness.

Inactive Publication Date: 2015-12-16
ZHEJIANG JINSHANG SYNTHETIC LEATHER
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a synthetic leather that is beneficial to improve the wear resistance and moisture permeability of the existing polyurethane synthetic leather in order to solve the defects of poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] Example 1

[0022] An antibacterial synthetic leather, composed of the following components by weight: 35 parts of thermoplastic polyurethane, 20 parts of diisocyanate, 15 parts of melamine copolymer resin, 7 parts of nano titanium oxide-Ag antibacterial agent, 3 parts of auxiliary agent, 4 parts part honey, 1 part elm powder.

[0023] The auxiliary agent is a mixture of nano-zirconia, carotenoids and glass microspheres, the mass ratio of nano-zirconia, carotenoids and glass microspheres is 1:5:3; elm wood powder is 1200 mesh elm wood powder.

[0024] A preparation method of antibacterial synthetic leather, the preparation method is: drop sodium hydroxide into silver nitrate solution, then add ammonia water to prepare 0.3mol / L silver ammonium solution, pH value is 13, in 60°C water bath environment, Apply a 0.5T magnetic field, and add nano-titanium oxide evenly within 5 minutes. After the nano-titanium oxide is completely added, the magnetic field strength is increase...

Example Embodiment

[0029] Example 2

[0030] An antibacterial synthetic leather, composed of the following components by weight: 45 parts of thermoplastic polyurethane, 25 parts of diisocyanate, 20 parts of melamine copolymer resin, 8 parts of nano titanium oxide-Ag antibacterial agent, 4 parts of auxiliary agent, 6 parts part honey, 2 parts elm powder.

[0031] The auxiliary agent is a mixture of nano-zirconia, carotenoids and glass microspheres, the mass ratio of nano-zirconia, carotenoids and glass microspheres is 1:5:3; elm powder is 2000 mesh elm powder.

[0032] A preparation method of antibacterial synthetic leather, the preparation method is: dripping sodium hydroxide into silver nitrate solution and then dripping ammonia water to prepare 0.4mol / L silver ammonium solution, the pH value is 13.6, in a water bath environment of 75°C, Apply a 0.8T magnetic field, and add nano-titanium oxide uniformly within 8 minutes. After the nano-titanium oxide is completely added, the magnetic field str...

Example Embodiment

[0037] Example 3

[0038] An antibacterial synthetic leather, composed of the following components by weight: 50 parts of thermoplastic polyurethane, 35 parts of diisocyanate, 25 parts of melamine copolymer resin, 9 parts of nano titanium oxide-Ag antibacterial agent, 5 parts of auxiliary agent, 8 parts 1 part honey, 3 parts elm powder.

[0039] The auxiliary agent is a mixture of nano-zirconia, carotenoids and glass microspheres, the mass ratio of nano-zirconia, carotenoids and glass microspheres is 1:5:3; elm wood powder is 2400 mesh elm wood powder.

[0040] A preparation method of antibacterial synthetic leather, the preparation method is: drop sodium hydroxide into silver nitrate solution, then add ammonia water to prepare 0.5mol / L silver ammonium solution, pH value is 14.6, in 85°C water bath environment, Apply a 1.2T magnetic field, and add nano-titanium oxide evenly within 10 minutes. After the nano-titanium oxide is completely added, the magnetic field strength is in...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Weft tensile loadaaaaaaaaaa
Weft tensile loadaaaaaaaaaa
Weft tensile loadaaaaaaaaaa
Login to view more

Abstract

The invention relates to an anti-microbial synthetic leather and a preparation method thereof. The anti-microbial synthetic leather is prepared from the following components by weight: 35 to 50 parts of thermoplastic polyurethane, 20 to 35 parts of diisocyanate, 15 to 25 parts of melamine copolymer resin, 7 to 9 parts of a nanometer titanium oxide-Ag anti-microbial agent, 3 to 5 parts of an auxiliary agent, 4 to 8 parts of honey and 1 to 3 parts of elm powder. The synthetic leather has wear resistance, moisture permeability and air permeability, reduces potential threat to the environment and the human body, can improve smoothness and cold-thermal fatigue performance, and has enhanced air permeability and moisture permeability, actual leather feel, wear resistance and service life.

Description

technical field [0001] The invention relates to the field of synthetic leather, in particular to an antibacterial synthetic leather which is beneficial to improving the wear resistance, moisture permeability and air permeability of synthetic leather, and reduces potential threats to the environment and human body and a preparation method thereof. Background technique [0002] People need to use a large amount of synthetic leather in their daily life, and when producing synthetic leather, due to adding a large amount of plasticizer and other materials, the synthetic leather produced is not ideal in terms of luster and hand feeling. In order to achieve a better and more ideal use effect, the surface treatment of synthetic leather must be carried out in the production process of synthetic leather, so as to endow the surface of synthetic leather with smooth, soft, matting, waterproof, antifouling and other comfortable feel and beautiful appearance. . [0003] Polyurethane synth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06N3/14C08L75/04C08L97/02C08K13/02C08K5/29C08K3/22C08K3/08
Inventor 田树松杨毅
Owner ZHEJIANG JINSHANG SYNTHETIC LEATHER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap